Preparation method of N-N'-methylene diacrylamide
A technology of methylenebisacrylamide and acrylamide, which is applied in organic chemistry and other fields, can solve problems such as high production cost, unstable products, and environmental pollution, and achieve the effects of low production cost, improved product quality, and fewer by-products
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0021] A preparation method of N-N′-methylenebisacrylamide, the steps of the preparation method are:
[0022] (1). Add 245kg of water to the reactor, turn on the stirring, and heat to 70°C;
[0023] (2). Then add 75kg of acrylamide, 105kg of formaldehyde, and at the same time add the polymerization inhibitor p-hydroxyanisole, the amount of which is 100~500ppm, and stir at 40℃ for 1 hour to fully react;
[0024] (3). Then add 75kg of acrylamide and 45kg of catalyst hydrochloric acid, heat to 70°C with stirring, react for 2 hours, and cool for 48 hours;
[0025] (4). The product is filtered out and dried at 80°C to obtain the finished product of N-N'-methylenebisacrylamide.
Embodiment 2
[0027] A preparation method of N-N′-methylenebisacrylamide, the steps of the preparation method are:
[0028] (1). Add 250kg of water into the reactor, turn on the stirring, and heat to 65°C;
[0029] (2). Then add 75kg of acrylamide, 100kg of formaldehyde, and at the same time add the concentration inhibitor phenothiazine, the amount of which is 50~300ppm, and stir for 1.2 hours at 45℃ to fully react;
[0030] (3). Then add 75kg of acrylamide and 50kg of catalyst sulfuric acid, heat to 65°C with stirring, react for 2.3 hours, and cool for 43 hours;
[0031] (4). The product is filtered out and dried at 75°C to obtain the finished product of N-N'-methylenebisacrylamide.
PUM

Abstract
Description
Claims
Application Information

- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com