Aqueous color-wrapping glaze base material and preparation method thereof

A water-based and water-based resin technology, applied in the direction of coating, etc., can solve the problems of stickiness, easy accumulation of coloring, thickening during construction, etc., and achieve strong coloring effect, convenient construction, and convenient construction.

Active Publication Date: 2014-09-17
JIANGSU HIMONIA TECH
View PDF5 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The main component of water-based UV coloring base material is UV-dryable water-based polyurethane resin. Due to its special molecular structur

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aqueous color-wrapping glaze base material and preparation method thereof
  • Aqueous color-wrapping glaze base material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A water-based color rubbing gel base material, made of the following components according to weight percentage: 15% water-based alkali-soluble emulsion, 10% pure water-based acrylic emulsion, 1% dispersant, 0.1% anti-fungal agent, TAFIGEL PUR421 %, talc powder 15%, BCS45%, TEGO AIREX901W0.2%, ammonia water 1.5%, color paste 6%, deionized water 5.2%; the sum of the percentages of the above components is 100%.

[0022] In the present invention, due to consideration of the slight chemical reaction between the water-based resin and the adjustment of the pH value and between the resin and the solvent, the specific addition sequence also has strict requirements. A preparation method of a water-based color rubbing gel base material includes Follow the steps below:

[0023] 1) According to the above mass fraction, slowly add water, dispersant, and antifungal agent under the action of stirring and dispersing to obtain mixture A, the stirring speed is 400rpm, and the stirring tim...

Embodiment 2

[0039] A water-based color rubbing gel base material, which is made of the following components according to weight percentage: 10% water-based alkali-soluble emulsion, 5% pure water-based acrylic emulsion, 3% dispersant, 0.3% anti-fungal agent, BYK4250. 5%, calcium carbonate 25%, propylene glycol 25%, Dehydran 129 30.1%, AMP-9 50.5%, color paste 18%, deionized water 12.6%; the sum of the percentages of the above components is 100%.

[0040] A preparation method of water-based color-rubbing gel base material, comprising the steps of:

[0041] 1) According to the above mass fraction, slowly add water, dispersant, and antifungal agent under the action of stirring and dispersing to obtain mixture A, the stirring speed is 500 rpm, and the stirring time is 5 minutes;

[0042] 2) Slowly add the filler to the mixture A while increasing the stirring speed to 1000rpm, and add the defoamer at the same time, and the stirring time is 20 minutes to obtain the mixture B;

[0043] 3) Slowly...

Embodiment 3

[0048]A water-based color rubbing gel base material, made of the following components according to weight percentage: 12.5% ​​water-based alkali-soluble emulsion, 7.5% pure water-based acrylic emulsion, 2% dispersant, 0.2% anti-mold agent, TAFIGEL PUR42 And BYK4250.75%, talcum powder and calcium carbonate 20%, BCS and propylene glycol 35%, TEGO AIREX901W and Dehydran12930.3%, ammonia water and AMP-951%, color paste 8%, the balance is deionized water; the above groups The sum of the percentages is 100%.

[0049] A preparation method of water-based color-rubbing gel base material, comprising the steps of:

[0050] 1) According to the above mass fraction, slowly add water, dispersant, and antifungal agent under the action of stirring and dispersing to obtain mixture A, the stirring speed is 450rpm, and the stirring time is 8 minutes;

[0051] 2) Slowly add the filler to the mixture A while increasing the stirring speed to 900rpm, and add the defoamer at the same time, and the st...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an aqueous color-wrapping glaze base material which is made of the following components in percentage by weight: 10-15% of aqueous resin A, 5-10% of aqueous resin B, 1-3% of dispersing agent, 0.1-0.3% of mildew preventive, 0.5-1% of thickening agent, 15-25% of packing, 25-45% of alcohol ether solvent, 0.1-0.5% of defoaming agent, 0.5-1.5% of pH value regulating agent, 6-30% of color paste and the balance of water, wherein the sum of the percentages of the components is 100%. The invention further discloses a preparation method of the base material. The base material has the advantages of high coloring effect, convenience in construction and the like. The base material can be directly used with aqueous base materials and diluted by water to blend appropriate color concentrate, and thus a perfect decoration effect is achieved, and requirements of client are met.

Description

technical field [0001] The invention belongs to the field of coatings, and in particular relates to a water-based color rubbing gel base material and a preparation method thereof. Background technique [0002] At present, in the traditional floor coating process, UV water-based coloring is used, followed by oil-based UV coating. The main component of water-based UV coloring base material is UV-dryable water-based polyurethane resin. Due to its special molecular structure, it is prone to stickiness and non-drying during the film forming process, easy accumulation of coloring, and thickening during construction. With the improvement of consumers' aesthetic requirements and differences in consumer levels, there are more and more requirements for differentiated and personalized products, and floor coloring is an important factor for people to choose flooring. Therefore, the development of floor coloring is becoming more and more important. more and more. Contents of the inven...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D201/00C09D133/00C09D7/12
Inventor 江益新陈明贵吴志飞常红言
Owner JIANGSU HIMONIA TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap