Thermo-sensitive polymeric hydrogel and preparation method thereof
A polymer hydrogel and temperature-sensitive technology, which is applied in the field of temperature-sensitive polymer hydrogel and its preparation, and achieves the effects of good application prospect, good temperature sensitivity and simple preparation process
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0023] Take 10kg of acrylic acid, 44.17kg of lauryl alcohol polyoxyethylene ether (polymerization degree is 3), 0.016kg of inhibitor hydroquinone, 0.813kg of catalyst p-toluenesulfonic acid, heat reaction at 110°C for 6 hours; after the reaction is completed, Acrylic acid-lauryl polyoxyethylene ether copolymer is obtained; 6kg of copolymer, acrylic acid 1.161kg, butyl acrylate 2.065kg, initiator benzoyl peroxide 0.046kg, crosslinking agent ethylene glycol dimethacrylate 0.092kg , polymerized at 80°C for 7 hours to obtain a thermosensitive hydrogel with a phase transition temperature of 15°C. At around 15°C, the volume of the gel shrinks by about 25%.
Embodiment 2
[0025] Take 10kg of acrylic acid, 50.28kg of lauryl alcohol polyoxyethylene ether (polymerization degree is 4), 0.016kg of inhibitor hydroquinone, 0.904kg of catalyst p-toluenesulfonic acid, heat and react at 105°C for 5.5 hours; after the reaction is completed, Obtain acrylic acid-lauryl polyoxyethylene ether copolymer; By copolymer 6kg, acrylic acid 1.038kg, butyl acrylate 1.846kg, initiator benzoyl peroxide 0.044kg, crosslinking agent ethylene glycol dimethacrylate 0.178kg , polymerized at 90°C for 6 hours to obtain a thermosensitive hydrogel with a phase transition temperature of 22°C. At around 22°C, the volume of the gel shrinks by about 30%.
Embodiment 3
[0027] Take 10kg of acrylic acid, 68.61kg of lauryl alcohol polyoxyethylene ether (the degree of polymerization is 7), 0.016kg of inhibitor hydroquinone, and 1.179kg of catalyst p-toluenesulfonic acid, and heat the reaction at 107°C for 5 hours; after the reaction is completed, Obtain acrylic acid-lauryl polyoxyethylene ether copolymer; Copolymer 6kg, acrylic acid 0.788kg, butyl acrylate 1.401kg, initiator benzoyl peroxide 0.041kg, crosslinking agent ethylene glycol dimethacrylate 0.246kg , polymerized at 85°C for 6.5 hours to obtain a thermosensitive hydrogel with a phase transition temperature of 68°C. At around 68°C, the volume of the gel shrinks by about 45%.
PUM
Property | Measurement | Unit |
---|---|---|
Phase transition temperature | aaaaa | aaaaa |
Phase transition temperature | aaaaa | aaaaa |
Phase transition temperature | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap