Magnesium-based block metal glass composite material and preparation method thereof

A technology of metallic glass and composite material, applied in the field of magnesium-based endogenous bulk metallic glass composite material and its preparation, can solve problems such as lack of practicability, and achieve the effects of avoiding uneven structure, high strength and uniform performance

Inactive Publication Date: 2011-01-12
NANJING UNIV OF SCI & TECH
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Obviously, this

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Magnesium-based block metal glass composite material and preparation method thereof
  • Magnesium-based block metal glass composite material and preparation method thereof
  • Magnesium-based block metal glass composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0017] The preparation method of a magnesium-based bulk metallic glass composite material of the present invention comprises the following steps:

[0018] The first step: prepare the high melting point component in the predetermined nominal composition alloy into a master alloy by the arc melting method;

[0019] The second step: put the broken intermediate alloy into the container together with Mg and Zn, and use the induction melting method to make the master alloy;

[0020] The third step: the master alloy is remelted by induction melting method, and the liquid master alloy is made into profiles by low-pressure copper mold blow casting method;

[0021] Step 4: After grinding and cleaning the profile, put it into a pre-treated crucible, and heat the bar to a fully melted or solid-liquid two-phase state by induction melting.

[0022] In the fourth step, the profiles are induced to melt under the protection of inert gas to prevent volatilization. The pulling rate of the seque...

Example Embodiment

[0032] Example 1

[0033] (1) Selection of raw materials

[0034] The purity of each metal component selected for preparing the master alloy in the present invention is as shown in the table: the formula of the composite material is Mg77Cu6Ni6Y6Zn5 (atomic percentage).

[0035] Table 1 The purity (%) of the selected metal component for preparing the master alloy ingot

[0036]

[0037] (2) Preparation of master alloy

[0038] First, under the condition of Ti inhalation and high-purity argon protection, a self-developed non-consumable arc melting furnace is used to melt the master alloy ingot. The specific procedures for the preparation of master alloy ingots are as follows:

[0039] After the surface of the metal raw materials Cu and Y with high melting point are mechanically polished to remove the oxide scale on the surface, the materials are prepared according to the selected / designed composition ratio; the prepared materials are put into the melting furnace according ...

Example Embodiment

[0051] Example 2

[0052] Using the same preparation method as Example 1, the formula of the composite material is Mg74Cu7Ni7Y7Zn5, and the pulling rate of sequential solidification is 5 mm / s. The prepared composite material has a uniform structure and a compressive plasticity of 12.3%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a magnesium (Mg)-based block metal glass composite material and a preparation method thereof. The Mg-based block metal glass composite material of the invention has the following components: 60 to 90 atomic percent of Mg, 1 to 15 atomic percent of Cu, 1 to 15 atomic percent of Ni, 1 to 15 atomic percent of Y and 1 to 15 atomic percent of Zn. The preparation method comprises the following steps of: preparing high-melting-point components in a reservation name component alloy into an intermediate alloy by an arc melting method; crushing the intermediate alloy; placing the crushed intermediate alloy, the Mg and the Zn into a contained together; preparing into a master alloy by adopting an induction melting method; remelting the master alloy by adopting the induction melting method; preparing liquid master alloy into a sectional bar by a low-pressure copper mould blow casting method; putting the sectional bar into a pretreated crucible after grinding and washing; heating a steel bar to a completely molten state or a solid-liquid two-phase state by adopting the induction melting method; and molding by adopting a consecutive solidification process after keeping temperature. The Mg-based block metal glass composite material prepared by the preparation method thereof has the advantages of obvious room temperature plasticity, structural homogeneity, and excellent performance.

Description

technical field [0001] The invention belongs to the technical field of preparation of magnesium-based bulk metallic glass materials, and particularly relates to a magnesium-based endogenous bulk metallic glass composite material with obvious room-temperature plasticity, uniform structure and excellent performance and a preparation method thereof. Background technique [0002] Compared with traditional crystalline magnesium alloys, the strength and specific strength of magnesium-based bulk metallic glasses are doubled, and the problem of corrosion resistance has also been improved. However, magnesium-based bulk metallic glasses have room-temperature brittleness common to bulk metallic glasses, which limits their application in engineering structural materials. Therefore, overcoming the room temperature brittleness of magnesium-based bulk metallic glasses has become the most cutting-edge research hotspot at home and abroad. [0003] With the continuous revelation of the natur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C45/00
Inventor 陈光张旭亮杜宇雷
Owner NANJING UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products