Production method of high-conductivity aluminium alloy sections
A technology of aluminum alloy profiles and high electrical conductivity, which is applied in the field of aluminum alloy preparation, can solve the problems of material electrical conductivity, low mechanical properties, microstructure defects, etc., and achieve the effect of improving strength, good electrical conductivity, and high strength
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0022] Example 1
[0023] Si is 0.40%%, Fe is 0.10%%, Cu is 0.05%%, Mn is 0.05%%, Mg is 0.50%%, Zn is ≤0.10%, Ti is ≤0.10%, Cr is ≤0.10%, single impurity≤0.05%, total impurity≤0.15%, the rest is Al;
[0024] The technical parameters of extrusion are: die temperature 455°C, ingot temperature 470°C, extrusion barrel temperature 420°C, extrusion speed 3±0.5m / min.
[0025] Online quenching, quenching temperature 420±5℃, quenching speed 300℃ / min;
[0026] Use strong wind and fog to cool down.
[0027] The tensile elongation is 1.5%.
[0028] The aging temperature is 195℃, the metal is kept for 12 hours, and the aging furnace is released.
Example Embodiment
[0029] Example 2
[0030] Si is 0.45%, Fe is 0.15%, Cu is 0.07%, Mn is 0.07%, Mg is 0.53%, Zn is ≤0.10%, Ti is ≤0.10%, and Cr is ≤0.10% , Single impurity≤0.05%, total impurity≤0.15%, the rest is Al;
[0031] The mold temperature is 480℃, the ingot temperature is 490℃, the extrusion barrel temperature is 460℃, and the extrusion speed is 3.5±0.5m / min.
[0032] Online quenching, the quenching temperature is 435±5℃, and the quenching speed is 315℃ / min.
[0033] Use strong wind and fog to cool down.
[0034] The tensile elongation is 1.5%.
[0035] The aging temperature is 195℃, the metal is kept for 12 hours, and the aging furnace is released.
Example Embodiment
[0036] Example 3
[0037] Si is 0.45%, Fe is 0.15%, Cu is 0.07%, Mn is 0.07%, Mg is 0.53%, Zn is ≤0.10%, Ti is ≤0.10%, and Cr is ≤0.10% , Single impurity≤0.05%, total impurity≤0.15%, the rest is Al;
[0038] The mold temperature is 485℃, the ingot temperature is 490℃, the extrusion cylinder temperature is 470℃, and the extrusion speed is 3.6±0.5m / min.
[0039] Online quenching, the quenching temperature is 435±5℃, and the quenching speed is 315℃ / min.
[0040] Use strong wind and fog to cool down.
[0041] The tensile elongation is 1.5%.
[0042] The aging temperature is 195℃, the metal is kept for 12 hours, and the aging furnace is released.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap