Spectacle lens made of resin

A spectacle lens and resin technology, which is applied in the field of optical materials, can solve problems such as failure to pass impact resistance tests, and achieve the effects of improving imaging clarity, reducing aberrations, and improving safety

Active Publication Date: 2008-01-30
JIANGSU MINGYUE PHOTOELECTRICS TECH
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] http: / / www.mingyue.com / e06.htm website: Shanghai Mingyue Optical Glass Co., Ltd., titled "PMC resin lens", its formula is: diethylene glycol propylene dicarbonate Brite-55, ultraviolet absorber UV -5411, blue inorganic pigment B, red inorganic pigment R, diisopropylene peroxycarbonate IPP, resin lens with a refractive index of 1.552, and its dispersion coefficient reaches 42, but it cannot pass the US FDA impact test

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0080] (KA-55, UV-31, B-51, R-51, HILVB-55, catalyst (1), and 3M are all supplied by Korea KOC Company)

[0081] test results

[0082] Inspection item Index Inspection result Conclusion

[0083] (1) Optical performance indicators

[0084] Vertex according to GB10810 Table 1 -0.02-+0.08 qualified

[0085] optical center and

[0086] Prism degree ≤0.25 0.00 Passed

[0087] Refractive index ±0.003 0.002 Pass

[0088] Dispersion coefficient ±4% -2.1% qualified

[0089] Visible light transmittance ≥90.0 90.2% pass

[0090] UV properties Comply with the provisions of GB10810 Comply with Qualified

[0091] (two), mechanical performance index

[0092] Impact Resistance FDA Standard Pass Pass

[0093] (3), Dimensions and surface quality

[0094] Meet the requirements of GB10810 Meet Qualified

[0095] (4), other

[0096] Yellow index ≤1.25 1.08 Passed

Embodiment 2

[0099] test results

[0100] Inspection item Index Inspection result Conclusion

[0101] (1) Optical performance indicators

[0102] Vertex according to GB10810 Table 1 -0.09 unqualified

[0103] optical center and

[0104] Prism degree ≤0.25 0.00 Passed

[0105] Refractive index ±0.003 0.002 Pass

[0106] Dispersion coefficient ±4% -2.1% qualified

[0107] Visible light transmittance ≥90.0 90.2% pass

[0108] UV properties Comply with the provisions of GB10810 Comply with Qualified

[0109] (two), mechanical performance index

[0110] Impact Resistance FDA Standard Pass Pass

[0111] (3), Dimensions and surface quality

[0112] Meet the requirements of GB10810 Meet Qualified

[0113] (4), other

[0114] Yellow index ≤1.25 1.08 Passed

[0115] raw material name

KA-55

UV-31

B-51

R-51

HILVB-55

Catalyst(1)

3M

Weight (g)

980

3.00

1.00

0.94

0.06

10.00

5.00

...

Embodiment 4

[0134] test results

[0135] Inspection item Index Inspection result Conclusion

[0136] (1) Optical performance index

[0137] Vertex according to GB10810 Table 1 -0.02-+0.08 qualified

[0138] optical center and

[0139] Prism degree ≤0.25 0.00 Passed

[0140] Refractive index ±0.003 0.002 Pass

[0141] Dispersion coefficient ±4% -3.6% qualified

[0142] Visible light transmittance ≥90.0 90.0% pass

[0143] UV properties Comply with the provisions of GB10810 Comply with Qualified

[0144] (two), mechanical performance index

[0145] Impact Resistance FDA Standard Pass Pass

[0146] (3), Dimensions and surface quality

[0147] Meet the requirements of GB10810 Meet Qualified

[0148] (4), other

[0149] Yellow index ≤1.25 1.08 Passed

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

This invention relates to resin glass slices, which comprise KA-55, UV-31, B-51, R-51, HILVB-55, accelerant one, 3M with their weight percentage as: KA-55,98-99; UV-31,0.1-0.3; B-51,0.03-0.1; R-51,0.02-0.1; HILVB-55,0.0005-0.001; acclerant(1),0.5-1; 3M,0.3-0.5.

Description

technical field [0001] The invention relates to an optical material, specifically a spectacle lens, especially a resin spectacle lens. technical background [0002] At present, resin lenses are in a priority position in the competition of the glasses market because of their light weight, high transparency, impact resistance, easy molding, and dyeability. The most domestically produced and sold resin lenses are 1.499 and 1.56 refractive index series, of which 1.499 resin lenses have higher impact resistance than 1.56, a dispersion coefficient of 58, and less dispersion, but due to the low refractive index, the lenses are thicker. However, the dispersion coefficient of the 1.56 refractive index lens is 38, and the impact resistance cannot pass the US FDA test (a steel ball with a diameter of 16mm is freely dropped from a height of 1.27 meters to impact the convex surface of the lens, and the lens should not be broken). [0003] According to the search, http: / / www.jiangteng.co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G02B7/02G02B1/04
Inventor 谢公晚谢公兴高维相
Owner JIANGSU MINGYUE PHOTOELECTRICS TECH
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com