Special low temperature adhesion promoter for PVC plastisol and preparation thereof

An adhesion promoter, low temperature technology, applied in the direction of adhesives, adhesive additives, polymer adhesive additives, etc., can solve the problems of aging, reduce the protection effect, the electrophoretic paint board is easily corroded, and achieve a low curing temperature. , the effect of high adhesion

Inactive Publication Date: 2008-12-24
匡建钢
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] PVC plastisol is widely used in the protection of automobile body steel plates. Adhesion is a main characteristic index of PVC plastisol. When PVC plastisol is sprayed on the surface of electrophoretic paint board, if the adhesion is poor, its protective effect will be greatly reduced, resulting in electrophoresis. The paint board is easy to

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0011] Example one:

[0012] Add fatty acids into the reactor, heat up to 220°C and keep it for 4 hours, add N-aminoethylpiperazine and diethylenetriamine, and then continue to react for 1.5 hours under vacuum conditions. At the end of the reaction, cool to 140°C, add dilution Agent, stir evenly and cool to room temperature to obtain adhesion promoter. The percentages of the above-mentioned components in the mass of the synthesized product are 30% for fatty acid, 50% for N-aminoethylpiperazine, 20% for tetraethylenepentamine, and 35% for diluent.

Example Embodiment

[0013] Embodiment two:

[0014] Add fatty acids into the reactor, heat up to 235°C and keep it warm for 5.5 hours, add N-aminoethylpiperazine and triethylenetetramine, and then continue to react for 2.5 hours under vacuum conditions. After the reaction, the temperature is reduced to 155°C, and diluted Agent, stir evenly and cool to room temperature to obtain adhesion promoter. The percentages of the above-mentioned components in the mass of the synthesized product are 20% for fatty acid, 40% for N-aminoethylpiperazine, 40% for diethylenetriamine, and 45% for diluent.

Example Embodiment

[0015] Embodiment three:

[0016] Add fatty acid into the reactor, heat up to 245℃ and keep it for 3 hours, add N-aminoethylpiperazine and tetraethylenepentamine, then continue the reaction under vacuum for 1 hour, after the reaction, cool down to 180℃, add dilution Agent, stir evenly and cool to room temperature to obtain adhesion promoter. The percentages of the above-mentioned components in the mass of the synthesized product are respectively 45% for fatty acid, 35% for N-aminoethylpiperazine, 55% for triethylenetetramine, and 25% for diluent.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Shear strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a low temperature type adhesive force promoter exclusively for PVC plastisol. As the promoter has a relatively lower curing temperature, the promoter can improve the adhesive force of the PVC plastisol without affecting the reaction of other compositions of the plastisol. Therefore, the invention also provides a preparation method thereof. The promoter comprising polyamide polyamine is characterized in that: the polyamide polyamine has 60 to 75 percent of imidazoline content and has an amine value of between 290 and 310 mg KOH/g; the polyamide polyamine is prepared from fatty acid, ethyleneamine and N-aminoethyl piperazine; the fatty acid is made by the self polymerization of unsaturated fatty acid containing 10 to 24 carbon atoms; and the structural formula of ethyleneamine is H2N(CH2CH2NH)nCH2CH2NH2. The preparation method comprises the following steps of: adding fatty acid into a reactor, heating the fatty acid up to between 220 and 260 DEG C, and keeping the temperature for 3 to 7 hours; adding ethyleneamine and N-aminoethyl piperazine into the reactor for continuing to react for 1 to 3 hours under the condition of vacuum pumping; cooling down the reacted solution to between 140 and 180 DEG C after the reaction is finished; and adding a diluent into the reacted solution for stirring evenly, and cooling down the solution to room temperature to obtain the adhesive force promoter.

Description

technical field [0001] The invention relates to the technical field of production of PVC plastisol ingredients, in particular to a special low-temperature adhesion promoter for PVC plastisol and a preparation method thereof. Background technique [0002] PVC plastisol is widely used in the protection of automobile body steel plates. Adhesion is a main characteristic index of PVC plastisol. When PVC plastisol is sprayed on the surface of electrophoretic paint board, if the adhesion is poor, its protective effect will be greatly reduced, resulting in electrophoresis. The paint board is easy to be corroded, and an adhesion promoter is usually added in the preparation process of PVC plastisol to improve the adhesion of PVC plastisol. The curing conditions of common adhesion promoter are: 140℃~150℃ / 30min, The temperature is high, and it is easy to cause the reaction between other components in the accelerator during curing, resulting in aging. Contents of the invention [0003...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J11/08C09J127/06
Inventor 匡建钢
Owner 匡建钢
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap