Bamboo carbon dacron fiber, soybean fiber and cashmere fiber scribbled and producing method thereof

A technology of bamboo charcoal polyester fiber and soybean fiber, which is applied in the direction of yarn, textile and paper making, can solve the problems of large shrinkage and deformation, and achieve the effects of preventing fiber damage, good hygroscopicity and soft hand feeling

Inactive Publication Date: 2009-08-05
WUXI PAIHO TEXTILES CO LTD
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the shrinkage deformation of the pure soybean fiber fabric is large

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bamboo carbon dacron fiber, soybean fiber and cashmere fiber scribbled and producing method thereof
  • Bamboo carbon dacron fiber, soybean fiber and cashmere fiber scribbled and producing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] Taking 40 lbs as an example, the weight percentage of bamboo carbon polyester fiber, soybean fiber and cashmere fiber blended is 23:70:7. The cotton opener adopts the comb beater, that is, the A036C comb roller opener, the speed of the card beater is 500-600 rpm, and the single beater, that is, the A076C single beater lap machine, the The speed of machine comb needle beater is 700-900 rev / min. The cylinder speed of the carding machine is 270-350 rpm, the licker-in roller speed is 700-800 rpm, and the five-point distance between the cylinder and the cover plate is easy to enlarge. From the inlet to the outlet, they are 0.30mm, 0.28mm, and 0.28mm respectively. , 0.28mm, 0.30mm; the draw frame adopts three draw frames, and each draw frame adopts 8 sliver feeding and 8 times drafting. The 40-count blended yarn spun through the spinning process provided by the present invention and processed has a single-yarn breaking strength of 13.4 cN / tex after testing, and a CV value of...

Embodiment 2

[0045]Take 40 lbs as an example, the blending weight percentage of bamboo carbon polyester fiber, soybean fiber and cashmere fiber is 35:50:15. The cotton opener adopts the comb beater, that is, the A036C comb roller opener, the speed of the card beater is 500-600 rpm, and the single beater, that is, the A076C single beater lap machine, the The speed of machine comb needle beater is 700-900 rev / min. The cylinder speed of the carding machine is 270-350 rpm, the licker-in roller speed is 700-800 rpm, and the five-point distance between the cylinder and the cover plate is easy to enlarge. From the inlet to the outlet, they are 0.30mm, 0.28mm, and 0.28mm respectively. , 0.28mm, 0.30mm; the draw frame adopts three draw frames, and each draw frame adopts 8 sliver feeding and 8 times drafting. The 40-count blended yarn spun through the spinning process flow provided by the present invention and processed, after testing, its single yarn breaking strength is 13.7cN / tex, and the single...

Embodiment 3

[0047] Taking 40 lbs as an example, the weight percentage of bamboo carbon polyester fiber, soybean fiber and cashmere fiber blended is 50:30:20. The cotton opener adopts the comb beater, that is, the A036C comb roller opener, the speed of the card beater is 500-600 rpm, and the single beater, that is, the A076C single beater lap machine, the The speed of machine comb needle beater is 700-900 rev / min. The cylinder speed of the carding machine is 270-350 rpm, the licker-in roller speed is 700-800 rpm, and the five-point distance between the cylinder and the cover plate is easy to enlarge. From the inlet to the outlet, they are 0.30mm, 0.28mm, and 0.28mm respectively. , 0.28mm, 0.30mm; the draw frame adopts three draw frames, and each draw frame adopts 8 sliver feeding and 8 times drafting. Through the spinning process flow provided by the present invention and the processed 40-count blended yarn, its single yarn breaking strength is 14.0cN / tex after testing, and the single yar...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
lengthaaaaaaaaaa
coefficient of variationaaaaaaaaaa
Login to View More

Abstract

The present invention discloses a bamboo carbon polyester fibre, soybean fibre and cashmere fibre blended yarn and its preparation method. It is made up by using 22-50% of bamboo carbon polyester fibre, 30-70% of soybean fibre and 7-20% of cashmere fibre through a certain preparation process. The performance indexes of said blended yarn are as follows: single yarn breaking strength is 9.0-18.0 cN / tex, the coefficient of variation CV value of single yarn breaking strength is 8.0-22.0% and the coefficient of variation CV value of yarn evenness is 12.5-24.0%.

Description

1. Technical field: [0001] The invention relates to a yarn containing bamboo charcoal particles and a preparation method thereof, more particularly to a blended yarn of bamboo charcoal polyester fiber, soybean fiber and cashmere fiber and a preparation method thereof. 2. Background technology [0002] Bamboo charcoal polyester fiber has the function of absorbing and eliminating odor, and has far infrared, negative ion, anti-ultraviolet, antibacterial and health care functions. However, the fabric made of pure bamboo carbon polyester has poor hygroscopicity, soft hand feeling and poor comfort function. [0003] The fineness of cashmere fiber is very soft and warm, it has good hygroscopicity and comfortable function, but it has no health care function. [0004] Soybean fiber has far-infrared, negative ion and anti-ultraviolet health care functions, strong hygroscopicity, soft touch, dry and comfortable. However, the shrinkage deformation of pure soybean fiber fabric is large...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D02G3/04
Inventor 郑国烟
Owner WUXI PAIHO TEXTILES CO LTD
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com