Manufacturing method of module type centerless grinding machine guide plate

A centerless grinding machine and a manufacturing method technology, which are applied to grinding machines, machine tools designed for grinding the rotating surface of workpieces, manufacturing tools, etc. Convenience, lower production costs, and lower scrap rates

Active Publication Date: 2015-02-11
CHONGYI ZHANGYUAN TUNGSTEN
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to overcome the short service life of the centerless grinder guide plate in the prior art, the steel substrate is difficult to recycle, and the defect of high scrap rate, the technical problem to be solved by the present invention is to provide a method for manufacturing the guide plate of a modular centerless grinder, so as to achieve The centerless grinder guide plate has a long service life, the steel substrate can be recycled, and the scrap rate is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing method of module type centerless grinding machine guide plate
  • Manufacturing method of module type centerless grinding machine guide plate
  • Manufacturing method of module type centerless grinding machine guide plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A manufacturing method of a modular guide plate for a centerless grinder. The manufacture of the guide plate for a centerless grinder divides the guide plate into two parts: an alloy bar 1 and a steel matrix 3 , and an adhesive 4 is used to bond the alloy bar 1 and the steel matrix 3 .

[0028] The steps of the present invention are as follows:

[0029] A. Processing of the steel matrix 3 part: when the thickness of the steel matrix 3 is greater than or equal to 5mm, such as figure 2 As shown, the steel base 3 is processed into a "concave" shape, and the steel base 3 is processed with horizontal planes I5 and II6, which are respectively 1 / 3 of the total width of the steel base 3, and the middle of the horizontal planes I5 and II6 is concave. groove;

[0030] B. Process the alloy strip 1 part: the thickness and width of the alloy strip 1 and the steel matrix 3 are the same, such as Figure 4 As shown, the alloy bar 1 is processed into a "convex" shape to match the "...

Embodiment 2

[0038] A manufacturing method of a modular guide plate for a centerless grinder. The manufacture of the guide plate for a centerless grinder divides the guide plate into two parts: an alloy bar 1 and a steel matrix 3 , and an adhesive 4 is used to bond the alloy bar 1 and the steel matrix 3 .

[0039] The steps of the present invention are as follows:

[0040] A. Process the steel matrix 3 part: when the thickness of the steel matrix 3 is less than 5mm, such as image 3 As shown, the steel base 3 is processed into an inclined "L" shape, and the steel base 3 is processed with an inclined plane I7, the angle between the inclined plane I7 and the horizontal direction is 10°, and the included angle between the inclined plane II8 and the horizontal direction is a, The size of a is 30°, and the projection length of the slope II 8 in the horizontal direction is 1 / 3 of the total width of the steel matrix 3;

[0041] B. Process the alloy strip 1 part: the thickness and width of the ...

Embodiment 3

[0049] A manufacturing method of a modular guide plate for a centerless grinder. The manufacture of the guide plate for a centerless grinder divides the guide plate into two parts: an alloy bar 1 and a steel matrix 3 , and an adhesive 4 is used to bond the alloy bar 1 and the steel matrix 3 .

[0050] The steps of the present invention are as follows:

[0051] A. Process the steel matrix 3 part: when the thickness of the steel matrix 3 is less than 5mm, such as image 3 As shown, the steel base 3 is processed into an inclined "L" shape, and the steel base 3 is processed with an inclined plane I7, the angle between the inclined plane I7 and the horizontal direction is 10°, and the included angle between the inclined plane II8 and the horizontal direction is a, The size of a is 45°, and the projection length of the slope II 8 in the horizontal direction is 1 / 3 of the total width of the steel matrix 3;

[0052] B. Process the alloy strip 1 part: the thickness and width of the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the field of module production, and particularly relates to a manufacturing method of a module type centerless grinding machine guide plate. The manufacturing method of the module type centerless grinding machine guide plate is provided to overcome the defects that the centerless grinding machine guide plates in the prior art are short in service life, the steel substrates are difficult to recycle and the rejection rate is high. The manufacturing method comprises the following steps: A, machining a steel substrate; B, machining an alloy bar; C, preparing an adhesive; D, adhering; and E, drying. According to the manufacturing method, the steel substrate and the alloy bar are machined and the prepared adhesive is used for adhering the steel substrate and the alloy bar, so that the recycling of the steel substrate is realized; and through the module type mounting of the alloy bar, the service life of the centerless grinding machine guide plate is prolonged, the rejection rate of the guide plate is reduced and the reduction of production cost of the enterprises is facilitated.

Description

technical field [0001] The invention belongs to the field of mold production, and in particular relates to a method for manufacturing a guide plate of a modular centerless grinder. Background technique [0002] Centerless grinding machine grinding is a grinding method in which the workpiece is placed on the pallet and guide plate from the front of the machine tool and pushed into the grinding area, and then passes through the grinding area from the back of the machine tool. It is mainly suitable for processing cylindrical and disc-shaped parts, and other parts such as short cones can be processed after special changes. In this processing process, if the selection and adjustment of the grinding wheel, the supporting plate, and especially the guide plate are improper, grinding defects will occur, which will affect the processing accuracy. [0003] In the existing technology, the traditional centerless grinding machine guide plate is made by welding method, such as figure 1 ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline