Problems solved by technology

[0002] At present, the tensile breaking strength of nylon and polyester is only about 5% of the theoretical value

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength fiber suede fabric
  • High-strength fiber suede fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0012] The present invention is described in further detail now in conjunction with accompanying drawing. The accompanying drawings are simplified schematic diagrams, which only illustrate the basic structure of the present invention in a schematic manner, so that they only show the components relevant to the present invention.

[0013] see figure 1 and figure 2 , a high-strength fiber fleece fabric, which is composed of a warp yarn 1, a weft yarn 2 and a wool yarn 3. Strength fiber, the density of the warp yarn 1 is 88 / cm, the density of the weft yarn 2 is 85 / cm, and the high-strength fiber is high-strength polyethylene fiber.

[0014] The invention relates to a high-strength fiber fleece fabric, which has high strength, which is 10 times that of ordinary chemical fibers, and has low density, high modulus, resistance to various chemical corrosion, and outstanding impact resistance and cutting resistance. Toughness characteristics, the product can be widely used in various...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to high-strength fiber suede fabric and belongs to the field of textile fabric. The high-strength fiber suede fabric is formed by interweaving warp yarn, weft yarn and wool yarn, wherein the warp yarn is 68D / 24F polyester-polyamide composite yarn, the weft yarn is 100D / 46F rayon, the wool yarn is high-strength fibers, the density of the warp yarn is 88 pieces / cm, the density of the weft yarn is 85 pieces / cm, and the high-strength fibers are high-strength polyethylene fibers. The high-strength fiber suede fabric is quite high in strength, and the strength of the high-strength fiber suede fabric is equivalent to 10 times that of common chemical fibers. Furthermore, the high-strength fiber suede fabric has the advantages of being small in density, high in modulus, resistant to various kinds of chemical corrosion and prominent in shock resistance and cutting-resistant tenacity. The product can be widely applied to various kinds of high-performance composite fabric.

Description

technical field [0001] The invention relates to a fabric, in particular to a high-strength fiber fleece fabric, which belongs to the textile field. Background technique [0002] At present, the tensile breaking strength of nylon and polyester is only about 5% of the theoretical value. The development of foreign high-strength fibers is still strong, and the main ones that meet the high-strength requirements are carbon fibers, aramid fibers, high-strength high-modulus polyethylene, and so on. High-strength fiber is mainly the effect that the fiber itself has high modulus, high strength, and high bending stiffness to achieve high strength. The products are mainly suitable for weaving industrial textiles, such as tire cords for automobiles and reinforcing materials for optical cables. [0003] The invention provides a high-strength fiber fleece fabric, which has high strength, which is 10 times that of ordinary chemical fibers, and has low density, high modulus, resistance to ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D03D27/14D03D15/00D03D15/20D03D15/283D03D15/292D03D15/50
Inventor 张丽娟
Owner SUZHOU LIXIU TEXTILE