Flame-retardant phenolic paint

A kind of phenolic paint and phenolic technology, which is applied in the direction of fireproof coatings, coatings, etc., can solve the problems of large-scale fires, failure to achieve flame-retardant effects, and phenolic paints without flame-retardant functions, so as to prevent combustion and achieve remarkable flame-retardant effects , The effect of eliminating potential safety hazards

Inactive Publication Date: 2012-11-14
SUZHOU CUIZHI NEW TECH DEV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to overcome that the existing phenolic paint has no flame retardant function, it will burn in case of fire and cannot achieve the effect of flame retardant, thus causing large-scale fires and serious The disadvantage of potential safety hazards, the invention provides an oil flame retardant phenolic paint

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flame-retardant phenolic paint

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] In a 400ml flask, add 40 parts of phenolic varnish, 18 parts of tris(β-chloroethyl) phosphate (TCEP), 8 parts of triethyl phosphate (TEP), tris(2-chloropropyl) phosphate ( TCPP) 12 parts, fully stirred at room temperature for 35 minutes to obtain flame retardant phenolic varnish.

Embodiment 2

[0016] In a 400ml flask, add 55 parts of phenolic varnish, 28 parts of tris(β-chloroethyl) phosphate (TCEP), 12 parts of triethyl phosphate (TEP), tris(2-chloropropyl) phosphate ( TCPP) 8 parts, fully stirred at room temperature for 35 minutes to obtain flame retardant phenolic varnish.

Embodiment 3

[0018] In a 400ml flask, add 50 parts of phenolic varnish, 24 parts of tris(β-chloroethyl) phosphate (TCEP), 16 parts of triethyl phosphate (TEP), tris(2-chloropropyl) phosphate ( TCPP) 10 parts, fully stirred at room temperature for 35 minutes to obtain flame retardant phenolic paint.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides flame-retardant phenolic paint. The flame-retardant phenolic paint is characterized by comprising the steps of: orderly adding 40-55 parts of phenolic paint vehicle, 18-28 parts of phosphate tri(2-chloropropyl) ester (TCEP), 12-18 parts of triethyl phosphate (TEP), and 8-12 parts of phosphate tri(2-chloropropyl) ester (TCPP) in parts by weight into a flask of 400ml; and fully agitating the mixture for 35 minutes at the normal temperature to obtain the flame-retardant phenolic paint. The flame-retardant phenolic paint rapidly becomes carbon in case of a fire, isolates oxygen and realizes flame retardance; the flame-retardant effect is significant; and a big fire is avoided, and potential safety hazards are removed.

Description

technical field [0001] The invention relates to a flame-retardant phenolic varnish. Background technique [0002] Phenolic paint is widely used in all kinds of construction projects, as well as in the decoration of homes and public places. With the improvement of people's living standards and the enhancement of fire protection awareness, especially the warnings of numerous fire accidents, people have put forward higher requirements for the flame-retardant and fire-resistant properties of various household materials. At present, there are also some flame retardant phenolic varnishes, such as Chinese patent: a phenolic varnish (201010513316.2), which provides a phenolic varnish consisting of light calcium carbonate, phenolic varnish, tung oil, solvent oil, cobalt naphthenate, Manganese naphthenate, lead naphthenate, red powder, composition, its weight ratio is: phenolic paint 70; light calcium carbonate 4-6; tung oil polymer 6-8; No. ; 2% cobalt naphthenate 0.5-0.6; 2% naph...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D161/06C09D7/12C09D5/18
Inventor 孟繁茂冷泠
Owner SUZHOU CUIZHI NEW TECH DEV