A kind of polymer matrix composite material and preparation method thereof

A composite material and polymer technology, which is used in the field of polymer matrix composite materials with high energy storage density and high discharge efficiency and its preparation, can solve the problem of low energy storage density of composite materials, resistance to breakdown field strength of sacrificial composite materials, low Energy storage density and other issues, to achieve the effects of low cost, improved energy storage performance, and increased energy storage density

Inactive Publication Date: 2017-11-07
TONGJI UNIV
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This patent uses a large amount of ceramic fillers to prepare composite materials to increase the dielectric constant, sacrifice the breakdown resistance field strength of the composite material, and obtain the energy storage density under low electric field conditions, so that the energy storage density of the prepared composite material lower

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of polymer matrix composite material and preparation method thereof
  • A kind of polymer matrix composite material and preparation method thereof
  • A kind of polymer matrix composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Preparation of BaTiO by Electrospinning 3 Nano ceramic fiber, 1.5g BaTiO 3 The nano-ceramic fibers were placed in a mixed solution of aluminum nitrate, PVP and ethanol, the mass ratio of aluminum nitrate, PVP and ethanol was 1:0.02:5, stirred for 2 hours in a water bath at 40 °C, and the stirring speed was 400 r / min. Washing, drying, and sintering at 600 °C for 2 h to obtain nanofiber materials with a core-shell structure, the core is barium titanate nano-ceramic fibers, and the shell layer is an alumina coating layer; the prepared nanofiber material is added in a mass ratio of 1:0.02 3-Aminopropyltriethoxysilane (APS) coupling agent, heated to 100°C and stirred for 5 hours, washed three times with deionized water and absolute ethanol, and dried in a drying oven at 80°C for 12 hours. hours, the APS surface-modified nanofiber material was obtained, and then the modified BaTiO 3 @Al 2 O 3 Fibers are added to PVDF / DMF mixtures (BaTiO 3 @Al 2 O 3 The volume ratio of ...

Embodiment 2

[0038] The method is the same as above, except that BaTiO is used 3 @Al 2 O 3 The volume ratio of nanofiber material to PVDF / DMF is 5:95, and the polymer matrix composite film can be prepared.

[0039] The energy storage density of the composite film is as image 3 shown, 6.6J / cm 3 .

Embodiment 3

[0041] The method is the same as above, except that BaTiO is used 3 @Al 2 O 3 The volume ratio of nanofiber material to PVDF / DMF is 7.5:92.5, and the polymer matrix composite film can be prepared.

[0042] The energy storage density of the composite film is as image 3 shown, 6.4J / cm 3 .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a polymer matrix composite and a preparation method thereof. The composite is a laminated film composed of a polyvinylidene difluoride matrix and a nano-fiber material dispersed in the polyvinylidene difluoride matrix. The nano-fiber material is of a core-shell structure, wherein a core layer is made of a ceramic fiber, and a shell layer is an aluminum oxide coating layer. The polymer matrix composite is prepared through the method comprises the following steps: (1) placing the ceramic fiber in mixed solution of aluminum nitrate, polyvinyl pyrrolidone and ethyl alcohol, and after uniform mixing, obtaining the nano-fiber material through sintering; (2) causing the nano-fiber material to undergo surface modification through a coupling agent, then adding the nano-fiber material into mixture of polyvinylidene difluoride and dimethylformamide, performing uniform mixing, pouring the mixture in a casting film machine to form a film through flow-casting, and performing drying to obtain the laminated film; (4) and causing the laminated film to undergo heating and heat insulation, quenching and drying, and obtaining the polymer matrix laminated film. Compared with the prior art, the polymer matrix composite has the advantages that the laminated film is high in energy density, good in energy storage efficiency, simple in preparation process and low in cost.

Description

technical field [0001] The invention relates to the technical field of composite material preparation, in particular to a polymer-based composite material with high energy storage density and high discharge efficiency and a preparation method thereof. Background technique [0002] High energy storage density capacitors have the advantages of large discharge power, high utilization efficiency, fast charging and discharging speed, and stable performance. They play an important role in power systems, electronic devices, and pulse power supplies. They are widely used in hybrid electric vehicles, pulse power systems, electromagnetic guns, electromagnetic launch platforms and other modern industrial and national defense fields. With the development of electronic devices in the direction of miniaturization, integration and high-speed, the requirements for high energy storage, miniaturization, light weight, low cost and high reliability are put forward for capacitive components. Ho...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L27/16C08K7/08C08K9/06C08K9/02C08J5/18
Inventor 翟继卫刘少辉李朋沈波
Owner TONGJI UNIV