Chrom vi test

Abstract

The present invention is in the field of chromium VI test, a chromium VI tester, a test kit comprising said chromium VI tester, and in particular to identify low amounts of chromium VI, such as in coatings and paints, which low amounts may form a health risk and may be toxic.

Description

[0001] Chromium VI test

[0002] FIELD OF THE INVENTION

[0003] The present invention is in the field of chromium VI test, a chromium VI tester, a test kit comprising said chromium VI tester, and in particular to identify low amounts of chromium VI, such as in coatings and paints, which low amounts may form a health risk and may be toxic.

[0004] BACKGROUND OF THE INVENTION

[0005] Hexavalent chromium (chromium(VI), Cr(VI), chromium 6) relates to chromium in the +6-oxidation state. Hexavalent chromium or compounds thereof may be present in chromium tri oxide, in various chrome salts, such as chromate and dichromate, in textile dyes, wood preserva tion products, anti-corrosion products, and chromate conversion coatings. Industrial uses of hex avalent chromium compounds include chromate pigments in dyes, paints, inks, and plastics; chromates added as anticorrosive agents to paints, primers, and other surface coatings; and chro mic acid electroplated onto metal parts to provide a decorative or protective coating.

[0006] Chromium VI is toxic and most likely may cause cancers. Therefore in 1991, in the USA, the maximum contaminant level (MCL) for chromium exposure was set based on potential of “adverse dermatological effects” related to long-term chromium exposure to 100 ppb (or 0.1 ppm) in drinking water. Likewise, the EPA came to the conclusion that chromium was associ ated with various health issues.

[0007] Chromium VI can be present in air, for example after spraying paints or by sanding paint layers. Inhalation of these airborne chromium VI is a major health concern. Therefore, the Occu pation Safety and Health Administration has established a permissible exposure limit of 5 pg / m ’ chromium VI for an 8-hour time weighted average.

[0008] No maximum chromium-6 concentration was found for chromium-6 paint layers yet. Some maximum concentration of solid materials were found; RoHS Directive 2011 / 65 / EU on the re striction of the use of certain hazardous substances in electronical and electronic equipment, notes that the maximum Chromium VI concentration of homogeneous materials is 1000 ppm (0.1 weight%).The European Directive 2019 / 48 / EG for the safety of toys is more strict and is 0.02 ppm.

[0009] Chromium VI is in particular an issue when refurbishing military equipment. For instance, the U.S. Army relied heavily on hexavalent chromium compounds to protect its vehicles, equip ment, aviation and missile systems from corrosion. The wash primer was sprayed as a pretreat ment and protective layer on bare metal, and subsequently the equipment was painted by a chro mium VI primer layer.

[0010] Chromium VI is difficult to determine. When present in a solution test kits are available, but these do no function for determining presence of chromium VI incorporated in another, typi cally solid, material, such as on surfaces.

[0011] Some documents recite indicator materials. For instance, WO 2006 / 112827 A recites a method to analyse the condition of a functional fluid comprising: (1) obtaining a sample of the used fluid; (2) placing the sample of the fluid to a test medium; (3) reacting the fluid with an in dicator in the test medium; (4) analysing visually the results of the reactor resulting in the deter mination of the condition of the fluid. Further an apparatus for analysing functional fluids is dis closed in the form of a test medium consisting of an absorbent or non-absorbent material which has been treated with a chemical indicator, marker substance or a developer or detector reagent upon which a sample of the fluid to be tested is placed. The components in the treated test me dium react with components in the test fluid providing a visual indication, for example a colour change, to judge the condition, the presence of a marker substance or another parameter of the fluid. US 9 310310 B2 recites a flowable dry powder composition comprising a mixture of di phenyl carbazide particles and glass bubbles; kits containing such compositions; methods of fill ing containers with such compositions; and, methods of using such compositions in the detecting of hexavalent chromium.

[0012] It is therefore an object of the present invention to provide an improved yet simple Chro mium VI tester, without jeopardizing functionality and advantages.

[0013] SUMMARY OF THE INVENTION

[0014] The present invention relates to an improved chromium Vl-tester, in particular suited for determining presence or absence thereof in a surface, comprising a volume of fluid absorbing material, in the fluid absorbing material a pH-indicator, i.e. an amount of chemical functioning as pH-indicator, wherein the pH indicator has a color in neutral form, and no color or a less in tense color (e.g. <20% of an initial intensity, preferably < 10% of the initial intensity, such as < 1%) under acidic conditions, that is the pH-indicator being discolors, typically being in ionic form, i.e. the fluid absorbing material appears to be colorless, and in the fluid absorbing material a chromium Vl-indicator, i.e. an amount of chemical functioning as chrome- Vl-indicator, wherein the chromium Vl-indicator has a color in the presence of chromium VI, and no color in absence of chromium VI, i.e. the fluid absorbing material appears to be colorless. The pH-indica- tor may also relate to a chemical compound that is broken down to smaller compounds under acidic conditions. Therewith the present tester provides a sensitive and yet simple tester for es tablishing presence or absence of Chrome- VI, even in low concentrations, such as above 10 ppm (0.001 weight %). With the simple test it is easy to determine of a safe and non-toxic environ ment exists, such as for human beings subsequently treating a tested surface, such as by polish ing or abrading, such as when using sandpaper. In a second aspect the present invention relates to a kit, typically a kit of parts, for testing presence of chromium VI comprising at least one chromium VI tester according to the in vention, a container for providing fluid drops of acid, wherein the acid is in pure or diluted form, such as diluted in water, wherein the acid has a pH of < 5, preferably pH<3, more preferably a pH<l, and optionally a data sheet, instruction, and a safety sheet. The acid may be selected from acetic acid, sulphuric acid, phosphoric acid, suitable carboxylic acids, HC1, typically in diluted form, such as < 40%, typically < 10%, and combinations thereof. Also, acid in combination with solvents, such as acetone and ethyl alcohol, methyl alcohol is possible. The chromium VI tester and container may also be combined, for example in a tester on a small tube containing the liq uid. Likewise, a container may be provided comprising a swab and liquid, wherein the container may be broken before application, releasing the liquid to the swab.

[0015] Measurements are typically carried out at ambient conditions, i.e. at about 20 °C, and at a pressure of about 100 kPa. For measurements identified typically any measurement technique or measurement tool can be used, having the indicated accuracy. For instance for the pH any Met- tler Toledo can be used, for a mass any Mettler Toledo can be used, likewise for a volume any calibrated pipette or calibrated cylinder can be used, etc. These tools are typically readily availa ble in any laboratory. Measurements do not require any further skills typically.

[0016] In a third aspect the present invention relates to a method of testing presence or absence of chromium VI comprising, providing a surface potentially comprising chromium VI, such as a coating surface or a paint surface, optionally pre-treating said surface, such as by abrasion, by cutting, by cleaning, providing at least one drop of acid to the chromium VI tester according to the invention, preferably lowering the pH to < 3, rubbing the acidic chromium VI tester over said surface, and determining coloration of the tester thereby identifying presence or absence of chro mium VI. Typically, when the pH is higher than 3, the chromium-6 in the paint layer does almost not dissolve, and therefore there is no visual or only a slightly visible purple coloration present.

[0017] In a fourth aspect the present invention relates to a method of producing a chromium VI tester according to the invention, comprising providing a volume of fluid absorbing material, providing the pH-indicator dissolved in a first solvent, adding pH-indicator dissolved in a first solvent to the fluid absorbing material, such as by drops, and providing the chromium Vl-indica- tor dissolved in a second solvent, adding chromium Vl-indicator dissolved in the second solvent to the fluid absorbing material, such as by drops, and removing the first and second solvent, such as by evaporation.

[0018] Thereby the present invention provides a solution to one or more of the above-mentioned problems.

[0019] Advantages of the present description are detailed throughout the description. DETAILED DESCRIPTION OF THE INVENTION

[0020] The present invention relates in a first aspect to a chromium Vl-tester according to claim 1.

[0021] In an exemplary embodiment of the present chromium VI tester the fluid absorbing mate rial may be selected from cotton, paper, cellulose comprising material, polymer comprising ma terial, such as acrylate polymers, sponge, fluff pulp, starch, polysaccharides, proteins, and com binations thereof.

[0022] In an exemplary embodiment of the present chromium VI tester the fluid absorbing mate rial may be provided on a carrier, such as a rod.

[0023] In an exemplary embodiment of the present chromium VI tester the volume of fluid ab sorbing material may be 1-1000 mm3, preferably 10-500 mm3, such as 50-300 mm3.

[0024] In an exemplary embodiment of the present chromium VI tester the pH indicator may be provided in an amount of 0.01-10 mg / cm3, preferably 0.1-50 mg / cm3, more preferably 0.5-10 mg / cm3, such as 1-5 mg / cm3.

[0025] In an exemplary embodiment of the present chromium VI tester the pH indicator may be selected from organic indicators, preferably indicators with structural formula wherein each of Rl, R2, and R3, each independently comprise at least one aromatic hydrocarbon moiety, such as benzene and naphthalene, and wherein each of Rl, R2, and R3, each inde pendently, comprise 0-2 sulfonate groups, and / or, each independently, comprise 0-2 tertiary am- mine groups, preferably wherein Rl and R2 comprise 0-1 sulfonate groups and wherein R2 com prise 1-2 sulfonate groups, such as E131, E133, E142, ethyl violet, methyl violet, malachite green, bromophenol blue, and methyl thymol blue. R4 may be selected from a C1-C5alkane, H, or may be absent, in which latter case a double bond is present (dashed line). An alternative is quinaldine red.

[0026] In an exemplary embodiment of the present chromium VI tester the pH indicator may be selected from sulfur comprising silicates SinCfinSj”1, wherein ne[5-8], j e[3-6], and me [5-20], typically having at least one S3moiety, and optionally at least one M3+counter cation, typically 3-9 cations, wherein M may be selected from Group 15 metals, such as Al, and Fe, and wherein the charge m- is preferably compensated by monovalent cations, such as Na+, K+, and NFL1 /

[0027] In an exemplary embodiment of the present chromium VI tester the pH indicator has a spectral absorbance of <10%, such as <5%. As a reference the wavelength with the respective highest peak may be selected to determine the absorbance.

[0028] In an exemplary embodiment of the present chromium VI tester the chromium Vl-indicator may be provided in an amount of 0.01- 200 mg / cm3, preferably 0.1- 50 mg / cm3.

[0029] In an exemplary embodiment of the present chromium VI tester the chromium Vl-indicator may be selected from 1,5-Diphenylcarbohydrazide, Penta methylene-bis triphenyl phospho- nium, triphenyltrazolium chloride, xylene cyanole, p-amino-N,N-diethylaniline, benzooxa- zol, benzothiazole, dimethylindocarboxyanine, dimethylindodicarboxyanine, p-amino- N,N-diethylaniline (change to red), benzidine (change to blue), 2,7-diaminodiphenylene oxide (change to blue), o-Dianisidine (change to red), indigo carmine, 2,2'-dipyridyl, KI, KIO3, Pyrrole (change to blue), Strychnine (change to blue violet / red), 3f Leuco xylene cy anole FF (change to blue), and nitro blue tetrazolon chloride.

[0030] In an exemplary embodiment of the present method of producing a chromium VI tester 0.1-3 ml of first solvent may be added.

[0031] In an exemplary embodiment of the present chromium VI test method 1-10 ml of second solvent may be added.

[0032] In an exemplary embodiment of the present method of producing a chromium VI tester the first solvent may comprise 0.01-10 mg pH indicator / cm3first solvent, preferably 0.1-3 mg / cm3pH indicator / cm3first solvent.

[0033] In an exemplary embodiment of the present method of producing a chromium VI tester the second solvent may comprise 0.01-200 mg chromium VI indicator per cm3second solvent, pref erably 0.1-50 mg / cm3, such as 0.5-3 mg / cm3.

[0034] The first and second solvent may be the same solvent.

[0035] For instance, the

[0036] In an exemplary embodiment of the present method of producing a chromium VI tester the first and second solvent may each individually be selected from alcohols, such as ethanol, metha nol, and isopropanol, from acetone, and from water.

[0037] The invention is further detailed by the accompanying figures and examples, which are exemplary and explanatory of nature and are not limiting the scope of the invention.

[0038] To the person skilled in the art it may be clear that many variants, being obvious or not, may be conceivable falling within the scope of protection, defined by the present claims.

[0039] SUMMARY OF FIGURES

[0040] Figs. 1 shows a chromium VI test.

[0041] Figs. 2a-i show exemplary pH indicators and fig. 2j a general chemical structural formula thereof. Figs. 3a-i show exemplary Cr-VI indicators

[0042] DETAILED DESCRIPTION OF THE FIGURES

[0043] Figs. 1 shows a chromium VI test. Figure 1 A: cotton swab (or cotton bud) with blue dye and indicator. B: moistened head of cotton wool with an acid, causing the color of the pH-indica- tor to fade. C: Moistened swab rubbed on a surface where chromium-6 was present, causing the head to turn purple, as the chromium VI indicator changes color.

[0044] Figs. 2a-e show exemplary pH indicators and fig. 2f a general chemical structural formula thereof. Fig. 2a shows E131 en E131 lake Patent blue V (CAS Number 3536-49-0), fig. 2b shows El 33

[0045] Brilliant Blue FCF (Blue 1) (CAS 3844-45-9), fig. 2c shows E142(CAS 3087-16-9), fig. 2d shows Bromophenol Blue (CAS 115-39-9), fig. 2e shows Methyl thymol blue (CAS 3778-22-1), fig. 2f shows pigment blue 29 (CAS 57455-37-5), fig. 2g shows malachite green (CAS number 569-64-2, chlorite salt), fig. 2h shows ethyl violet, analogue to methyl violet (CAS 8004-87-3), which may comprise, each individually, an alkane moiety on each N-end-group, and fig. 2i shows quinaldine red (CAS 117-92-0). Fig. 2j shows generic pH-indicators, wherein each of Rl, R2, and R3, each independently comprise at least one aromatic hydrocarbon moiety, such as ben zene and naphthalene, and wherein each of Rl, R2, and R3, each independently, comprise 0-2 sulfonate groups, and / or, each independently, comprise 0-2 tertiary ammine groups, preferably wherein Rl and R2 comprise 0-1 sulfonate groups and wherein R2 comprise 1-2 sulfonate groups, such as E131, E133, E142, ethyl violet, methyl violet, malachite green, bromophenol blue, and methyl thymol blue. R4 may be selected from a C1-C5alkane, H, or may be absent, in which latter case a double bond is present (dashed line).

[0046] EXAMPLES / EXPERIMENTS

[0047] The invention although described in detailed explanatory context may be best under stood in conjunction with the accompanying examples and figures.

[0048] Experimental

[0049] Background chromium-6 (or chrome- VI) test, such as for paints, coatings, and surfaces.

[0050] Test rods, such as the cotton swabs above, can be produced by adding an indicator in the cotton head of a cotton swab. This swab can then be used to detect chromium-6; the swab head is moistened with an acid, such as diluted sulphuric acid, and then rubbed over a layer of paint or another surface that may contain chromium-6. A chromium-6 indicator in combination with an acid reacts with the dissolved chromium-6 leading to a purple discoloration.

