An alloy and zinc-based technology, applied in the field of metal alloy materials, can solve the problems of casting surface foaming, electroplating acceleration, etc., and achieve the effects of increasing strength, reducing reaction ability, and reducing the content of impurities
Inactive Publication Date: 2014-02-05
CHANGSHU LIONY METALS
View PDF5 Cites 10 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] As we all know, there are inevitably harmful impurities in zinc-based alloys. These harmful impurities such as lead, cadmium, and tin will gather at the grain junctions to cause intergranular corrosion. The metal matrix is broken due to intergranular corrosion, and electroplating accelerates this scourge. , the part subject to intergranular corrosion will expand and lift up the coating, causing blisters on the surface of the casting
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0024] A zinc-based alloy, the zinc-based alloy is a Zn-Al-Cu-Mg alloy, and the contained elements and mass percentages are: aluminum 5%, copper 0.8%, magnesium 0.06%, iron 0.015%, cadmium 0.001%, Tin 0.001%, the rest is zinc 94.123%.
[0025] The zinc-based alloy has a melting point of 350°C and a density of 4.8g / cm 3 , the thermal conductivity is 150W / m.k, and the tensile strength is 350MPa.
Embodiment 2
[0027] A zinc-based alloy, the zinc-based alloy is a Zn-Al-Cu-Mg alloy, the elements and mass percentages are: 4.8% aluminum, 1% copper, 0.05% magnesium, 0.017% iron, 0.001% cadmium, Tin 0.001%, the rest is zinc 94.131%.
[0028] The zinc-based alloy has a melting point of 350°C and a density of 5g / cm 3 , the thermal conductivity is 150W / m.k, and the tensile strength is 350MPa.
[0029] The invention discloses a zinc-based alloy, which adopts aluminum, copper and magnesium elements in a reasonable proportion, improves the casting performance of the alloy, increases the strength, hardness and fluidity of the alloy, and reduces the reaction ability to harmful impurities; In particular, the content of unavoidable impurities in the alloy is effectively reduced, and the impurities do not contain lead, a metal element harmful to the human body, which reduces intergranular corrosion and makes the alloy have high corrosion resistance. The zinc-based alloy of the invention is suitabl...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
melting point
aaaaa
aaaaa
density
aaaaa
aaaaa
tensile strength
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses a zinc-base alloy. The zinc-base alloy is a Zn-Al-Cu-Mg series alloy and comprises the following elements in percentage by mass: 4%-5.5% of aluminum, 0.8%-1.2% of copper, 0.05%-0.08% of magnesium, not more than 0.02% of iron, not more than 0.001% of lead, not more than 0.002% of cadmium, not more than 0.001% of tin, and the balance of zinc and inevitable impurities, wherein the content of the zinc is no less than 94%, and the total content of the impurities is not more than 0.02%. By the manner, the zinc-base alloy is low in the content of detrimental impurities, has high corrosion resistance, high strength and high wear resistance and is suitable for the casting of metal ornaments and accessories which are high in accuracy and complicated in structure; and castings have high surface quality and are difficult to fracture.
Description
technical field [0001] The invention relates to the field of metal alloy materials, in particular to a zinc-based alloy. Background technique [0002] The main additive elements of zinc-based alloys are aluminum, copper and magnesium, etc., which can be used for casting household appliance accessories, architectural decoration, bathroom accessories, lighting parts, toys, clothing metal accessories, etc. Castings must have high surface quality and good surface treatment Performance, while the common defect of zinc-based alloy die castings is surface blistering. [0003] As we all know, there are inevitably harmful impurities in zinc-based alloys. These harmful impurities such as lead, cadmium, and tin will gather at the grain junctions to cause intergranular corrosion. The metal matrix is broken due to intergranular corrosion, and electroplating accelerates this scourge. , the part affected by intergranular corrosion will expand and lift the coating, causing blistering on ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more