Spun pure cotton garment material and preparing technology thereof

A preparation process, pure cotton technology, applied in the field of clothing fabrics, can solve the problems of not being soft and smooth enough, easy to deform, and dark color, etc., and achieve the effect of avoiding excessive yarn stretching, enhancing yarn strength, and soft hand feeling

Inactive Publication Date: 2015-10-07
芜湖市瑞都服装贸易有限公司
View PDF0 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Natural pure cotton textiles are soft, comfortable, and breathable, but they still have their inherent shortcomings, such as easy to wrinkle and difficult to smooth, while ordinary cotton fabrics are easy to shrink, deform, and stick to wool, and have poor acid resistance. Difference
Moreover, after printing and dyeing, cotton fabrics generally feel hard, not soft and smooth enough, and the fabric itself lacks luster, which makes pure cotton woven fabrics of lower grade, which is difficult to use in the production and application of high-end clothing.
Although cotton fabrics have the characteristics of being breathable, after inhaling sweat, the drying speed is very slow, and the sweat cannot be removed quickly, and the expansion of cotton fibers after absorbing water will reduce the air permeability, especially after strenuous exercise and sweating a lot, wet clothes It also feels sticky and uncomfortable to human skin, and after long-term outdoor sports wear, the color becomes dull, and the moisture absorption and sweat conduction performance becomes poor.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Spun pure cotton garment material and preparing technology thereof
  • Spun pure cotton garment material and preparing technology thereof
  • Spun pure cotton garment material and preparing technology thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A spun pure cotton clothing fabric, which is woven with warp yarns and weft yarns, the warp yarns are blended with 50% tencel fibers, 30% bamboo fibers, and 20% polyester fibers by mass percentage, and the weft yarns are 50% by mass percentage % pure cotton fiber and 50% wool fiber are blended into yarn.

[0034] Such as figure 1 as shown, figure 1 It is a flow chart of the preparation process of a kind of spun pure cotton clothing fabric proposed by the present invention.

[0035] refer to figure 1 , the preparation technology of described spinning pure cotton clothing fabric, comprises the steps:

[0036] S1, spinning department

[0037] Tencel fibers, bamboo fibers and polyester fibers are blended into warp yarns through cleaning, carding, three-way drawing, coarse sand, and spun yarn processes. 700r / min; in the carding process, the raw sliver weight is 25g / 5m, the cylinder speed is 300r / min, the licker-in roller speed is 840r / min, and the doffer speed is 20r / mi...

Embodiment 2

[0046] A spun pure cotton clothing fabric, which is woven from warp yarns and weft yarns. The warp yarns are blended with 70% tencel fibers, 10% bamboo fibers and 30% polyester fibers in mass percentages. The weft yarns are made of a mass percentage of 70% pure cotton fiber and 30% wool fiber are blended into yarn.

[0047] The preparation technology of described spinning pure cotton clothing fabric, comprises the steps:

[0048] S1, spinning department

[0049] Tencel fibers, bamboo fibers and polyester fibers are blended into warp yarns through cleaning, carding, three-way drawing, coarse sand, and spun yarn processes. 800r / min; in the carding process, the raw sliver weight is 18g / 5m, the cylinder speed is 360r / min, the licker-in roller speed is 780r / min, and the doffer speed is 25r / min; in the three drawing frames, the sliver weight is 19.0g / 5m , and the combined number is 8, the total draft multiple is 5 times, the rear zone draft multiple is 1.7 times, and the sliver de...

Embodiment 3

[0058] A spun pure cotton clothing fabric, which is woven from warp yarns and weft yarns, the warp yarns are blended with 60% tencel fibers, 20% bamboo fibers, and 20% polyester fibers by mass percentage, and the weft yarns are 60% by mass percentage % pure cotton fiber and 40% wool fiber blended into yarn.

[0059]The preparation technology of described spinning pure cotton clothing fabric, comprises the steps:

[0060] S1, spinning department

[0061] Tencel fibers, bamboo fibers and polyester fibers are blended into warp yarns through cleaning, carding, three-way drawing, coarse sand, and spun yarn processes. 750r / min; in the carding process, the raw sliver weight is 22g / 5m, the cylinder speed is 330r / min, the licker-in roller speed is 810r / min, and the doffer speed is 22r / min; in the three drawing frames, the sliver weight is 20.0g / 5m , combined number 6, total draft multiple 8 times, back zone draft multiple 1.5 times, sliver delivery speed 330m / s; in the roving process...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a spun pure cotton garment material. The spun pure cotton garment material is formed by weaving warp and weft. The warp is formed by blending tencel fiber, bamboo fiber and polyester fiber. The weft is formed by blending pure cotton fiber and wool fiber. The garment material overcomes the inherent defects of natural pure cotton fabrics, various indexes such as moisture absorption and air permeability are superior, the garment material is smooth in hand feeling, good in luster and capable of caring the skin of the human body better.

Description

technical field [0001] The invention relates to the technical field of clothing fabrics, in particular to a spun pure cotton clothing fabric and a preparation process thereof. Background technique [0002] In recent years, people's requirements for clothing have been continuously improved, not only requiring clothing fabrics to keep warm and crisp, but also hoping to have more functions. Among them, the wearing comfort of textiles has attracted more and more attention. Natural pure cotton textiles are soft, comfortable, and breathable, but they still have their inherent shortcomings, such as easy to wrinkle and difficult to smooth, while ordinary cotton fabrics are easy to shrink, deform, and stick to wool, and have poor acid resistance. Difference. Moreover, after printing and dyeing, cotton fabrics generally feel hard, not soft and smooth enough, and the fabric itself lacks luster, which makes pure cotton woven fabrics of low grade and difficult to be used in the producti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine