A kind of butyl rubber and preparation method thereof

A technology of butyl rubber and rubber, which is applied in the field of butyl rubber, can solve the problems of slow vulcanization speed, poor self-adhesiveness and inter-adhesiveness, and poor compatibility of butene rubber, and achieve improved strength and gloss, improved anti-aging, Effect of improving vulcanization performance

Active Publication Date: 2017-05-24
ZHEJIANG SHITAI IND CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention provides a kind of butyl rubber for the shortcomings of butene rubber in the prior art, such as slow vulcanization speed, poor self-adhesiveness and inter-adhesiveness, poor compatibility, and poor interaction with reinforcing agents.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of butyl rubber and preparation method thereof
  • A kind of butyl rubber and preparation method thereof
  • A kind of butyl rubber and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A kind of butyl rubber, comprises following mass parts components:

[0027]

[0028] Among them, the halogenated diene rubber is 55 parts by mass of brominated butyl rubber and 45 parts by mass of chlorinated butyl rubber, and the average particle diameter of nanoscale titanium dioxide, nanoscale silver powder and nanoscale montmorillonite powder is 100nm. The agent is mica treated with silane coupling agent, and the vulcanizing agent is sulfur.

Embodiment 2

[0030] A kind of butyl rubber, comprises following mass parts components:

[0031]

[0032] Among them, the halogenated diene rubber is 70 parts by mass of brominated butyl rubber and 30 parts by mass of chlorinated butyl rubber, and the average particle diameter of nanoscale titanium dioxide, nanoscale silver powder and nanoscale montmorillonite powder is 50nm, reinforcing The agent is a mixture of silica and mica treated with a silane coupling agent, and the vulcanizing agent is sulfur.

Embodiment 3

[0034] A kind of butyl rubber, comprises following mass parts components:

[0035]

[0036]

[0037] Among them, the halogenated diene rubber is 35 parts by mass of brominated butyl rubber and 65 parts by mass of chlorinated butyl rubber, and the average particle diameter of nanoscale titanium dioxide, nanoscale silver powder and nanoscale montmorillonite powder is 200nm, and the reinforcement The agent is a mixture of modified clay and kaolin treated with a silane coupling agent, and the vulcanizing agent is sulfur.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to rubber composition and discloses novel butyl rubber. The novel butyl rubber comprises components in parts by mass as follows: 100 parts of halogenated diene rubber, 3-10 parts of stearic acid, 1-20 parts of nanoscale titanium dioxide, 2-10 parts of phenolic resin, 1-10 parts of zinc oxide, 0.5-2 parts of a vulcanizing agent and 0.5-1 part of nanoscale silver powder. The vulcanization performance, the mechanical property, the wear resistance, the crosslinking density, the strength, the glossiness and the like of the novel butyl rubber are all improved; meanwhile, the novel butyl rubber has anti-bacterial performance, ultraviolet resistance, ageing resistance and pulverization resistance, has good airtightness and is suitable for being used as a food container.

Description

technical field [0001] The invention relates to a rubber composition, in particular to a butyl rubber. Background technique [0002] Butyl rubber (IIR) is the first highly saturated rubber variety in the history of the development of the synthetic rubber industry. It is a low-temperature (about -100°C) copolymer of isobutylene and a small amount of isoprene. [0003] A small amount of isoprene is introduced to obtain double bonds available for vulcanization for sulfur vulcanization, thereby improving the versatility of butyl rubber. Due to its structural characteristics, butyl rubber has good air tightness, but it also has disadvantages such as slow vulcanization speed, poor self-adhesiveness and mutual adhesion, poor compatibility, and poor interaction with reinforcing agents. Contents of the invention [0004] The invention provides a butyl rubber aiming at the disadvantages of butene rubber in the prior art, such as slow vulcanization speed, poor self-adhesiveness and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L15/02C08L61/06C08K13/06C08K9/06C08K3/36C08K5/09C08K3/22C08K3/08C08K3/34B29B7/72
Inventor 陈建会陈中敢
Owner ZHEJIANG SHITAI IND CO LTD