Anode material of nickel-metal hydride battery

A cathode material, nickel-hydrogen battery technology, applied in battery electrodes, nickel batteries, alkaline batteries, etc., can solve the problems of poor low temperature performance, affecting applications, low battery output power, etc., to improve discharge potential and service life, improve Effectiveness of utilization rate, improved performance and high current discharge capacity

Active Publication Date: 2014-11-19
砀山县纳方包装材料有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing Ni-MH battery is an aqueous electrolytic system, which has the problems of low discharge platform voltage and poor low-temperature performance during use; and, due to the low discharge platform voltage of the Ni-MH battery, the output power of the battery is low. When the Ni-MH battery is discharged at a high rate, the problem of low discharge platform voltage is particularly prominent, which affects its application in high-power power batteries

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anode material of nickel-metal hydride battery

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A kind of positive electrode material of nickel-metal hydride battery, it is made up of the raw material of following parts by weight:

[0024] Active material 100, conductive agent 1, binder 6, additive 0.2;

[0025] The active material is composed of spherical nickel hydroxide, cobalt oxide, zinc oxide and magnesium hydroxide with a mass ratio of 100:10:2:0.1;

[0026] Described conductive agent is made up of nickel powder, carbon powder, graphite powder, cobalt powder that mass ratio is 100:50:20:3;

[0027] The adhesive is composed of carboxymethyl cellulose, polyethylene glycol 1000, bone glue and PTFE emulsion with a mass ratio of 20:4:3:1;

[0028] The additive is composed of molybdenum trioxide, cobaltous oxide, nickel oxide, neodymium oxide, ethyl orthosilicate, stearic acid, trimethylol with a mass ratio of 100:60:40:1:0.2:0.2:3. Base propane composition; The preparation method of described additive comprises the following steps:

[0029] Heat stearic acid ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an anode material of a nickel-metal hydride battery. The anode material is prepared from the following raw materials in parts by weight: 90-100 parts of active substance, 0.05-3 parts of conductive agent, 6-10 parts of adhesive and 0.2-1 part of additive. By adopting the anode material of the battery, the utilization rate of a nickel electric active substance is effectively improved, the discharge potential of a nickel electrode is improved, the service life of the nickel electrode is prolonged, and the use performance and the large-current discharge capability of the nickel electrode within a large temperature range are improved.

Description

technical field [0001] The invention mainly relates to the battery field, in particular to a nickel-hydrogen battery positive electrode material. Background technique [0002] As a high-energy green rechargeable battery that is rapidly developing today, Ni-MH battery has been widely used in notebook computers, camcorders, digital cameras and electric bicycles by virtue of its advantages of high energy density, fast charge and discharge, long cycle life and no pollution. widely used. In order to promote the improvement of the performance of nickel-metal hydride batteries, the research on negative electrode hydrogen storage materials has never stopped; [0003] At present, nickel-metal hydride batteries are widely used due to their environmental protection, stable performance, and good adaptability under various conditions. However, the existing Ni-MH battery is an aqueous electrolytic system, which has the problems of low discharge platform voltage and poor low-temperature...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M4/48H01M4/52H01M4/62
CPCH01M4/62H01M4/622H01M4/624H01M10/30Y02E60/10
Inventor 翟恩宏
Owner 砀山县纳方包装材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com