A new type of fast-climbing solid mercury

A new type of technology with a weight percentage content, which is applied to the parts of gas discharge lamps, etc., can solve the problems of slow climbing, achieve the effects of shortening the time difference, good practicality and promotion value, and speeding up the climbing speed

Inactive Publication Date: 2016-05-18
扬州市邗江圣珠光电有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, compared with liquid mercury, the existing solid mercury species still have the disadvantage of slow climbing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A new type of fast-climbing solid mercury

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0010] The present invention will be further described below in conjunction with specific examples.

[0011] A new type of fast-climbing solid mercury, the composition of which is shown in Table 1. Th, ThO in solid mercury in the present invention 2 It can automatically release α particles. When the lamp is started, an electronic avalanche similar to a chain reaction occurs, and the circulating gas is instantly broken down, which greatly shortens the time difference from cathode glow discharge to thermal electron emission, thereby accelerating the climbing speed of the lamp tube. .

[0012] Table 1 Composition of new solid mercury that climbs fast

[0013]

sn

Sb

Hg

Th or ThO 2

Product 1

40%

8%

51.999%

0.001%

Product 2

41%

7%

51.9%

0.1%

Product 3

42%

6%

51.5%

0.5%

Product 4

43%

5%

51%

1%

Product 5

44%

4%

50.5%

1.5%

Product 6 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses novel solid mercury high in climbing speed. The novel solid mercury comprises, by weight, 40% to 50% of Sn, 1% to 8% of Sb, 40% to 52% of Hg, and 0.001% to 5% of Th or ThO2, wherein the sum of the weight percentages of the components is 100%. According to the novel solid mercury high in climbing speed, the defect that existing solid mercury is low in climbing speed is overcome, the climbing speed of the novel solid mercury is comparable with the climbing speed of liquid mercury, and the novel solid mercury has high practical value and popularization value.

Description

technical field [0001] The invention belongs to the technical field of mercury fixation, and in particular relates to a new type of mercury fixation with fast climbing. Background technique [0002] At present, solid mercury has been widely used instead of liquid mercury in the production of energy-saving lamps. Solid mercury can effectively reduce mercury pollution in production sites, and can also effectively reduce environmental pollution after the life of the lamp ends. However, compared with liquid mercury, existing solid mercury types still have the disadvantage of slow climbing. Contents of the invention [0003] Purpose of the invention: Aiming at the deficiencies in the prior art, the purpose of the present invention is to provide a new type of solid mercury with fast climbing, which can provide a climbing speed comparable to that of liquid mercury at room temperature. [0004] Technical solution: In order to realize the above-mentioned purpose of the invention, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01J61/20
Inventor 朱加才宋维申朱圣武
Owner 扬州市邗江圣珠光电有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com