Noble metal preparation with stable microwave resistant function and manufacturing process and application thereof

A precious metal preparation technology, applied in the field of precious metal preparations, can solve the problems that did not mention the anti-microwave oven performance of precious metal preparations

Active Publication Date: 2010-07-21
SHENZHEN YONG FENG YUAN IND
View PDF1 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this patent does not mention the microwave resistance of precious metal formulations

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Lustrous Precious Metal Preparations

[0036] Gold-tert-Dodecylmercaptide

30.9% Gold

(30.9% Au)

32.6％

Silver-t-Dodecyl Mercaptan Resinate

(Silver-tert-Dodecylmercaptide)

20% silver

(20%Ag)

5.0％

Rhodium sulforesinate in pine oil (Rhodium sulforesinate in

terpineol)

5% rhodium

1.4％

Silicon resinate, soluble in pine oil (Siliconresinate in Pine Oil)

10% silicon

2.1％

Bismuth resinate in terpineol

5% bismuth

22％

Aluminum carboxylate in toluene

7% aluminum

2.1％

Zirconium-2-ethylhexanoate

5% zirconium

0.9％

[0037] Gold-tert-Dodecylmercaptide

30.9% Gold

(30.9% Au)

32.6％

Indium trishydroxymethylaminomethane (Tris) compound, soluble in toluene (Indium

acetonylacetonate in toluene)

4% indium

1.8％

Nickel resinate in terpineol

5% Nickel

2.1％

Polyam...

Embodiment 2

[0041] Lustrous Precious Metal Preparations

[0042] Gold-t-dodecyl mercaptan resinate (Gold

-tert-Dodecylmercaptide)

30.9% Gold

(30.9% Au)

20.6％

Platinum sulforesinate

10% Platinum

(10%Pt)

4.0％

Rhodium sulforesinate in pine oil (Rhodium sulforesinate in

terpineol)

5% rhodium

1.4％

Silicon resinate, soluble in pine oil (Siliconresinate in Pine Oil)

10% silicon

2.1％

Bismuth resinate in terpineol

5% bismuth

22％

[0043] Gold-t-dodecyl mercaptan resinate (Gold

-tert-Dodecylmercaptide)

30.9% Gold

(30.9% Au)

20.6％

Aluminum carboxylate, soluble in toluene (Aluminum carboxylate in

toluene)

7% aluminum

2.1％

Zirconium-2-ethylhexanoate

5% zirconium

0.9％

Indium trishydroxymethylaminomethane (Tris) compound, soluble in toluene (Indium

acetonylacetonate in toluene)

4% indium

1.8％

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a noble metal preparation with a stable microwave resistant function, belonging to the field of noble metal preparation, and comprising a noble metal compound. The noble metal preparation of the invention can be used for direct and / or indirect screen printing on a silicate substrate surface of ceramics, glass, refined ceramics or porcelain and the like to form a noble metal decorative pattern (decalcomania), wares which comprise the decorative pattern can be directly heated in a microwave oven, and the integrality and color authenticity of the noble metal decorative pattern on the wares can be kept.

Description

technical field [0001] The invention belongs to the technical field of noble metal preparations used on the surface of silicate substrates, and in particular relates to a noble metal preparation with a stable microwave-resistant function, and a preparation process and application of the noble metal preparation. Background technique [0002] Gold, platinum, palladium and other glossy precious metal preparations used to decorate glass, ceramics, and white porcelain are organic metal compound solutions, and the solution contains organic bearing media such as sulfur resin hydrochloric acid. During the firing process, the organic carrier medium is completely decomposed. In addition, they usually contain sulfur resin hydrochloric acid of rhodium, bismuth, silver, silicon. [0003] In the operating instructions and technical data provided by microwave oven manufacturers, it is usually written that when heating food in a microwave oven, it is not allowed to use tableware with metal...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C17/06C04B41/88
Inventor 刘权辉史蒂芬刘权耀
Owner SHENZHEN YONG FENG YUAN IND