A kind of laser water transfer decal paper color layer coating and its preparation method and application

A water transfer and laser technology, applied in paper coating, coating, paper making, etc., can solve problems such as hot stamping speed, fastness, cutting surface, easy change of adhesion, uncontrollable post-processing transfer effect, and failure to meet production needs, etc. , to achieve the effect of beautiful adhesion, low production cost and simple method

Active Publication Date: 2017-01-25
DONGGUAN K LASER TECH
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the formula of commonly used laser water transfer decal paper color coating is mainly phenolic resin. Due to the high temperature resistance of phenolic resin, its brightness is not high enough for laser imprinting, so it cannot meet the production needs.
Therefore, the existing technology increases the embossing brightness by increasing the embossing brightness of the laser water transfer decal paper color coating, and increases the embossing brightness by the resin proportion in its formula. However, the hot stamping of the laser water transfer decal paper color coating after the formula adjustment Speed, fastness, cutting surface, adhesion and other related functions are easy to change, which makes the transfer effect of post-processing uncontrollable
Moreover, in the control of the coating process of laser water transfer decal paper color layer coating, the production conditions are also changed due to the change of the color layer formula, which greatly reduces the production efficiency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] A kind of laser water transfer pattern paper color coating, it comprises the following components by weight:

[0039] 18 kg of phenolic resin, 0.8 kg of methyl acrylate, 0.8 kg of n-butyl acrylate, 0.4 kg of methyl methacrylate, and 80 kg of absolute ethanol.

[0040] The preparation method of above-mentioned laser water transfer decal paper color coating is as follows:

[0041] Step 1, adding the phenolic resin into absolute ethanol according to the formula amount, stirring evenly to obtain the mixture;

[0042] Step 2, add methyl acrylate, n-butyl acrylate and methyl methacrylate to the mixture obtained in step 1, and after fully stirring for 30 minutes, obtain a laser water-transfer floral paper color coating with a certain viscosity; wherein, using -When measuring the viscosity of the above-mentioned laser water transfer decal paper color coating with a 4-cup viscometer, the outflow time of the laser water transfer decal paper color coating is 15 seconds.

[0043]...

Embodiment 2

[0047] A kind of laser water transfer pattern paper color coating, it comprises the following components by weight:

[0048] 15 kg of phenolic resin, 1 kg of methyl acrylate, 1 kg of n-butyl acrylate, 0.5 kg of methyl methacrylate, and 82.5 kg of absolute ethanol.

[0049] The preparation method of above-mentioned laser water transfer decal paper color coating is as follows:

[0050] Step 1, adding the phenolic resin into absolute ethanol according to the formula amount, stirring evenly to obtain the mixture;

[0051] Step 2, add methyl acrylate, n-butyl acrylate and methyl methacrylate to the mixture obtained in step 1, and after fully stirring for 20 minutes, obtain a laser water transfer decal paper color coating with a certain viscosity; wherein, using When measuring the viscosity of the above-mentioned laser water transfer decal paper color coating with a 4-cup viscometer, the outflow time of the laser water transfer decal paper color coating is 13 seconds.

[0052] Whe...

Embodiment 3

[0056] A kind of laser water transfer pattern paper color coating, it comprises the following components by weight:

[0057] 20 kg of phenolic resin, 0.5 kg of methyl acrylate, 0.5 kg of n-butyl acrylate, 0.2 kg of methyl methacrylate, and 78.8 kg of absolute ethanol.

[0058] The preparation method of above-mentioned laser water transfer decal paper color coating is as follows:

[0059] Step 1, adding the phenolic resin into absolute ethanol according to the formula amount, stirring evenly to obtain the mixture;

[0060] Step 2, add methyl acrylate, n-butyl acrylate and methyl methacrylate to the mixture obtained in step 1, and after fully stirring for 40 minutes, obtain a laser water-transfer decal paper color coating with a certain viscosity; wherein, using -When measuring the viscosity of the above-mentioned laser water transfer decal paper color coating with a 4-cup viscometer, the outflow time of the laser water transfer decal paper color coating is 16 seconds.

[0061...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of laser water transfer-printing stained paper color layers and particularly relates to laser water transfer-printing stained paper color layer coating as well as a preparation method and an application thereof. The laser water transfer-printing stained paper color layer coating is prepared from the following components in percentage by weight: 15%-20% of phenolic resin, 0.5%-1% of methyl acrylate, 0.5%-1% of n-butyl acrylate, 0.2%-0.6% of methyl methacrylate and 78%-83% of absolute ethyl alcohol. A certain amount of methyl acrylate, n-butyl acrylate and methyl methacrylate is used for preparing the phenolic resin, so that the tolerable temperature of the prepared laser water transfer-printing stained paper color layer painting is lowered, and therefore, the embossing brightness of the laser water transfer-printing stained paper color layer coating can be greatly increased during laser embossing, and the production needs can be met. Moreover, the laser water transfer-printing stained paper color layer coating can be used for ensuring that associated functions such as embossing speed, firmness, section and adhesion are not changed, so that the production efficiency can be improved.

Description

technical field [0001] The invention relates to the technical field of laser water transfer decal paper color layer, in particular to a laser water transfer decal paper color layer coating and its preparation method and application. Background technique [0002] At present, the commonly used formula of laser water transfer decal paper color coating is mainly phenolic resin. Due to the high temperature resistance of phenolic resin, its brightness is not high enough for laser imprinting, so it cannot meet the production needs. Therefore, the existing technology increases the embossing brightness by increasing the embossing brightness of the laser water transfer decal paper color coating, and increases the embossing brightness by the resin proportion in its formula. However, the hot stamping of the laser water transfer decal paper color coating after the formula adjustment Relevant functions such as speed, fastness, cut surface, and adhesion are easy to change, which makes the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D4/06C09D4/02B41M3/12D21H19/24
Inventor 张亚飞吴俊德
Owner DONGGUAN K LASER TECH