Shock resistant high-abrasion-proof paint for hydraulic parts

A technology of high wear resistance and hydraulic parts, applied in the direction of coating, can solve the problems of poor impact resistance and high temperature resistance, and achieve the effect of good high temperature resistance and high impact resistance.

Inactive Publication Date: 2015-10-14
王俐帧
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a coating for hydraulic parts with high impact resistance and high wear resistance, so as to solve the problem of poor impact resistance and high temperature resistance of coatings for hydraulic parts in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Wherein, the coating is made up of the following raw materials by weight:

[0031] 15 parts of butylated urea-formaldehyde resin; 2 parts of pine oil; 25 parts of nitrile rubber; 18 parts of acrylate; 8 parts of curing agent; 4 parts of fluorinated graphite; 5 parts of calcium carbonate; and 8 parts of fumed silica.

Embodiment 2

[0033] Wherein, the coating is made up of the following raw materials by weight:

[0034] 25 parts of butylated urea-formaldehyde resin; 5 parts of pine oil; 40 parts of nitrile rubber; 25 parts of acrylate; 12 parts of curing agent; 5 parts of fluorinated graphite; 8 parts of calcium carbonate; and 10 parts of fumed silica.

[0035] From the above description, it can be seen that the above-mentioned embodiments of the present invention achieve the following technical effects:

[0036] The invention provides a coating for hydraulic parts with high impact resistance and high wear resistance, which not only has high impact resistance performance, but also has good high temperature resistance performance.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a shock resistant high-abrasion-proof paint for hydraulic parts. The paint consists of the following raw materials in parts by weight: 12-25 parts of butylated urea formaldehyde resin, 2-5 parts of pine oil, 25-40 parts of chemigum, 18-25 parts of acrylic ester, 8-12 parts of a curing agent, 4-5 parts of fluoridized graphite, 2-8 parts of calcium carbonate and 5-10 parts of gas-phase silicon dioxide. The shock resistant high-abrasion-proof paint for hydraulic parts, disclosed by the invention, not only is high in shock resistance, but also is high in resistance to high temperature.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a coating for impact-resistant and high-wear-resistant hydraulic parts. Background technique [0002] Today's technological products are changing with each passing day, and the development is even faster, so the problem of impact resistance and high temperature resistance is expanding. [0003] In the process of using hydraulic parts, they are easily peeled off by external forces and lose their thermal insulation effect, resulting in a local temperature difference in the hydraulic parts using the coating, which in turn poses a serious threat to safety production. Therefore, a high-performance and excellent Thermal insulation coatings with high impact resistance are necessary. SUMMARY OF THE INVENTION [0004] The purpose of the present invention is to provide a coating for hydraulic parts with impact resistance and high wear resistance, so as to solve the problem of poor impa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D4/02C09D4/06C09D7/12
Inventor 王俐帧
Owner 王俐帧