Flame-retardant glass fiber-reinforced ABS/PA66 alloy material with high CTI value and high GWIT value

A technology of alloy materials and glass fiber, which is applied in the field of ABS/PA66 alloy materials, can solve the problems of unsuitable electricity environment, low CTI value and GWIT value, etc., so as to improve oxidation resistance, processing fluidity and smoothness sexual effect

Inactive Publication Date: 2015-06-03
SHANGHAI SUNNY
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Some traditional methods are (GF+decabromodiphenylethane+antimony trioxide) compound system, (GF+brominated polystyrene+antimony trioxide) compound system, but the CTI value and GWIT of these compound systems The value is not high, not suitable for high-demand electricity environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flame-retardant glass fiber-reinforced ABS/PA66 alloy material with high CTI value and high GWIT value
  • Flame-retardant glass fiber-reinforced ABS/PA66 alloy material with high CTI value and high GWIT value
  • Flame-retardant glass fiber-reinforced ABS/PA66 alloy material with high CTI value and high GWIT value

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～6

[0031] The high CTI value, high GWIT value flame-retardant glass fiber reinforced ABS / PA66 alloy material of Examples 1-6, each component contained is as shown in Table 1, wherein, ABS is commercially available acrylonitrile-butadiene-styrene , PA66 is a commercially available polyhexamethylene adipamide with an intrinsic viscosity of 2.8dl / g, and the glass fiber is an alkali-free glass fiber whose surface is treated with a silane coupling agent (specifically: add the alkali-free glass fiber to the silane coupling agent in which the surface is treated with a silane coupling agent), the compatibilizer is commercially available maleic anhydride grafted ABS, and the compound flame retardant A is a mixture of three components, and its mass percentage is BPS: 50%, Magnesium hypophosphite: 25%, talcum powder: 25%, compound flame retardant B is BPS (brominated polystyrene), GF (non-reactive nitrogen-containing, phosphorus-containing flame retardant) with a mass ratio of 2:1:1 Flame r...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a flame-retardant glass fiber-reinforced ABS / PA66 alloy material with a high CTI value and a high GWIT value. The alloy material comprises the following components: by weight, 22.5 to 41% of ABS, 22.5 to 41% of PA66, 6 to 20% of a compound fire retardant, 3 to 15% of antimonony oxide, 20 to 30% of a glass fiber, 2 to 10% of a compatilizer, 0.1 to 1% of an anti-oxidant and 0.1 to 1% of a metallic oxide. In preparation of the alloy material, all the components are added into a high-speed mixer for mixing for 2 to 5 min, and then discharging and extrusion granulation are carried out, wherein extrusion temperature is 220 to 255 DEG C and screw revolution is 30 to 40 Hz. Compared with the prior art, the alloy material provided by the invention has the advantages of a high glow wire temperature, a high tracking index, environment-friendliness, balanced comprehensive properties and the like and can be extensively used for low-voltage electronic capacitor shells, load break switches, carbon brush supports and molded case circuit breakers.

Description

technical field [0001] The invention relates to an ABS / PA66 alloy material, in particular to a flame-retardant glass fiber reinforced ABS / PA66 alloy material with high CTI value and high GWIT value. Background technique [0002] ABS resin features: the resin has good comprehensive properties, high impact strength, chemical stability, and good electrical properties; it has good fusion properties with plexiglass, and can be made into two-color plastic parts, and the surface can be chrome-plated and spray-painted; it has high impact resistance. , high heat resistance, flame retardant, enhanced, transparent and other grades; fluidity is a little worse than HIPS, better than PMMA, PC, etc., and good flexibility; Nylon (Nylon), Chinese name polyamide, English name Polyamide (referred to as PA), It is a general term for thermoplastic resins containing repeating amide groups—[NHCO]—on the main molecular chain. Its name depends on the specific number of carbon atoms in the synthetic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L55/02C08L77/06C08L25/04C08K13/06C08K9/06C08K7/14C08K3/22C08K3/32C08K3/34
Inventor 杨涛郭建鹏
Owner SHANGHAI SUNNY
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com