Preparation method of three- dimensional MoS2
A three-dimensional, foamed nickel technology, applied in the direction of molybdenum sulfide, etc., to achieve the effect of strong operability, good process repeatability, and large specific surface area
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0021] Example 1:
[0022] Take (NH 4 ) 2 MoS 4 And DMF, mixed into three-dimensional MoS 2 The reaction raw material solution, and the (NH 4 ) 2 MoS 4 The mass percentage is 1.1%, and then the foamed nickel substrate is immersed in the three-dimensional MoS 2 In the reaction raw material solution, and keep it for 15 min, then take it out and place it in a vacuum drying oven, and dry it at 70 ℃ for 25 min. Repeat the above steps 5 times to obtain (NH 4 ) 2 MoS 4 / Foam nickel, then (NH 4 ) 2 MoS 4 / The nickel foam is placed in a mixed atmosphere of argon and hydrogen with a volume ratio of 9.5:0.5 in a tube furnace at a temperature of 750℃ for 2h, and then cooled to room temperature to obtain MoS 2 / Foam nickel; MoS 2 / Put the nickel foam into a PMMA anisole solution with a mass fraction of 4% and a PMMA molecular weight of 950,000 for 1 min, then take it out, and then vacuum-dry it at 120℃ for 1 h to obtain PMMA-coated MoS 2 / Nickel foam, then will be coated with PMMA MoS 2 / The ni...
Example Embodiment
[0023] Example 2:
[0024] Take (NH 4 ) 2 MoS 4 And DMF, mixed into three-dimensional MoS 2 The reaction raw material solution, and the (NH 4 ) 2 MoS 4 The mass percentage is 1.1%, and then the foamed nickel substrate is immersed in the three-dimensional MoS 2 In the reaction raw material solution, and keep it for 20 min, then take it out and place it in a vacuum drying oven, and dry it at 70 ℃ for 35 min. Repeat the above steps 5 times to obtain (NH 4 ) 2 MoS 4 / Foam nickel, then (NH 4 ) 2 MoS 4 / The nickel foam is placed in a mixed atmosphere of argon and hydrogen with a volume ratio of 9.5:0.5 in a tube furnace at 700℃ for 2h, and then cooled to room temperature to obtain MoS 2 / Foam nickel; MoS 2 / Put the nickel foam into a PMMA anisole solution with a mass fraction of 4% and a PMMA molecular weight of 950,000 for 2 min, then take it out, and then vacuum-dry it at 120°C for 1 h to obtain PMMA-coated MoS 2 / Nickel foam, then will be coated with PMMA MoS 2 / The nickel foam is im...
Example Embodiment
[0025] Example 3:
[0026] Take (NH 4 ) 2 MoS 4 And DMF, mixed into three-dimensional MoS 2 The reaction raw material solution, and the (NH 4 ) 2 MoS 4 The mass percentage is 1.1%, and then the foamed nickel substrate is immersed in the three-dimensional MoS 2 In the reaction raw material solution, and keep it for 17 min, then take it out and place it in a vacuum drying oven, and dry it at 75 ℃ for 20 min. Repeat the above steps 5 times to obtain (NH 4 ) 2 MoS 4 / Foam nickel, then (NH 4 ) 2 MoS 4 / The nickel foam is placed in a mixed atmosphere of argon and hydrogen with a volume ratio of 9.5:0.5 in a tube furnace at 800℃ for 2h, and then cooled to room temperature to obtain MoS 2 / Foam nickel; MoS 2 / Put the nickel foam into a PMMA anisole solution with a mass fraction of 4% and a molecular weight of PMMA of 950,000 for 2 minutes, then take it out, and then vacuum-dry it at 130°C for 1 hour to obtain PMMA-coated MoS 2 / Nickel foam, then will be coated with PMMA MoS 2 / The nickel...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap