A conductive powder coating

A conductive powder and coating technology, applied in powder coatings, conductive coatings, polyether coatings, etc., can solve the problems of unstable resistivity and achieve the effect of uniform and stable surface resistivity

Active Publication Date: 2018-03-06
DEQING COUNTY JINQIU PLASTIC POWDER CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, the practical light-colored conductive powder coatings on the market are all made of conductive fibers. The problem with conductive powder coatings is that the resistivity is extremely unstable, some of which are around 100 ohms, and some of which can reach more than 1000 ohms. , this feature makes it difficult for the existing light-colored conductive powder coatings to further develop the market

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Embodiment 1: a kind of conductive powder paint, is made up of following raw material by weight ratio:

[0037] Polyphenol resin, average particle diameter 30-40 micron 400-600 parts;

[0038] 30 parts of polyamine curing agent;

[0039] 350 parts of titanium dioxide;

[0040] Zinc oxide powder, average particle size 20-30 micron 10 parts;

[0041] Conductive carbon black, average particle diameter 20-30 micron 15 parts;

[0042] 1 part of amide wax defoamer;

[0043] BPO cross-linking agent 1 part.

Embodiment 2

[0044] Embodiment 2: a kind of conductive powder paint, is made up of following raw material by weight ratio:

[0045] Polyphenol resin, average particle diameter 30-40 micron 600 parts;

[0046] 50 parts of polyamine curing agent;

[0047] 500 parts of titanium dioxide;

[0048] Zinc oxide powder, average particle size 20-30 micron 30 parts;

[0049] Conductive carbon black, average particle diameter 20-30 micron 25 parts;

[0050] 100 parts of polyethylene wax defoamer defoamer;

[0051] 100 parts of DBHP and BPO mixture cross-linking agent;

[0052] 15 parts of conductive titanium dioxide.

Embodiment 3

[0053] Embodiment 3: a kind of conductive powder coating, is made up of following raw material by weight ratio:

[0054] Polyphenol resin, average particle diameter 30-40 micron 450 parts;

[0055] 40 parts of polyamine curing agent;

[0056] 420 parts of titanium dioxide;

[0057] Zinc oxide powder, average particle size 20-30 micron 18 parts;

[0058] Conductive carbon black, average particle diameter 20-30 micron 18 parts;

[0059] 35 parts of polypropylene wax defoamer defoamer;

[0060] 20 parts of DBHP cross-linking agent;

[0061] 1 part polyaniline.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a conductive powder coating and belongs to the technical field of powder coatings. The conductive powder coating is prepared from, by weight percentage, resin, a curing agent, titanium dioxide, zinc oxide powder, conductive carbon black, a defoaming agent and a crosslinking agent. The powder coating is good in conductive performance.

Description

technical field [0001] The invention relates to the technical field of powder coatings, in particular to a conductive powder coating. Background technique [0002] Powder coatings started in the late 1930s. The earliest prototype was to spray polyethylene powder onto metal surfaces in a molten state by flame spraying. [0003] Conductive powder coating is a composite polymer conductive material. After electrostatic spraying and high-temperature curing, downstream customers can obtain polymer protective conductive coatings, which are used in fields such as eliminating static electricity, electromagnetic shielding, electric heating, and anti-corrosion; the earliest conductive Powder coating can be traced back to 1948, when the United States published a patent for making conductive adhesive from silver and epoxy resin. [0004] The existing conductive powder coatings are mostly made of dark conductors such as carbon black, which has the advantages of obvious conductive effect,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D171/10C09D175/06C09D5/03C09D5/24