High-gloss ABS (acrylonitrile-butadiene-styrene) alloy and method for preparing same from matte ABS

An alloy and high-gloss technology, which is applied in the field of high-gloss ABS alloy and its preparation, can solve problems such as poor fluidity and poor coloring, and achieve the effects of cost reduction, excellent gloss, and moderate impact strength

Active Publication Date: 2015-04-08
SHANDONG UNIV +1
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Matte ABS is cheap and has excellent impact resistance. However, due to its poor fluidity and poor colorability, there is still no use of matt ABS base materials. It is suitable for rapid thermal cycle high-gloss injection molding technology through physical modification. A report on high-performance high-gloss ABS alloy and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-gloss ABS (acrylonitrile-butadiene-styrene) alloy and method for preparing same from matte ABS
  • High-gloss ABS (acrylonitrile-butadiene-styrene) alloy and method for preparing same from matte ABS
  • High-gloss ABS (acrylonitrile-butadiene-styrene) alloy and method for preparing same from matte ABS

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] The weight composition of high-gloss ABS alloy is shown in Table 1.

[0035] The matte ABS resin is acrylonitrile-styrene-butadiene graft copolymer (Shanghai Gaoqiao ABS275), with a melt flow rate of 8g / 10min (10Kg, 220°C) and high impact resistance (notched impact strength is 270J / m);

[0036] The selected permeability AS is Taiwan Taihua NF2200, which has high hardness, high transparency and high melt flow rate, and the melt index is 35g / 10min;

[0037] The selected black masterbatch is ABS-based high-precision bright masterbatch, such as fine bright pigment masterbatch 2016C;

[0038] The selected processing aid is a combination of lubricant, white mineral oil and brightening agent, wherein the weight ratio is 1 part of lubricant, 0.2 part of white mineral oil, and 0.5 part of brightening agent.

[0039] Selected light stabilizers Ciba Irganox1010, Irganox168.

[0040] Dry the matte ABS resin, AS (SAN), black masterbatch, light stabilizer and processing aid separate...

Embodiment 2

[0044] High-gloss ABS alloy, the weight composition of its raw materials is shown in Table 1, and the preparation method is the same as in Example 1.

Embodiment 3

[0046] High-gloss ABS alloy, the weight composition of its raw materials is shown in Table 1, and the preparation method is the same as in Example 1.

[0047] Table 1 embodiment proportioning

[0048]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
fluidityaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention relates to a high-gloss ABS (acrylonitrile-butadiene-styrene) alloy and a method for preparing the same from matte ABS, which comprises the following steps: preparing matte ABS resin, permeable AS (acrylonitrile-styrene), black color master batch, photostabilizer and processing assistant in a weight ratio of (40-80):(20-60):(3-7):(0.2-2):(0.1-5), respectively drying, thoroughly mixing in a high-speed mixer, sending the mixture into a double screw extruder, compounding, extruding, drawing, cooling, granulating and drying to obtain the injection molding finished product. By material selection, advantage complementation of different component materials, combination of preparation technique quick thermal circulation injection molding technique and other measures, the invention greatly lowers the raw material cost on the premise of ensuring excellent performance indexes, and especially overcomes the defects of low gloss, poor permeability, poor density and poor flowing property of the matte material, thereby implementing application in the high-end field and obviously lowering the material cost.

Description

technical field [0001] The invention relates to a high-gloss ABS alloy and its preparation, which is mainly used in the rapid thermal cycle injection molding process, and uses matt ABS to produce shell-like appearance injection molding with high requirements for appearance (including gloss, weld marks, flow marks, color, etc.) Components (such as display front shells, etc.), low production cost, excellent comprehensive performance, and have broad market prospects. Background technique [0002] The development of new spray-free high-gloss ABS alloy and its preparation technology is an important development direction of plastic shell materials for high-end electrical appliances. Through the design of polymer materials and the cooperation of rapid thermal cycle injection molding process and high-gloss mold, the green injection molding effect of energy saving, environmental protection, high gloss and spray-free can be achieved. [0003] Rapid Heating Cycle Molding (RHCM) is to ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L55/02C08L51/00C08L25/12B29B9/06B29C47/92B29C45/78B29C48/92
CPCB29C47/0011B29C47/8815B29C47/0066B29C47/92B29C48/0022B29C48/04B29C48/40B29C48/911
Inventor 赵国群王伟华高民王成功管延锦王小新
Owner SHANDONG UNIV