Phosphate phosphor and UV light-emitting device utilizing the same
A technology of fluorescent materials and light-emitting devices, applied in the field of fluorescent materials, can solve the problems of rare fluorescent powder and other problems
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0038] Take potassium carbonate, yttrium oxide, praseodymium oxide, and diammonium hydrogen phosphate according to the chemical dosage ratio, mix them evenly, put them into a crucible, put them in a high-temperature furnace and sinter at 900°C~1100°C under air to prepare different Y / Pr molar ratios K 3 (Y 1-y PR y )(PO 4 ) 2 , where y is 0.02, 0.04, 0.06, 0.08, 0.1, 0.12, and 0.14, respectively. figure 2 K for different Y / Pr molar ratios 3 (Y 1-y PR y )(PO 4 ) 2 The emission spectrum is for emitting UV light with a wavelength between 230nm and 300nm. Such as figure 2 Shown, 8mol% of Pr 3+ Adding can get the best luminous intensity. image 3 for K 3 (Y 0.92 PR 0.08 )(PO 4 ) 2 The excitation spectrum, its excitation band is between 140 and 240nm.
[0039] Take potassium carbonate, yttrium oxide, gadolinium oxide, and diammonium hydrogen phosphate according to the chemical dosage ratio, mix them evenly, put them into a crucible, put them in a high-temperature ...
Embodiment 2
[0044] Take potassium carbonate, calcium carbonate, yttrium oxide, praseodymium oxide, and diammonium hydrogen phosphate according to the chemical dosage ratio, mix them evenly, put them into a crucible, put them in a high-temperature furnace and sinter at 950°C~1250°C under air to prepare different Y / KCa(Y 1-y PR y )(PO 4 ) 2 , where y is 0.01, 0.02, 0.05, 0.1, and 0.15, respectively. Figure 11 KCa(Y 1-y PR y )(PO 4 ) 2 The emission spectrum is for emitting UV light with a wavelength between 230nm and 330nm. Such as Figure 11 Shown, 10mol% of Pr 3+ Adding can get the best luminous intensity.
[0045] Take potassium carbonate, calcium carbonate, yttrium oxide, gadolinium oxide, and diammonium hydrogen phosphate according to the chemical dosage ratio, mix them evenly, put them into a crucible, put them in a high-temperature furnace and sinter at 950°C~1250°C under air to prepare different Y / KCa(Y 1-z Gd z )(PO 4 ) 2 , where z is 0.1, 0.2, 0.3, 0.4, and 0.5, r...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap