A technology of activated coke and activation treatment, which is applied in the direction of separation methods, chemical instruments and methods, and other chemical processes. It can solve problems such as endangering human health, destroying the ecological environment, and affecting human genes, etc., and achieves good desulfurization effect and large accumulation ratio. , The effect of high activation treatment yield
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0071] Example 1: Preparation and Performance Measurement of Active Coke
[0072] 1. Preparation of active coke
[0073] About 1.6t of Inner Mongolia lignite and about 0.4t of Hebei anthracite are mixed and pulverized. The particle size of pulverized coal is less than 200 mesh, about 180 mesh. Add about 0.84t of high-temperature coal tar and about 0.06t of catalyst MgO to the coal raw material particles at 70°C and knead for 20min, and then press at 800kgf / cm 2 Extruded to obtain dry charcoal strips. The dry charcoal strips were subjected to carbonization treatment and steam activation treatment in an external heat type carbonization and activation rotary furnace. The final temperature of the carbonization treatment was 650°C and the time was 30 minutes, and the activation treatment temperature was 850°C and the activation treatment time was 30 minutes. Water vapor is about 14t.
[0074] 2. Performance measurement
[0075] Active coke with a particle diameter (Φ) of 9 mm w...
Embodiment 2
[0076] Embodiment 2: Preparation and performance measurement of active coke
[0077] 1. Preparation of active coke
[0078] About 1.2t of Inner Mongolia lignite and about 0.8t of Hebei anthracite are mixed and pulverized. The particle size of pulverized coal is 325 mesh. Add about 0.8t of high-temperature coal tar and catalyst K to coal raw material particles at 50°C 2 CO 3 Knead about 0.05t for 25min, then press 1000kgf / cm 2 Extruded to obtain dry charcoal strips. The dry charcoal strips were subjected to carbonization treatment and steam activation treatment in an external heat type carbonization and activation rotary furnace. The final temperature of the carbonization treatment was 650°C for 30 minutes, the activation treatment temperature was 850°C, and the activation treatment time was 50 minutes. The water vapor is about 16t.
[0079] 2. Performance measurement
[0080] Active coke with a particle size (Φ) of 12 mm was obtained, about 1.70 t, with a yield of 75%. ...
Embodiment 3
[0082] Example 3: Preparation and Performance Measurement of Active Coke
[0083] 1. Preparation of active coke
[0084] Mix about 1.33t of Inner Mongolian lignite and about 0.57t of Hebei anthracite to make pulverized coal. The particle size of coal powder is 200 mesh. Add about 0.79t of high-temperature coal tar and mixed catalysts MgO and K to the raw coal particles at 60°C. 2 CO 3 About 0.06t kneading for 30min, then pressure 900kgf / cm 2 Extruded to obtain dry charcoal strips. The dry charcoal strips were subjected to carbonization treatment and steam activation treatment in an external heat type carbonization and activation rotary furnace. The carbonization treatment temperature was 600°C, the carbonization treatment time was 30 minutes, the activation treatment temperature was 800°C, and the activation treatment time was 40 minutes. The water vapor is about 17t.
[0085] 2. Performance measurement
[0086] About 1.78t of activated coke with a particle diameter (Φ) o...
PUM
| Property | Measurement | Unit |
|---|---|---|
| particle size (mesh) | aaaaa | aaaaa |
| particle diameter | aaaaa | aaaaa |
| particle size (mesh) | aaaaa | aaaaa |