Production method of automobile engine fracture splitting connecting-rod high-strength steel continuous casting billet
A technology for automobile engines and expanding connecting rods is applied in the field of metallurgy, which can solve the problems of corrosion of basic furnace lining ladle, low phosphorus content at the end of smelting, increased energy consumption, etc., and achieves low production cost, easy control of S component, and energy saving. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0026] Example 1:
[0027] Process used: electric furnace smelting-eccentric tapping-LF furnace refining-continuous casting, the production chemical composition is: C0.4%, Si0.7%, Mn1.2%, P0.03%, S0.035%, N0 .016% of the high-strength steel continuous casting billets of automobile engine expansion and broken connecting rods, the steps are as follows:
[0028] 1) Electric furnace smelting: using molten iron and scrap steel as raw materials, the ratio of which is: molten iron: scrap = 6:1; rapid temperature increase in the early stage of smelting for decarburization and low flow slag, oxidation endpoint temperature: 1630℃; endpoint carbon is 0.3%, endpoint Phosphorus is 0.03%.
[0029] 2) Eccentric tapping: The tapping adopts the operation of retaining steel and slag. When tapping 1 / 3, add active lime 4kg / t, ferrous sulfide 2kg / t, aluminum block 1.5kg / t, silicon calcium barium 2.5kg / t, the molten steel entering the LF refining furnace has an oxygen content of 80 ppm and a sulfur cont...
Example Embodiment
[0038] Example 2:
[0039] Process used: electric furnace smelting-eccentric tapping-LF furnace refining-continuous casting, the production chemical composition is: C0.45%, Si0.6%, Mn1.3%, P0.05%, S0.045%, N0 .02% of the high-strength steel continuous casting billet of automobile engine expansion and broken connecting rod, the steps are as follows:
[0040] 1) Electric furnace smelting: using molten iron and scrap steel as raw materials, the ratio of which is: molten iron: scrap = 8:1; rapid decarburization and low flow slag in the early stage of smelting, oxidation end temperature: 1645 ℃; end carbon 0.35%, end point Phosphorus is 0.045%.
[0041] 2) Eccentric tapping: The tapping adopts the operation of retaining steel and slag. When tapping 1 / 3, add active lime 3kg / t, ferrous sulfide 2.5kg / t, aluminum block 1.2kg / t, calcium silicon Barium is 2.3kg / t, the oxygen content in the LF refining furnace is 60ppm, and the sulfur content is 0.06%.
[0042] 3) LF refining furnace: after mol...
Example Embodiment
[0050] Example 3:
[0051] Process used: electric furnace smelting-eccentric tapping-LF furnace refining-continuous casting, the production chemical composition is: C0.5%, Si0.75%, Mn1.1%, P0.045%, S0.04%, N0 .018% of the high-strength steel continuous casting billets of automobile engine expansion and broken connecting rods, the steps are as follows:
[0052] 1) Electric furnace smelting: using molten iron and scrap steel as raw materials, the ratio of which is: molten iron: scrap = 8:1; rapid temperature increase in the early stage of smelting for decarburization and low flow slag, oxidation endpoint temperature: 1630℃; endpoint carbon is 0.4%, endpoint Phosphorus is 0.042%.
[0053] 2) Eccentric tapping: The tapping adopts the operation of retaining steel and slag. When tapping 1 / 3, add active lime 3.5kg / t, ferrous sulfide 2.2kg / t, aluminum block 1.2kg / t, silicon The calcium barium is 2.2kg / t, and the oxygen content in the LF refining furnace is 70ppm, and the sulfur content is ...
PUM
Property | Measurement | Unit |
---|---|---|
Melting point | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap