Jewelry polishing agent and preparation method therefor

A production method and polishing agent technology, applied in the direction of chemical instruments and methods, detergent compositions, non-surface active detergent compositions, etc., can solve problems such as easy dirt, difficult to clean, damage to jewelry color, etc., to achieve The effect of strong scavenging ability

Inactive Publication Date: 2016-02-03
李伟
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In recent years, with the improvement of people's living standards, jewelry has become a common item that people wear daily. Jewelry is divided into natural gemstones, natural jade, and natural organic gemstones, which are expressed in brilliant colors, or transparent and clean, or have special Optical effects (such as cat's eye, color change, luminous phenomenon, etc.), or special patterns (such as chrysanthemum stone, agate, plum jade, etc.), and j

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0015] Example 1

[0016] A jewellery polish consisting of the following components according to mass percentage:

[0017] A Oxalic acid: 5%, deionized water: 46%,

[0018] B concentration of 27% ammonia water 4%, deionized water: 45%,

[0019] C Acetone: 4%.

[0020] A manufacturing method of jewelry polish, including the following steps:

[0021] (1) Stir the A component evenly and heat it to 70°C and keep it at constant temperature.

[0022] (2) Stir the B component evenly and add it to the A component, stir for 30 minutes, cool to room temperature, add the C component,

[0023] (3) Put it in a filter centrifuge and centrifuge at 1400 rpm, then take it out for distillation for 4 hours.

Example Embodiment

[0024] Example 2

[0025] A jewellery polish consisting of the following components according to mass percentage:

[0026] A Oxalic acid: 3%, deionized water: 50%,

[0027] Ammonia water with a B concentration of 27%: 4%, deionized water: 40%,

[0028] C Acetone: 3%.

[0029] A manufacturing method of jewelry polish, including the following steps:

[0030] (1) Stir the component A and heat it to 65℃ and keep it at constant temperature.

[0031] (2) Stir the B component evenly and add it to the A component, stir for 40 minutes, cool to room temperature, add the C component,

[0032] (3) Put it in a filter centrifuge and centrifuge at 1800 rpm, then take it out for distillation for 3 hours.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a jewelry polishing agent. The jewelry polishing agent is prepared from ingredients A, ingredients B and an ingredient C, wherein the ingredient A comprises, in percentage by mass, 3-6% of oxalic acid, and 40-50% of deionized water, the ingredient B comprises, in percentage by mass, 1-4% of 27% ammonia water, 40-50% of deionized water, and the ingredient C comprises, in percentage by mass, 1-4% of acetone. A preparation method for the jewelry polishing agent comprises the steps of uniformly stirring the ingredients A, then, heating the ingredients A to the temperature of 60-70 DEG C, uniformly stirring the ingredients B, then, adding the uniformly-stirred ingredients B into the ingredients A, carrying out stirring for 30-40 minutes, cooling the mixture to room temperature, adding the ingredient C into the mixture, putting the ingredient C added mixture into a filtering centrifuge, carrying out centrifugation at the rate of 1,200-1,800 revolutions per second, then, taking out the centrifuged mixture, and distilling the centrifuged mixture for 3-6 hours. The jewelry polishing agent can be used for polishing all kinds of jewelry; when in use, the jewelry polishing agent is daubed to dirty parts, and the jewelry is bright and eye-catching after the jewelry polishing agent is swabbed up with clean fabrics; the jewelry polishing agent has a high removing capacity to oil stains and other dirt, which are entrapped on the jewelry in long term; and meanwhile, the jewelry polishing agent cannot damage the color and luster, purity and the like of the jewelry.

Description

technical field [0001] The invention belongs to the technical field of jewelry maintenance, and in particular relates to a jewelry polish and a preparation method thereof. Background technique [0002] In recent years, with the improvement of people's living standards, jewelry has become a common item that people wear daily. Jewelry is divided into natural gemstones, natural jade, and natural organic gemstones. Optical effects (such as cat's eye, color change, night light, etc.), or special patterns (such as chrysanthemum stone, agate, plum jade, etc.), and jewelry is prone to dirt after long-term wearing. If it is not cleaned in time, it may be damaged. Damage the color of the jewelry itself, or even cause chemical reactions, especially jewelry with complex shapes is not easy to clean, and the conventional cleaning method is to use water washing, the cleaning effect is very poor, especially for oil stains and other stains are difficult to clean, Cleaning with kerosene can ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C11D7/60C11D7/26C11D7/06C11D7/32
Inventor 李伟
Owner 李伟
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products