Electrolyte, lithium ion battery including the same, and preparation method thereof

A lithium-ion battery and electrolyte technology, applied in the field of lithium-ion batteries, can solve the problems of lithium-ion battery cycle and storage performance degradation, battery power performance degradation, battery failure, etc., to suppress battery gas production, improve power performance, and facilitate The effect of the operation

Active Publication Date: 2018-05-08
NINGDE AMPEREX TECH
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, in order to increase the energy density of lithium-ion batteries, the voltage of lithium-ion batteries has been continuously increased. However, higher voltage means that the cathode material has a higher electrode potential and is more oxidative. Therefore, during the storage and cycle of the battery , will lead to the degradation of the cycle and storage performance of the lithium-ion battery and even lead to the failure of the battery
[0005] In the prior art, the above-mentioned problems are improved through the introduction of cathode additives, a protective layer is formed on the surface active points of the cathode material, and direct contact between the surface active points of the cathode material and the electrolyte is avoided, and the occurrence of side reactions is suppressed. The use will also bring some negative effects, such as the decrease of the power performance of the battery

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Electrolyte, lithium ion battery including the same, and preparation method thereof
  • Electrolyte, lithium ion battery including the same, and preparation method thereof
  • Electrolyte, lithium ion battery including the same, and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0074] Another object of the present application is to provide a method for preparing a lithium-ion battery, which includes injecting the electrolyte solution provided by the application, wherein injecting the electrolyte solution includes the following two steps.

[0075] Step (1), after putting the battery cell into the packaging case, inject the electrolyte E1 containing the additive A, and then carry out chemical formation and exhaust.

[0076] In the above step (1), preferably, the content of the additive A is 0.15% to 8% of the total weight of the electrolyte E1 part, and more preferably, the content of the additive A is 0.25% of the total weight of the electrolyte E1 part. ~7.5%, more preferably, the content of the additive A is 0.35~5% of the total weight of the electrolyte E1 part.

[0077] In the above step (1), the electrolyte solution E1 containing part of lithium salt, part of organic solvent and additive A is injected. Preferably, the content of the part of the ...

Embodiment

[0086] The present application is further described below through specific examples. However, these examples are merely exemplary and do not constitute any limitation to the protection scope of the present application.

[0087] In the following examples, comparative examples and test examples, the reagents, materials and instruments used are commercially available unless otherwise specified.

[0088] In the following experimental examples, comparative examples and test examples, the materials used are as follows:

[0089] Organic solvent: The organic solvent is a mixture containing ethylene carbonate (abbreviated as EC), ethyl methyl carbonate (abbreviated as EMC) and diethyl carbonate (abbreviated as DEC). The weight ratio is EC:EMC:DEC=1:1:1.

[0090] Additive: vinylene carbonate (VC), the total content of VC is 0.2% of the total weight of the electrolytic solution.

[0091] Lithium salt: LiPF 6 , LiPF 6 The total content is 12.5% ​​of the total weight of the electrolyte....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present application relates to an electrolytic solution, a lithium ion battery including the electrolytic solution and a preparation method thereof, wherein the electrolytic solution includes a lithium salt, an organic solvent, an additive A and an additive B, and the additive A is selected from phosphoric acid ester compounds, boric acid One or more of ester compounds, the additive B is one or more of sulfite compounds and sultone compounds. After the provided electrolyte is applied to the lithium-ion battery, the cycle performance, high-temperature storage performance and power performance of the lithium-ion battery can be improved. When preparing a lithium-ion battery, part of the electrolyte E1 is added before formation, and the remaining electrolyte E2 is added before the capacity is tested. By selecting the provided preparation method, the lithium-ion battery can have excellent cycle performance, high-temperature storage performance and power performance.

Description

technical field [0001] The present application relates to the field of lithium-ion batteries, in particular to an electrolyte, a lithium-ion battery including the electrolyte, and a method for preparing the lithium-ion battery. Background technique [0002] With the depletion of fossil energy and the increasing pressure of environmental pollution, the automotive industry urgently needs a new type of energy to drive it. Lithium-ion batteries stand out due to their high energy density, no memory effect, and high operating voltage. It is currently the preferred solution for new energy vehicles. The automotive industry requires power lithium-ion batteries to have the following properties: high power performance, long cycle life, and long storage life. However, this is a big challenge for traditional lithium-ion batteries. [0003] Generally speaking, a more stable solid electrolyte interface (Solid Electrolyte Interface, SEI) film can provide better protection for the anode, e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M10/0567H01M10/0525H01M10/058C07F7/08C07F9/17C07D327/10C07D327/04
CPCC07D327/04C07D327/10C07F7/08C07F9/17H01M10/0525H01M10/0567H01M10/058Y02E60/10Y02P70/50
Inventor 周晓崇韩昌隆付成华冯绍伟田少杰
Owner NINGDE AMPEREX TECH