A kind of preparation method of hydrogen storage material with high reversible hydrogen storage capacity

A hydrogen storage material and hydrogen storage technology, applied in the field of hydrogen storage materials, can solve problems such as the gap in hydrogen storage performance, and achieve the effects of simple preparation process and high reversible hydrogen release amount

Inactive Publication Date: 2015-12-02
CHANGAN UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] Although there are various types of hydrogen storage materials currently being studied, each with its own advantages, compared with the requirements of practical applications and the goal of hydrogen storage ≥ 6.5wt% and decomposition temperature of 60-120 °C proposed by the US Department of Energy (DOE) , there is still a large gap in the hydrogen storage performance of the above materials, therefore, exploring and developing new high-performance hydrogen storage materials is still one of the main tasks at present

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of hydrogen storage material with high reversible hydrogen storage capacity

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A method for increasing the reversible hydrogen storage capacity of hydrogen storage material HPSB, the steps are as follows: 1) 1.07gNaBH 4 with 0.101gCoCl 2 Add 4g of water, then carry out the hydrolysis reaction at 30°C for 2 minutes, filter the filter residue after the hydrolysis reaction, dry the filter residue in the air (drying temperature is 20°C) for 16 hours to obtain the Co-B catalyst; 2) add 0.004g Co- Catalyst B with 0.01gY 2 o 3 Stir the mixture evenly with a glass rod in a mortar; 3) Make NaOH and water into a strong alkali solution with a pH of 12-13, and then add 0.0178g of sodium borohydride weighed in a glove box filled with argon to Mix evenly in a strong alkali solution to obtain a sodium borohydride alkaline aqueous solution, the mass fraction of sodium borohydride in the sodium borohydride alkaline aqueous solution is 9%, and finally add the mixture to the sodium borohydride alkaline aqueous solution at 25°C for hydrolysis Hydrogen reaction, af...

Embodiment 2

[0025] A method for increasing the reversible hydrogen storage capacity of hydrogen storage material HPSB, the steps are as follows: 1) 1.07gNaBH 4 with 0.101gCoCl 2 Add 4g of water, then carry out the hydrolysis reaction at 25°C for 3 minutes, filter the filter residue after the hydrolysis reaction, dry the filter residue in the air (drying temperature is 30°C) for 12 hours to obtain the Co-B catalyst; 2) add 0.007g Co- Catalyst B with 0.007gY 2 o 3 Stir the mixture evenly with a glass rod in a mortar; 3) Make NaOH and water into a strong alkali solution with a pH of 12-13, and then add 0.0178g of sodium borohydride weighed in a glove box filled with argon to Mix evenly in a strong alkali solution to obtain a sodium borohydride alkaline aqueous solution, the mass fraction of sodium borohydride in the sodium borohydride alkaline aqueous solution is 9%, and finally add the mixture to the sodium borohydride alkaline aqueous solution at 25°C for hydrolysis Hydrogen reaction, a...

Embodiment 3

[0027] A method for increasing the reversible hydrogen storage capacity of hydrogen storage material HPSB, the steps are as follows: 1) 1.07gNaBH 4 with 0.101gCoCl 2 Add 4g of water, then carry out the hydrolysis reaction at 20°C for 4 minutes, filter the filter residue after the hydrolysis reaction, dry the filter residue in the air (drying temperature is 20°C) for 20 hours to obtain the Co-B catalyst; 2) add 0.01g Co- Catalyst B with 0.004gY 2 o 3 Stir the mixture evenly with a glass rod in a mortar; 3) Make NaOH and water into a strong alkali solution with a pH of 12-13, and then add 0.0178g of sodium borohydride weighed in a glove box filled with argon to Mix evenly in a strong alkali solution to obtain a sodium borohydride alkaline aqueous solution, the mass fraction of sodium borohydride in the sodium borohydride alkaline aqueous solution is 9%, and finally add the mixture to the sodium borohydride alkaline aqueous solution at 20°C for hydrolysis Hydrogen reaction, af...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of a hydrogen storage material with high reversible hydrogen storage capacity. The preparation method comprises the following steps: uniformly stirring a Co-B catalyst and rare earth oxide in a mortar to obtain a mixture; adding the mixture into a sodium borohydride alkaline aqueous solution, then carrying out hydrolytic hydrogen release reaction at 10-30 DEG C, filtering after the reaction is ended, drying filter residues obtained by filtering for 5-20 days to obtain a component A at 10-30 DEG C, and mixing the component A and TiO2 accounting for 3-12 percent by mass of the component A to obtain the hydrogen storage material. The preparation method is simple in preparation process; in addition, the prepared hydrogen storage material is high in reversible hydrogen release capacity, and is a hydrogen storage material with high reversible hydrogen storage capacity.

Description

technical field [0001] The invention belongs to the field of hydrogen storage material HPSB (Hydrolysis Production of Sodium Borohydride), and specifically relates to a preparation method of a hydrogen storage material with a high reversible hydrogen storage capacity. Background technique [0002] With the depletion of petrochemical resources and the resulting environmental pollution, the development of non-polluting renewable energy has become an urgent task facing mankind. Hydrogen energy is regarded as the clean energy with the most development potential in the 21st century. However, due to the lack of convenient and effective hydrogen storage materials and hydrogen storage technologies, the application of hydrogen energy has been greatly hindered for a long time. The hydrogen storage materials currently studied mainly include hydrogen storage alloys, coordination hydrides, amino compounds, organic liquids, carbon-based materials, and metal-organic frameworks (MOFs). [...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01B3/06B01J23/75B01J23/83
CPCY02E60/36
Inventor 郑雪萍刘胜林温久然罗伟华鲁卓睿刘敏
Owner CHANGAN UNIV