Low-cost magnesia converter lining patching material and preparation method thereof
A low-cost technology for furnace lining repair, applied in the field of low-cost magnesia converter lining repair material and its preparation, can solve the problems affecting the production cost of iron and steel enterprises, high cost, and large amount of repair materials, so as to achieve sustainable development and reduce Production cost, the effect of increasing economic benefits
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0020] A low-cost magnesia converter lining repair material is made of the following materials in parts by weight:
[0021] 10 parts of large particles of 5-8mm waste refractories; 10 parts of medium particles of 3-5mm waste refractories; 20 parts of fine particles of 1-3mm waste refractories; 15 parts of fine particles of 0-1mm waste refractories; waste refractories ≤ 0.088mm 25 parts of powder, 10 parts of asphalt; 5 parts of iron oxide red.
[0022] Add the above-mentioned waste refractory materials of various particle sizes, asphalt and red iron oxide into the mixer according to the stated weight ratio, stir and mix until uniform, then add 2 parts of waste engine oil into the mixer, continue to stir evenly, the total mixing time is 5-20 minutes , can be used for bagging or construction.
Embodiment 2
[0024] A low-cost magnesia converter lining repair material is made of the following materials in parts by weight:
[0025] 20 parts of large particles of 5-8mm waste refractories; 15 parts of medium particles of 3-5mm waste refractories; 15 parts of fine particles of 1-3mm waste refractories; 10 parts of fine particles of 0-1mm waste refractories; waste refractories ≤ 0.088mm 20 parts of powder, 11 parts of asphalt; 4 parts of red iron oxide.
[0026] Add the above-mentioned waste refractory materials, asphalt and iron oxide red of each particle size into the mixer according to the stated weight ratio, stir and mix until uniform, then add 2 parts of waste diesel oil into the mixer, continue to stir evenly, the total mixing time is 5-20 minutes , can be used for bagging or construction.
Embodiment 3
[0028] A low-cost magnesia converter lining repair material is made of the following materials in parts by weight:
[0029] 15 parts of large particles of 5-8mm waste refractories; 15 parts of medium particles of 3-5mm waste refractories; 20 parts of fine particles of 1-3mm waste refractories; 10 parts of fine particles of 0-1mm waste refractories; 20 parts of powder, 9 parts of asphalt; 6 parts of iron oxide red.
[0030] Add the above-mentioned waste refractory materials of various particle sizes, asphalt and red iron oxide into the mixer according to the stated weight ratio, stir and mix until uniform, then add 3 parts of waste engine oil into the mixer, continue to stir evenly, the total mixing time is 5-20 minutes , can be used for bagging or construction.
PUM
Property | Measurement | Unit |
---|---|---|
Granularity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap