Composite panel of cabinet door, manufacturing method of composite panel and wardrobe

A composite panel and cabinet door technology, which is applied in the field of furniture, can solve the problems of fragile skin, high weight, and increased cost, and achieve the effects of ensuring strength, reducing wardrobe cost, and reducing quantity

Inactive Publication Date: 2015-04-29
BYD CO LTD
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The invention solves the technical problems of the cabinet door panel in the prior art that the skin is easily damaged and the cost i

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite panel of cabinet door, manufacturing method of composite panel and wardrobe
  • Composite panel of cabinet door, manufacturing method of composite panel and wardrobe
  • Composite panel of cabinet door, manufacturing method of composite panel and wardrobe

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0030] The present invention also provides a preparation method of the cabinet door composite panel, which includes the following steps:

[0031] S10, respectively forming a hollow structure plastic substrate and a transparent plastic surface layer through an extrusion molding process;

[0032] S20, forming a pattern layer on the other surface of the transparent plastic surface layer, or forming a pattern layer on one surface of the plastic substrate;

[0033] S30. Laminating the side of the transparent plastic surface layer with the pattern layer in step S20 and the plastic substrate obtained in step S10 and then press molding, or bonding the side of the plastic substrate with the pattern layer in step S20 to one surface of the transparent plastic surface layer After pressing and forming, the composite panel of the cabinet door is obtained.

[0034] Among them, both the plastic substrate and the transparent plastic surface layer can be prepared by an extrusion molding process, that i...

Example Embodiment

[0042] Example 1

[0043] (1) A plastic extruder is used to separately extrude a honeycomb hollow structure PP plastic substrate with a thickness of 6mm and a PC transparent plastic board with a thickness of 1mm.

[0044] (2) PVD treatment is performed on one surface of the PC transparent plastic board, and a PVD hardened layer with a thickness of 0.01 mm is formed on the surface. Then, a color printer is used to print the ink according to the required pattern on the other side of the PC transparent plastic plate, and a pattern layer is formed on the surface after curing.

[0045] (3) Spray an adhesive with a thickness of 0.2mm on the surface of the PC transparent plastic board with a pattern layer; then attach the surface to the PP plastic substrate of step (1), and automatically glue it through a rolling machine to cut into After you need the size, get figure 2 , image 3 The cabinet door composite panel S1 of the structure shown.

Example Embodiment

[0046] Example 2

[0047] (1) A plastic extruder is used to separately extrude a honeycomb hollow structure PP plastic substrate with a thickness of 6mm and a PC transparent plastic board with a thickness of 1mm.

[0048] (2) Then use a color printer to print the ink according to the required pattern on one surface of the PC transparent plastic board, and form a pattern layer on the surface after curing.

[0049] (3) Spray an adhesive with a thickness of 0.2mm on the surface of the PC transparent plastic board with a pattern layer; then attach the surface to the PP plastic substrate of step (1), and automatically glue it through a rolling machine to cut into After the dimensions are required, the cabinet door composite panel S2 of this embodiment is obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention provides a composite panel of a cabinet door and a manufacturing method of the composite panel. The composite panel of the cabinet door comprises a plastic base plate and a transparent plastic surface layer, wherein the plastic base plate has a hollow structure; and a pattern layer is arranged between the plastic base plate and the transparent plastic surface layer. The invention also provides a wardrobe which comprises the composite panel of the cabinet door. The composite panel of the cabinet door has a double-layered composite structure, the patterns and the color of the composite panel are durable, and the composite panel is top-grade and high-quality in appearance, light in weight and stable in structure, and is damp-proof, environment-friendly and recyclable. The wardrobe with the composite panel of the cabinet door is low in cost and is convenient to mount and carry.

Description

technical field [0001] The invention belongs to the technical field of furniture, and in particular relates to a cabinet door composite panel, a preparation method thereof and a wardrobe. Background technique [0002] At present, the common wardrobe door panels on the market are mostly fiberboard-based louver panels and wood-plastic lily panels. However, these two boards have many disadvantages. The skin process must use a large amount of glue for coating and coloring, which will release toxic gases such as formaldehyde for a long time; Cabinet doors have a short service life. [0003] The IKEA (IKEA) store has launched a PAX series high-end wardrobe sliding door, which uses 4mm tempered glass as the panel, the frame is aluminum alloy, and its structure is a top-hanging full-cover sliding door. This kind of movable cabinet door with tempered glass as the panel, the surface is tempered glass, which solves the defect that the skin of the cabinet door is easily damaged, and l...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): E06B3/78B32B27/08B32B27/30B32B27/32B32B3/12
Inventor 王传华
Owner BYD CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products