[0051] So in the present chromium VI tester a use of an additional dye in addition to a chromium VI indicator (for the swab head of the wadding rods) that fades or discolors (to a light color or no color at all) when the cotton swabs are moistened (dripped) with an acid, such as sulphuric acid. The fading may be due to the fact, for example, that the dye is (intentionally) not stable, and therefore breaks down at high acidity. But these can also be dyes that don't give a color, or a lighter color when the pH changes (i.e. a pH indicator).

[0052] Treatment of the cotton swabs with 'fading' dyes has several advantages:

[0053] (1) During production, the color of the cotton swabs allows us to clearly see which cotton wool rods have been treated. This prevents mistakes: the white untreated cotton wool rods cannot be confused with the treated rods. Such is also subject to government regulations.

[0054] (2) Cosmetic products, such as cotton swabs, may not legally be treated with chemicals without this being clearly visible.

[0055] (3) A customer can clearly see that the cotton wool bars have been treated. She will therefore not think that she can use untreated cotton swabs (white cotton swabs) for the test.

[0056] (4) A customer can clearly see if a cotton swab is sufficiently moistened with sulphuric acid: only in this case the blue color will disappear.

[0057] (5) After moistening with e.g. sulphuric acid, the color becomes light (i.e. no longer blue) so that any purple discoloration due to presence of chromium-6 becomes clearly visible during the test. This will result in a lower detection limit compared to a cotton swab treated with a dye that does not fade. The detection limit (just visible coloration by bare eye) is at present about 100 ppm (0.01 weight% chromium VI in a paint layer) for a swab size of ap-proximately 0.2 cm3. At this detection limit approximately 0,1 pg chromium VI is dissolved. With smaller swab sizes lower amounts of chromium VI can be detected, such as 10 ppm.

[0058] (6) The color of the cotton swab may camouflage the light-purple discoloration that occurs over time when cotton wool rods are stored longer in a bag. With the blue discolored cotton wool rods this (innocent) discoloration will not / less stand out and therefore will not cause discussion. The shelf life can therefore be extended.

[0059] Examples of dyes

[0060] These are typically pH-indicators. The chemical (acid-base) reaction involved can be represented by:

[0061] Hind + H2O H30++Ind

[0062] Wherein Hind has a different color than Ind (the conjugated form). In the present applica tion Hind has a light color or is colorless. This is obtained with the acid (moist) state of the cot ton bud. For the present application, the Ind form preferably has the basic color of the not mois tened cotton wool bar (neutral).

[0063] A few examples of successful pH indicators are given in figs. 2a-i, whereas fig. 2j repre sents a generic chemical structure. Fig. 3a shows benzidine (CAS 92-87-5), 3b 2,7-diaminodiphenylene oxide, 3c o-Dianis- idine (CAS 119-90-4), 3d pyrrole (CAS 109-97-7), 3e strychnine (CAS 57-24-9), 3f Leuco xy lene cyanole FF (CAS 303-373-0), 3g tetrazolium chloride (CAS 298-96-4).

Claims

CLAIMS1. Chromium Vl-tester comprising a volume of fluid absorbing material, in the fluid absorbing material, a pH-indicator, wherein the pH indicator has a color in neu tral form, and no color under acidic conditions, and in the fluid absorbing material, a chromium Vl-indicator, wherein the chromium Vl-indica- tor has a color in the presence of chromium VI, and no color in absence of chromium VI.

2. Chromium Vl-tester according to claim 1, wherein the fluid absorbing material is selected from cotton, paper, cellulose comprising material, polymer comprising material, such as acrylate polymers, sponge, fluff pulp, starch, polysaccharides, proteins, and combinations thereof.

3. Chromium Vl-tester according to any of claims 1-2, wherein the fluid absorbing material is provided on a carrier, such as a rod.

4. Chromium Vl-tester according to any of claims 1-3, wherein the volume of fluid absorbing material is 1-1000 mm3, preferably 10-500 mm3.

5. Chromium Vl-tester according to any of claims 1-4, wherein the pH indicator is provided in an amount of 0.01-10 mg / cm3, preferably 0,05-5 mg / cm3.

6. Chromium Vl-tester according to any of claims 1-5, wherein the pH indicator is selected from organic indicators, preferably indicators with structural formulawherein each of Rl, R2, and R3, each independently comprise at least one aromatic hydrocarbon moiety, such as benzene and naphthalene, and wherein each of Rl, R2, and R3, each inde pendently, comprise 0-2 sulfonate groups, and / or, each independently, comprise 0-2 tertiary am- mine groups, preferably wherein Rl and R2 comprise 0-1 sulfonate groups and wherein R2 com prise 1-2 sulfonate groups, such as E131, E133, E142, ethyl violet, methyl violet, malachite green, bromophenol blue, and methyl thymol blue, wherein R4 may be selected from a C1-C5al kane, H, or may be absent, in which latter case a double bond is present, and from sulfur com prising silicates Sin04nSjm, wherein ne[5-8], je[3-6], and me [5-20], and from quinaldine red, and / or wherein the pH indicator has an absorbance of <10%.

7. Chromium Vl-tester according to any of claims 1-6, wherein the chromium Vl-indicator is provided in an amount of 0.01-200 mg / cm3, preferably 0.1-50 mg / cm3.

8. Chromium Vl-tester according to any of claims 1-7, wherein the chromium Vl-indicator is se lected from 1,5-Diphenylcarbazide, Penta methylene-bis triphenyl phosphonium (change to vio let), triphenyltrazolium chloride, xylene cyanole, p-amino-N,N-diethylaniline, benzooxazol, benzothiazole, dimethylindocarboxyanine, dimethylindodicarboxyanine, p-amino-N,N-di- ethylaniline, benzidine, 2,7-diaminodiphenylene oxide, o-Dianisidine, indigo carmine, 2,2'-dipyridyl, KI, KIO3, Pyrrole, Strychnine, 3f Leuco xylene cyanole FF, and nitro blue te- trazolon chloride.

9. Kit for testing presence of chromium VI comprising at least one chromium VI tester according to any of claims 1-8, a container for providing fluid drops of acid, wherein the acid is in pure or diluted form, such as diluted in water, wherein the acid has a pH<3, preferably a pH<l, and optionally a data sheet, instruction, and a safety sheet.

10. Kit according to claim 9, wherein the container comprising 0.1-20 ml of acid, and / or comprising more than two chromium VI testers, such as 3-100 testers.

11. Method of testing presence or absence of chromium VI comprising, providing a surface potentially comprising chromium VI, such as a coating surface or a paint surface, optionally pre-treating said surface, such as by abrasion, by cutting, by cleaning, providing at least one drop of acid to the chromium VI tester according to any of claims 1- 8, preferably lowering the pH to < 3, rubbing the acidic chromium VI tester over said surface, and determining coloration of the tester thereby identifying presence or absence of chromium VI.

12. Method of producing a chromium VI tester according to any of claims 1-8, comprising providing a volume of fluid absorbing material, providing the pH-indicator dissolved in a first solvent, adding pH-indicator dissolved in the first solvent to the fluid absorbing material, such as by drops, and providing the chromium Vl-indicator dissolved in a second solvent, adding chromium VI- indicator dissolved in the second solvent to the fluid absorbing material, such as by drops, and removing the first and second solvent, such as by evaporation.

13. Method according to claim 12, wherein 0.1-3 ml of first solvent is added, and / or wherein 1-10 ml of second solvent is added, and / or wherein the first solvent comprises 0.01-10 mg pH indicator / cm3first solvent, preferably 0.05-5 mg pH indicator / cm3first solvent, and / orwherein the second solvent comprises 0.01-200 mg chromium VI indicator per cm3second sol vent, preferably 0.1-50 mg / cm3, such as 0.5-3 mg / cm3, and / or wherein the first and second solvent are each individually selected from alcohols, such as etha nol, methanol, and isopropanol, from acetone, and from water.