Preparation of polyester hot-melt adhesive
A polyester hot-melt adhesive and polyolefin technology, applied in the direction of adhesives, etc., can solve the problems of high melt viscosity, low bonding strength, and high production cost, and achieve the effects of reduced melt viscosity, easy coating, and reduced dosage
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0008] The preparation method of the polyester hot-melt adhesive of the present invention includes esterification reaction of dibasic acid and glycol in the presence of a catalyst, and then subjecting the product liquid obtained by the esterification reaction to polycondensation reaction, wherein the method also includes: Aliphatic polyolefin is added to the product liquid obtained by the polycondensation reaction and melted. The aliphatic polyolefin has excellent compatibility with the polyester obtained by the reaction.
[0009] Relative to the total weight of the dibasic acid and the diol, the amount of the aliphatic polyolefin may be 5-70% by weight, and preferably, the amount of the aliphatic polyolefin is 10-35% by weight. The aliphatic polyolefin in the preferred range can further strengthen the bonding strength of the formed polyester hot melt adhesive, and at the same time, can reduce the viscosity of the hot melt adhesive during melting.
[0010] The aliphatic polyolefin...
Example Embodiment
[0021] Example 1
[0022] This example illustrates the preparation method of the polyester hot melt adhesive of the present invention.
[0023] [Esterification reaction]
[0024] Add 180g of terephthalic acid, 52g of isophthalic acid, 20g of sebacic acid, 252g of 1,4-butanediol, and 0.2g of triphenyl phosphite into a three-necked flask, stir and raise the temperature to 170 ℃, then add 0.2g of tetra-n-butyl titanate. The temperature was continued to rise to 210°C and kept for 50 minutes. Water began to distill out after the temperature rose to 190°C. The total amount of water distilled out after 50 minutes at 210°C was 50 grams, indicating that the reaction was basically over.
[0025] In the above esterification reaction, the weight ratio of the diol to the dibasic acid is 1:1, and the weight ratio of the aliphatic dibasic acid to the aromatic dibasic acid in the dibasic acid is 1:11.6, which is relative to the dibasic acid and The total weight of the glycol, the amount of the ca...
Example Embodiment
[0029] Example 2
[0030] This example illustrates the preparation method of the polyester hot melt adhesive of the present invention.
[0031] [Esterification reaction]
[0032] Add 180 g of terephthalic acid, 72.5 g of isophthalic acid, 40 g of sebacic acid, 270 g of 1,4-butanediol, and 0.23 g of triphenyl phosphite into a three-necked flask, stir and heat to At 170°C, 0.23 g of tetra-n-butyl titanate was then added. The temperature was continued to rise to 210°C and kept for 60 minutes, where water began to distill out after the temperature rose to 190°C, and the total distilled amount of water after 60 minutes at 210°C was 57 grams, indicating that the reaction was basically over. Then the temperature in the three-necked flask was increased to 240°C and kept at a pressure of 100 Pa for 20 minutes.
[0033] In the above esterification reaction, the weight ratio of the diol to the dibasic acid is 1:1.08, and in the dibasic acid, the weight ratio of the aliphatic dibasic acid to ...
PUM
Property | Measurement | Unit |
---|---|---|
Melt viscosity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap