Thermally conductive and insulating polycarbonate composition and preparation method thereof
A polycarbonate, thermally conductive and insulating technology, applied in the field of polycarbonate compositions and their preparation, can solve problems such as loss of mechanical properties, and achieve the effects of increasing thermal conductivity, reducing dosage, and improving mechanical properties
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0031] Take 300g of Al with an average particle size of 5 μm and a thermal conductivity of 42W / m.K 2 o 3 , add 10g of vinyltrimethoxysilane coupling agent diluted with 2 times ethanol, and stir in a high-speed mixer for 30min for surface treatment. With 150g linear low density polyethylene (LLDPE, brand 7144), 307g above-mentioned surface-treated Al 2 o 3 1.5g of antioxidant B215 is dispersed and mixed by a high-speed mixer, and then melted and extruded by a twin-screw extruder in the range of 170-180°C to obtain a heat-conducting masterbatch, wherein the feeding section is 170°C, the melting section is 180°C, and the homogenization section 180°C; then disperse and mix the thermally conductive masterbatch, 500g polycarbonate (viscosity average molecular weight: 10000), 40g linear low density polyethylene grafted maleic anhydride and 1.5g antioxidant B215 through a high-speed mixer, and pass through a twin-screw Machine melt extrusion, drying, pelletizing and packaging. The...
Embodiment 2
[0033] Take 500g of MgO with an average particle size of 4μm and a thermal conductivity of 48W / m.K, add 15g of γ-glycidoxypropyltrimethoxysilane diluted 3 times with ethanol, and stir in a high-speed mixer for 30min for surface treatment. After dispersing and mixing 164g polypropylene (grade 425), 512g surface-treated MgO, and 2g antioxidant B225 through a high-speed mixer, knead at 180-190°C through a double-roller kneader to obtain a thermally conductive masterbatch; Thermally conductive masterbatch, 250g polycarbonate (viscosity average molecular weight: 20,000), 70g MBS and 2g antioxidant B225 are dispersed and mixed by a high-speed mixer, melt-extruded by a twin-screw machine, dried, pelletized, and packaged. The temperature of each zone of the used twin-screw extruder screw is 245-270°C, wherein the feeding section is 245°C, the melting section is 260°C, and the homogenizing section is 270°C.
Embodiment 3
[0035]Take 400g of SiC with an average particle size of 2μm and a thermal conductivity of 180W / m.K, add 15g of titanate coupling agent isopropyl triisostearyl titanate (OL-T999) diluted 4 times with ethanol, and put it in a high-speed mixer Stir for 25min for surface treatment. After dispersing and mixing 200g of ethylene-octene copolymer (brand 8400), 415g of surface-treated SiC, and 2.5g of antioxidant 626 in a high-speed mixer, they were kneaded at 180-190°C by a double-roller kneader to obtain thermal conductivity Masterbatch; then heat-conducting masterbatch, 330g polycarbonate (viscosity-average molecular weight is 40000), 50g SMA and 2.5g antioxidant 626 are dispersed and mixed through a high-speed mixer, melted and extruded by a twin-screw extruder, dried, Packed after dicing. The temperature of each zone of the used twin-screw extruder screw is 245-270°C, wherein the feeding section is 245°C, the melting section is 260°C, and the homogenizing section is 270°C.
PUM
Property | Measurement | Unit |
---|---|---|
The average particle size | aaaaa | aaaaa |
Notched impact strength | aaaaa | aaaaa |
Notched impact strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap