Production method of single-side low temperature aluminum-plastic compound belt

A technology of an aluminum-plastic composite tape and a production method, which is applied in the field of thermal processing and manufacturing, can solve the problems of reduced service life, complicated production and processing process, easy corrosion, etc., and achieves reduced working temperature and airflow, low initial bonding temperature, high heat The effect of sealing and bonding performance

Active Publication Date: 2010-07-28
无锡速达新材料科技股份有限公司
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In the existing technology, the composite tapes currently used for cables and optical cables have poor shielding performance, noise, crosstalk and other phenomena often occur, and the anti-interference ability is poor, and it has high requirements for the use environment. Under the environment, it is easy to be affected by moisture and easy to corrode, which greatly reduces the service life and virtually increases the production cost
At the same time, the heating temperature of the general composite tape is relatively strict in the production process of cables and optical cables. The entire production and processing process is complicated and cumbersome, and the product quality often does not meet the requirements.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Embodiment 1: A production method of a single-sided low-temperature aluminum-plastic composite tape of the present invention adopts the following process steps:

[0030] 1. Selection of materials for single-sided low-temperature aluminum-plastic composite tape:

[0031] Raw material aluminum strip: use 8011-O aluminum strip with a thickness of 0.15mm and a width of 500mm. Main standards: tensile strength ≥ 16Mpa, elongation at break ≥ 15%, thickness tolerance ± 8%. The PE polyethylene plastic film produced by EAA DuPont Company is selected. The thickness of PE polyethylene plastic film is 0.05mm and the width is 500mm. %, heat seal strength ≥ 18.5N / cm, peel strength ≥ 6.3N / cm, delamination: no delamination.

[0032] 2. Unwinding process

[0033] The aluminum strip roll frame is placed on the unwinding roller, and the unwinding roller is connected to the magnetic powder brake, which uses magnetic powder to transmit torque. Equipment magnetic powder brake: model CZ40,...

Embodiment 2

[0050] Embodiment 2: A production method of a single-sided low-temperature aluminum-plastic composite tape of the present invention adopts the following process steps:

[0051] 1. Selection of materials for single-sided low-temperature aluminum-plastic composite tape:

[0052] Raw material aluminum strip: use 8011-O aluminum strip with a thickness of 0.20mm and a width of 500mm. Main standards: tensile strength ≥ 16Mpa, elongation at break ≥ 15%, thickness tolerance ± 8%. The PE polyethylene plastic film produced by EAA DuPont Company is selected. The thickness of PE polyethylene plastic film is 0.05mm and the width is 500mm. %, heat seal strength ≥ 18.5N / cm, peel strength ≥ 6.3N / cm, delamination: no delamination.

[0053] 2. Unwinding process

[0054] The aluminum strip roll frame is placed on the unwinding roller, and the unwinding roller is connected to the magnetic powder brake, which uses magnetic powder to transmit torque. Equipment magnetic powder brake: model CZ40,...

Embodiment 3

[0071] Embodiment 3: A production method of a single-sided low-temperature aluminum-plastic composite tape of the present invention adopts the following process steps:

[0072] 1. Selection of materials for single-sided low-temperature aluminum-plastic composite tape:

[0073] Raw material aluminum strip: use 8011-O aluminum strip with a thickness of 0.185mm and a width of 500mm. Main standards: tensile strength ≥ 16Mpa, elongation at break ≥ 15%, thickness tolerance ± 8%. The PE polyethylene plastic film produced by EAA DuPont Company is selected. The thickness of PE polyethylene plastic film is 0.05mm and the width is 500mm. %, heat seal strength ≥ 18.5N / cm, peel strength ≥ 6.3N / cm, delamination: no delamination.

[0074] 2. Unwinding process

[0075] The aluminum strip roll frame is placed on the unwinding roller, and the unwinding roller is connected to the magnetic powder brake, which uses magnetic powder to transmit torque. Equipment magnetic powder brake: model CZ40...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Widthaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a production method of a single-side low temperature aluminum-plastic compound belt, belonging to the field of hot processing manufacturing technology. The production method mainly adopts an aluminum belt and a polyethylene (PE) plastic film as raw materials and comprises the working procedures of unwinding, preheating, compounding, cooling, winding, cutting, checking of finished products and the like, and finally the single-side low temperature aluminum-plastic compound belt can be produced. The single-side low temperature aluminum-plastic compound belt has better shielding performance, strong anti-interference capability, lower initial bonding temperature, higher heat-seal adhesive property and good electrical conductivity. The tensile strength is more than or equal to 54MPa, the elongation at break is more than or equal to 15%, and the peel strength between the aluminum belt and the PE plastic film is more than or equal to 6.13N / cm.

Description

technical field [0001] The invention relates to a production method of a single-sided low-temperature aluminum-plastic composite tape, specifically a material used in the manufacture of electric cables and optical cables, and belongs to the technical field of thermal processing and manufacturing. Background technique [0002] In the existing technology, the composite tapes currently used for cables and optical cables have poor shielding performance, noise, crosstalk and other phenomena often occur, and the anti-interference ability is poor, and it has high requirements for the use environment. Under the environment, it is easy to be affected by moisture and easy to corrode, which greatly reduces the service life and virtually increases the production cost. At the same time, the heating temperature of the general composite tape is relatively strict during the production process of electric cables and optical cables. The entire production and processing process is complicated ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B32B37/06B32B37/10
Inventor 袁齐阳
Owner 无锡速达新材料科技股份有限公司