Special crumpling resin for processing leather surface and preparing method thereof

A special and leather technology, applied in the field of special kneading resin, can solve the problems of weak lubricity, wear resistance, color fastness to bending, etc., and achieve the effect of strong lubricity and smoothness.

Inactive Publication Date: 2009-05-13
沈雪峰
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the leather surface is easy to change color, not easy to withstand high temperature, not wear-resistant, not scratch-resistant, not resistant to twists and turns, poor color fastness, oily and smooth, weak and not durable, so it is necessary to mix a special rubbing resin on the leather surface

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] NC: 45--55, CP: 14--18, butyl acetate: 35--50, dimethylformamide: 40--60, butanone: 40--60.

[0011] According to above-mentioned components and proportioning, a kind of method for the special kneading resin of leather surface, its process step is:

[0012] 1) Stir butyl acetate, dimethylformamide, NC, and CP according to the proportion for 10 minutes;

[0013] 2) At this time, add butanone and stir for 2 minutes to obtain the finished product.

Embodiment 2

[0015] NC: 50, CP: 15, butyl acetate: 40, dimethylformamide: 50, butanone: 50.

[0016] According to above-mentioned components and proportioning, a kind of method for the special kneading resin of leather surface, its process step is:

[0017] 1) Stir butyl acetate, dimethylformamide, NC, and CP according to the proportion for 10 minutes;

[0018] 2) At this time, add butanone and stir for 2 minutes to obtain the finished product.

[0019] Wherein embodiment 2 is the best embodiment, and the product that it makes is the best product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses special graining resin for treating the leather surface and a manufacturing method thereof. The special graining resin for treating the leather surface comprises the following compositions: 45 to 55 portions of NC, 14 to 18 portions of CP, 35 to 50 portions of butyl acetate, 40 to 60 portions of dimethyl formamide and 40 to 60 portions of butanone. The manufacturing method comprises the following technological steps: 1) the butyl acetate, the dimethyl formamide, the NC and the CP are stirred for 10 minutes according to the mixture ratio; and 2) the butanone is added into the mixture and stirred for 2 minutes, and the finished product can be obtained. The special graining resin for treating the leather surface has the advantages that the requirements on abrasion resistance, scraping resistance, flection resistance, the color fastness and so on meet the international standards; water resistance, moisture permeability, water pressure resistance, solvent resistance, strong acid and strong alkali resistance, external moisture variation resistance and moisture variation resistance meet the standards; and the oily light sense is strong and permanent.

Description

Technical field: [0001] The invention relates to a treatment agent for leather surface, in particular to a special embossing resin for leather surface treatment. Background technique: [0002] At present, leather products such as clothing, luggage, decoration, packaging, military leather and other surface treatment methods are various, including color-changing crazy horse, high-solid cracking, high-solid ironing, bright surface treatment agent, matte surface treatment agent, cracking Scorching, bright crystal high solid, etc., among which the surface gloss technology is relatively mature and popular, such as various existing bright surface treatment agents, bright crystal high solid, high solid ironing. However, the leather surface is easy to change color, not easy to withstand high temperature, not wear-resistant, not scratch-resistant, not resistant to twists and turns, poor color fastness, oily and smooth, weak and not durable, so it is necessary to mix a special rubbing ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine