Capillary wool fabric glaze material

A technology of woolen wool and woolen wool is applied in the field of ceramic glaze to achieve the effect of soft color and delicate touch

Inactive Publication Date: 2014-12-31
东莞市高诚陶瓷制品有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, ceramic products with capillary lines have not been sold

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] 1. Formula

[0011] 1. Bottom glaze: 64.5% by weight of porcelain clay (206# produced by Shandong Hongci clay processing factory in Daling, Dongguan), 16% by weight of transparent glaze (Y-522 produced by Taiyi Ceramics (Yixing) Co., Ltd.), pigment 19.5% by weight (PGK-3207 royal blue pigment of COLOROBBIA company).

[0012] 2, wool powder: fine kaolin 34% (206# produced by Shandong Hongci clay processing factory in Daling, Dongguan), zirconium powder 33% (COLOROBBIA company 5006, coloring material 33% (COLOROBBIA company PGK-3207 royal blue coloring material).

[0013] 2. Preparation method

[0014] Grind and dry the bottom glaze and woolen powder respectively, and screen them in turn with 40 mesh and 80 mesh, and use between 40 and 80 mesh; mix 80wt% of the bottom glaze with 20wt% of the woolen glaze to form a glaze, The glaze can be applied by adding an appropriate amount of water to adjust the required concentration, and the weight concentration of the glaze in wa...

Embodiment 2

[0017] 1. Formula

[0018] 1. Bottom glaze: 64.5% by weight of porcelain clay (206# produced by Shandong Hongci clay processing factory in Daling, Dongguan), 16% by weight of transparent glaze (Y-522 produced by Taiyi Ceramics (Yixing) Co., Ltd.), pigment 19.5% by weight (PGK-3302 praseodymium yellow pigment from COLOROBBIA Company).

[0019] 2. Wool wool powder: 34% fine kaolin (206# produced by Shandong Hongci clay processing factory in Daling, Dongguan), 33% zirconium powder (5006 from COLOROBBIA company, 33% pigment (PGK-3302 praseodymium yellow pigment from COLOROBBIA company) .

[0020] 2. Preparation method

[0021] Grind and dry the bottom glaze and woolen powder respectively, and screen them in turn with 40 mesh and 80 mesh, and use between 40 and 80 mesh; mix 80wt% of the bottom glaze with 20wt% of the woolen glaze to form a glaze, The glaze can be applied by adding an appropriate amount of water to adjust the required concentration, and the weight concentration o...

Embodiment 3

[0024] 1. Formula

[0025] 1. Bottom glaze: 64.5% by weight of porcelain clay (206# produced by Shandong Hongci clay processing factory in Daling, Dongguan), 16% by weight of transparent glaze (Y-522 produced by Taiyi Ceramics (Yixing) Co., Ltd.), pigment 19.5% by weight (PGK-3401 black pigment from COLOROBBIA Company).

[0026] 2. Wool powder: fine kaolin 34% (206# produced by Shandong Hongci clay processing factory in Daling, Dongguan), zirconium powder 33% (COLOROBBIA company 5006, colorant 33% (COLOROBBIA company PGK-3401 black color pigment).

[0027] 2. Preparation method

[0028] Grind and dry the bottom glaze and woolen powder respectively, and screen them in turn with 40 mesh and 80 mesh, and use between 40 and 80 mesh; mix 80wt% of the bottom glaze with 20wt% of the woolen glaze to form a glaze, The glaze can be applied by adding an appropriate amount of water to adjust the required concentration, and the weight concentration of the glaze in water is 25%.

[0029]...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a capillary wool fabric glaze material which is characterized by including a base glaze and capillary wool fabric powder, the base glaze comprises, by weight, 64.5% of porcelain clay, 16% of a transparent glaze and 19.5% parts of a pigment; and the capillary wool fabric powder comprises, by weight, 34% parts of fine kaolin, 33% parts of zirconium powder and 33% parts of a pigment. The capillary wool fabric glaze material can form capillary lines on the surface of a ceramic product, so that the surface has the fluffy texture, is delicate in the sense of touch, and soft in color.

Description

technical field [0001] The invention relates to a glaze with woolen wool effect, which belongs to the technical field of glazes for ceramics. Background technique [0002] Driven by the tide of modern civilization, people's expectations and pursuit of the aesthetic level of ceramic products are becoming stronger and stronger. Ceramic products with different patterns make the field of ceramic effects more colorful. At present, there are no sales of ceramic products with capillary lines. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a capillary woolen glaze, which can make ceramic products present the effect of capillary lines. [0004] In order to solve the above-mentioned problems, the present invention provides a woolen woolen glaze, which is characterized in that it includes a bottom glaze and woolen wool powder, and the bottom glaze includes 64.5% by weight of porcelain clay, 16% by weight of transparent gl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C8/18C04B41/86
Inventor 吴青莲
Owner 东莞市高诚陶瓷制品有限公司