Unlock instant, AI-driven research and patent intelligence for your innovation.

Novel melamine veneer

A technology of melamine and decorative panels, applied in fire-resistant coatings, coatings, etc., can solve the problems of moisture-proof and flame-retardant performance of the outer surface that cannot meet the requirements of users.

Inactive Publication Date: 2015-02-18
亚恪新材料(江苏)有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Existing melamine veneer, the moisture-proof and flame-retardant performance of the outer surface can not meet the user's requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0060] A novel melamine veneer, the outer surface of the novel melamine veneer is coated with a protective layer, and the protective layer consists of the following components in parts by weight:

[0061] 1.2 parts sodium hexametaphosphate,

[0062] 1.2 parts zinc sulfide,

[0063] 2.3 parts xylene,

[0064] 1.2 parts diatomaceous earth,

[0065] 2.3 parts pentachlorobiphenyl,

[0066] 4.5 parts antimony dioxide,

[0067] 1.2 parts silicone oil,

[0068] 1.2 parts ammonium sulfate,

[0069] 2.3 parts barium sulfate,

[0070] 4.5 parts magnesium hydroxide,

[0071] 2.3 parts citric acid,

[0072] 1.2 parts of hexamethylene diisocyanate.

Embodiment 2

[0074] A novel melamine veneer, the outer surface of the novel melamine veneer is coated with a protective layer, and the protective layer consists of the following components in parts by weight:

[0075] 2 parts sodium hexametaphosphate,

[0076] 2 parts zinc sulfide,

[0077] 3 parts xylene,

[0078] 2 parts diatomaceous earth,

[0079] 3 parts Pentachlorobiphenyl,

[0080] 5 parts antimony dioxide,

[0081] 2 parts silicone oil,

[0082] 2 parts ammonium sulfate,

[0083] 3 parts barium sulfate,

[0084] 5 parts magnesium hydroxide,

[0085] 3 parts citric acid,

[0086] 2 parts hexamethylene diisocyanate.

Embodiment 3

[0088] A novel melamine veneer, the outer surface of the novel melamine veneer is coated with a protective layer, and the protective layer consists of the following components in parts by weight:

[0089] 1 part sodium hexametaphosphate,

[0090] 1 part zinc sulfide,

[0091] 2 parts xylene,

[0092] 1 part diatomaceous earth,

[0093] 2 parts Pentachlorobiphenyl,

[0094] 4 parts antimony dioxide,

[0095] 1 part silicone oil,

[0096] 1 part ammonium sulfate,

[0097] 2 parts barium sulfate,

[0098] 4 parts magnesium hydroxide,

[0099] 2 parts citric acid,

[0100] 1 part hexamethylene diisocyanate.

[0101]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a novel melamine veneer. The outside surface of the novel melamine veneer is coated with a protecting layer, and the protecting layer is composed of the following components in parts by weight: 1-2 parts of sodium hexametaphosphate, 1-2 parts of zinc sulfide, 2-3 parts of xylene, 1-2 parts of diatomite, 2-3 parts of pentachlorodiphenyl, 4-5 parts of antimony dioxide, 1-2 parts of organic silicone oil, 1-2 parts of ammonium sulfate, 2-3 parts of barium sulfate, 4-5 parts of magnesium hydroxide, 2-3 parts of citric acid, and 1-2 parts of hexamethylene diisocyanate. The outside surface of the novel melamine veneer disclosed by the invention has certain moisture resistance and fire resistance.

Description

technical field [0001] The invention relates to a novel melamine veneer. Background technique [0002] The moisture-proof and flame-retardant properties of the outer surface of the existing melamine veneer cannot meet the requirements of users. Contents of the invention [0003] The object of the present invention is to provide a novel melamine veneer, the outer surface of which has certain moisture-proof and flame-retardant properties. [0004] In order to achieve the above object, the technical solution of the present invention is to design a novel melamine veneer, the outer surface of the novel melamine veneer is coated with a protective layer, and the protective layer is composed of the following components in parts by weight: [0005] 1 to 2 parts of sodium hexametaphosphate, [0006] 1 to 2 parts of zinc sulfide, [0007] 2 to 3 parts of xylene, [0008] 1 to 2 parts of diatomaceous earth, [0009] 2 to 3 parts of pentachlorobiphenyl, [0010] 4 to 5 parts of a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/00C09D5/18C09D7/12
Inventor 杨晓娜
Owner 亚恪新材料(江苏)有限公司