Ultra-high-temperature carbonization process
An ultra-high temperature and process technology, applied in the field of ultra-high temperature carbonization process, can solve the problems of inconvenience, unstable processing quality, low processing efficiency, etc., achieve continuous and efficient process flow, improve product utilization and applicability, and product specification adaptability strong effect
Inactive Publication Date: 2013-04-10
ADVANCED FOR MATERIALS & EQUIP
View PDF4 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
However, although this kind of processing process can meet the basic production needs, due to the limited specifications of the carbon fiber felt in a single process, the processing efficiency is low, and the processing quality is not stable enough. At the same time, the heating equipment needs to be continuously heated and cooled during the processing process. Operation, energy consumption is relatively large, which causes a lot of inconvenience to related process operations
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0024] The core of the present invention is to provide an ultra-high temperature carbonization process, and the processing process of the ultra-high temperature carbonization process is relatively continuous and efficient.
[0025] In order to enable those skilled in the art to better understand the solution of the present invention, the present invention will be further described in detail below in conjunction with the accompanying drawings and specific embodiments.
[0026] Please refer to figure 1 , figure 1 It is a flowchart of the ultra-high temperature carbonization process provided by Embodiment 1 of the present invention.
[0027] The ultra-high temperature carbonization process provided by Embodiment 1 of the present invention includes:
[0028] Step 101: feeding;
[0029] The material to be processed is transported to the corresponding processing position through the unwinding roller, so that the subsequent carbonization and other technological processes can be im...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention discloses an ultra-high-temperature carbonization process. According to the ultra-high-temperature carbonization process, the operation of a cooling process can be rapidly implemented after the completion of ultra-high-temperature carbonization processing of material through the sequential process steps of feeding, carbonizing, cooling and receiving, the whole implementation process does not need to shut down a furnace frequently to cool, take and place the material, the process flow is continuous and efficient, the whole carbonization processing process is more stable and reliable, the product specification is strong in applicability, the follow-up splicing and other operations are not required, and the utilization rate and the applicability of a product are greatly improved.
Description
technical field [0001] The invention relates to the technical field of carbonization processing equipment, in particular to an ultra-high temperature carbonization process. Background technique [0002] As one of the excellent heat insulation materials, ultra-high temperature carbon felt has been widely used in thermal equipment, such as vacuum furnaces, crystal growth furnaces, single crystal furnaces, polycrystalline furnaces, etc. Because there are 90% voids in the ultra-high temperature carbon felt, the thermal insulation performance in vacuum or inert atmosphere is very superior. It has stable performance especially at ultra-high temperature. Because of its light weight, small specific heat capacity, soft texture and good heat insulation effect, it can greatly save energy as a heat insulation material. With the continuous improvement of production intensity, people have put forward higher requirements for the processing of ultra-high temperature carbon felt. [0003] ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(China)
IPC IPC(8): C01B31/02C01B32/05
Inventor 胡祥龙戴煜蒋振宇
Owner ADVANCED FOR MATERIALS & EQUIP