Electrode composite material, preparation method of electrode composite material, as well as negative electrode and battery with electrode composite material

A composite material and electrode technology, which is applied in nanotechnology for materials and surface science, battery electrodes, secondary batteries, etc., can solve the problems of unsatisfactory electrochemical performance and large-scale production obstacles of manganese oxide electrode materials, etc. problems, to achieve the effects of large-scale production potential, abundant modifiable points, and non-toxic modifiable points

Active Publication Date: 2015-03-18
POSITEC POWER TOOLS (SUZHOU) CO LTD +1
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, many synthesis methods of manganese oxides involve high-temperature processes or complex experimental designs, which hinder the large-scale production of manganese oxide-based electrode materials, and some of the existing research on manganese oxide-based electrode materials has insufficient electrochemical performance. Ideal, therefore, it is necessary to find a new type of manganese oxide electrode material and find a simpler and lower energy consumption preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Electrode composite material, preparation method of electrode composite material, as well as negative electrode and battery with electrode composite material
  • Electrode composite material, preparation method of electrode composite material, as well as negative electrode and battery with electrode composite material
  • Electrode composite material, preparation method of electrode composite material, as well as negative electrode and battery with electrode composite material

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0034] A preparation method of an electrode composite material, the preparation method comprising the following steps: mixing raw materials, the raw materials include M13 phage suspension and manganese source; adding alkali and hydrogen peroxide solution to the mixture in sequence; storing at 3°C ​​to 5°C; Wash; collect the precipitate; dry the precipitate to obtain M13 phage / Mn 3 o 4 electrode composites.

[0035] An electrode composite including M13 bacteriophage and Mn 3 o 4 , the electrode composite also includes carbon nanotubes. The addition of carbon nanotubes can significantly improve the capacity and cycle performance of batteries assembled with electrode composite materials. Preferably, the carbon nanotubes are selected from at least one of single-wall carbon nanotubes or multi-wall carbon nanotubes. In electrode composite materials, M13 phage, Mn 3 o 4 And the mass ratio between carbon nanotubes is 9.99:90:0.01.

[0036] A preparation method of an electrode ...

Embodiment 1

[0070] Preparation of electrode composite material: Mix 10 mL of M13 phage suspension with 100 mL of 0.10 M manganese sulfate solution. Then 100 μL of multi-walled carbon nanotube (American Nanomaterials, 3% W.W) solution was added to the above mixture. Stirring was continued at room temperature for 24 hours. After stirring, 10 mL of 2.5 mol / L NaOH solution was added to the mixture, and stirred for 10 seconds. Subsequently, an additional 1.4 mL of 30% hydrogen peroxide solution was added. The resulting solution was stored at 4°C for 1.5 hours. The final product was washed twice with Milli-Q water and collected by centrifugation. The resulting powder was dried at 320 °C for 3 hours to obtain M13 phage / Mn 3 o 4 / carbon nanotube electrode composites.

[0071] figure 1 M13 phage / Mn in embodiment 1 3 o 4 / XRD patterns of carbon nanotube electrode composites. The vertical line in the figure corresponds to Mn 3 o 4 The standard XRD pattern characteristic peak, from figur...

Embodiment 2

[0073] The preparation of negative electrode: be the M13 phage / Mn in the embodiment 1 of 70% by weight percentage 3 o 4 / carbon nanotube electrode composite, 10% by weight of polyvinylidene fluoride (PVdF) (Kynar, HSV900) as a binder and 20% by weight of Lithium carbon black (MTI, with a purity of 99.5%) was mixed, and N-methyl-2-pyrrolidone (NMP, Sigma, with a purity of 99.5%) was used as a dispersant to prepare a negative electrode slurry. The prepared negative electrode slurry was then coated on copper foil using doctor blade coating. Dry overnight in a vacuum oven at 60° C. to obtain a negative electrode.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
widthaaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The invention provides an electrode composite material which comprises a M13 bacteriophage and Mn3O4. The electrode composite material has a good nano structure and a good electrochemical performance, and can be used as a negative electrode material of a lithium ion battery; moreover, a preparation method of the electrode composite material is simple and feasible, and can be implemented at low temperature. The invention also provides the preparation method of an electrode composite material, and a negative electrode and a battery which comprise the electrode composite material.

Description

technical field [0001] The invention relates to an electrode composite material. [0002] The invention also relates to a preparation method of the electrode composite material. [0003] The invention also relates to a negative electrode and a battery comprising the electrode composite. Background technique [0004] In recent years, with the development of science and technology, the demand for energy, especially renewable green energy, has become more and more prominent. As an energy storage and conversion device, batteries are playing an irreplaceable role. As a new type of renewable secondary energy, lithium-ion batteries are currently the focus of development in the battery field because of their low cost, high-quality specific energy, high volume specific energy, high energy density, and long cycle life. It has been widely used in mobile phones, notebook computers, electric tools, digital cameras and electric vehicles. [0005] As cobalt oxides and iron oxides have b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H01M4/36H01M4/60H01M4/50H01M10/0525B82Y30/00
CPCB82Y30/00H01M4/362H01M4/502H01M4/60H01M4/625H01M10/0525Y02E60/10
Inventor 杰伊·J·Y·皇甫董德贤陈璞
Owner POSITEC POWER TOOLS (SUZHOU) CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap