fe3o4/ceo2 nanocomposite material, preparation method and application

A nano-composite material, fe3o4 technology, applied in the field of water treatment, to achieve good application effect, strong operability, and good application prospects

Inactive Publication Date: 2018-10-19
ZHENGZHOU UNIVERSITY OF AERONAUTICS
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, compared with natural horseradish peroxidase, the activity of ferric oxide peroxide mimetic enzyme needs to be further improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • fe3o4/ceo2 nanocomposite material, preparation method and application
  • fe3o4/ceo2 nanocomposite material, preparation method and application
  • fe3o4/ceo2 nanocomposite material, preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0070] Fe provided in the present invention 3 o 4 / CeO 2 Nanocomposites are mainly prepared by co-precipitation method. The co-precipitation method means that when the solution contains two or more cations, all kinds of cations exist in the solution in a homogeneous phase. With the addition of the precipitating agent, after the precipitation reaction, a uniform precipitation of various components can be obtained. The co-precipitation method is an important method for preparing composite oxide nanoparticles containing two or more metal elements, which has the advantages of simple preparation process, easy control of preparation conditions, short synthesis period, and low cost. Introduce Fe in the present invention below in conjunction with embodiment 3 o 4 / CeO 2 Preparation of nanocomposites and related testing and identification.

[0071] Fe prepared in this example 3 o 4 / CeO 2 The nanocomposite material is prepared by the following steps:

[0072] (1) Preparation ...

Embodiment 2

[0106] With the Fe prepared in Example 1 3 o 4 / CeO 2 Based on the nanocomposite material, this example mainly introduces the relevant research on the application of the composite material in wastewater containing p-nitrophenol.

[0107] For the convenience of measuring and evaluating the content of p-nitrophenol in the wastewater solution, the common method is to establish the corresponding relationship between the absorbance and the concentration of p-nitrophenol by using the absorbance method with the help of a spectrophotometer, so as to facilitate the determination of the content of p-nitrophenol in the wastewater, but due to P-nitrophenol exists in different states under different pH conditions, so it needs to be treated differently when using the absorbance method to determine the absorption peak. The following is a brief introduction to the relevant situation when using the absorbance method to determine the content of p-nitrophenol in wastewater.

[0108] Determina...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of water treatment, and specifically relates to a patent application for a Fe3O4 / CeO2 nanocomposite material, a preparation method and its application. The composite material is prepared by co-precipitation method, and the nano-Fe3O4 particles in the composite material are wrapped on the surface of CeO2. Fe3O4 / CeO2 nanocomposites can be used as peroxide mimic enzymes in p-nitrophenol wastewater treatment. This application provides a new preparation method for Fe3O4 / CeO2 nanocomposite materials. The new preparation method provided has strong operability and can better meet the needs of large-scale production and practical applications. Based on the Fe3O4 / CeO2 nanocomposite material prepared by the new method, the inventor conducted new application research. When used in the treatment of p-nitrophenol wastewater, it showed good application effects and the degradation rate of p-nitrophenol. It can be better maintained above 90% and has good application prospects.

Description

technical field [0001] The invention belongs to the technical field of water treatment, in particular to a Fe 3 o 4 / CeO 2 Patent applications for nanocomposite materials, preparation methods and applications. Background technique [0002] As important organic products, phenolic compounds and their derivatives are important chemical raw materials and intermediates, as well as by-products of many industrial productions, and important organic pollutants. Petroleum, coal chemical, dyestuff, pharmaceutical, pesticide, paint, spice, plastic, leather, synthetic fiber, disinfectant and grease chemical factories all produce a variety of phenolic wastewater. Therefore, phenolic wastewater is a kind of industrial wastewater with a wide range of sources. [0003] Phenol-containing wastewater has always been a difficult problem in domestic sewage treatment. Although there are physicochemical methods including adsorption method, extraction method, steam method, coagulation precipita...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J23/83C02F1/72
CPCC02F1/725B01J23/83C02F2101/345B01J35/396
Inventor 李春光崔节虎窦书豪梁丽珍罗旭周浩郑宾国何艳红
Owner ZHENGZHOU UNIVERSITY OF AERONAUTICS