A technology of knife horse and underglaze color, which is applied in the field of painted pottery production, can solve the problems of export restrictions, environmental protection, etc., and achieve the effect of easy permanent preservation, beautiful appearance and good hand feeling

Inactive Publication Date: 2016-06-29
JIESHOU LUSHI TEXTURING PAINTED POTTERY CO LTD
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the limitations of high-temperature pigments, glazes, and craftsmanship, ceramic products have been limited to using lead-containing glazes and low-temperature firing (800°C-900°C). Lead-containing glazes are not environmentally friendly, and exports are also restricted.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A special glaze for underglaze painted Daomaren painted pottery, made of the following components: 30g of ferromolybdenum, 25g of bone powder, 20g of shells, 30g of clay, 20g of cobalt oxide, 5g of titanium carbide, 5g of silicon carbide, and 4g of proanthocyanidin , tea alkaloid 3g, natural marine stone 8g, blue sidelite 8g, lepidolite 6g, Benshan green clay 5g, boron oxide 3g, magnesite 8g, potassium feldspar 8g; when preparing, mix the above components in proportion , put it into a ball mill and grind it continuously for 4 hours, the fineness reaches 450-500 mesh sieve, and it is prepared by sieving.

Embodiment 2

[0022] A special glaze for underglaze painted Daomaren painted pottery, made of the following components: 35g of ferromolybdenum, 24g of bone powder, 25g of shells, 25g of clay, 50g of cobalt oxide, 4g of titanium carbide, 6g of silicon carbide, and 3g of proanthocyanidin , tea alkaloid 4g, natural marine stone 7g, blue sidelite 9g, lepidolite 5g, Benshan green clay 6g, boron oxide 2g, magnesite 9g, potassium feldspar 7g; when preparing, mix the above components in proportion , put it into a ball mill and grind it continuously for 4 hours, the fineness reaches 450-500 mesh sieve, and it is prepared by sieving.

Embodiment 3

[0024] A special glaze for underglaze painted Daomaren painted pottery, made of the following components: 25g of ferromolybdenum, 26g of bone powder, 15g of shells, 35g of clay, 5g of cobalt oxide, 6g of titanium carbide, 4g of silicon carbide, and 5g of proanthocyanidin , tea alkaloid 2g, natural marine stone 9g, blue sidelite 7g, lepidolite 7g, Benshan green clay 4g, boron oxide 4g, magnesite 7g, potassium feldspar 9g; when preparing, mix the above components in proportion , put it into a ball mill and grind it continuously for 4 hours, the fineness reaches 450-500 mesh sieve, and it is prepared by sieving.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides glaze special for underglaze colour depicted knife, horse person coloured pottery. The glaze is prepared from, by weight, 25-35 g of ferromolybdenum, 24-26 g bone meal, 15-25 g of shells, 25-35 g of clay, 5-50 g of cobaltous oxide, 4-6 g of titanium carbide, 4-6 g of silicon carbide, 3-5 g of procyanidine, 2-4 g of tea alkaloids, 7-9 g of natural sea stone, 7-9 g of hauynite, 5-7 g of lepidolite, 4-6 g of pear skin mud, 2-4 g of boric oxide, 7-9 g of magnesite and 7-9 g of potassium feldspar. According to the glaze, lead-removed glaze is adopted in cooperation with high temperature sintering, glaze cannot flow, a product is pure in color, original shapes of knives, horses and persons are maintained, and the preservation time is long.

Description

technical field [0001] The invention relates to the technical field of painted pottery production, in particular to a special glaze material for underglaze painted pottery depicting saber-horse people. Background technique [0002] China is an ancient country of ceramics. When talking about ceramics, foreigners think of China. Pottery is an artificial form. The basic materials in ceramic form are earth, water, and fire. Only by mastering the plasticity and rheology of water and soil mixing, as well as the molding method and sintering law, can people promote the generation and evolution of ceramic art forms and make ceramic utensils produce beautiful forms. At the same time, it pays attention to the organic combination of modeling and decoration. Through people's keen inspiration and innovative consciousness, it captures and reveals the plastic beauty, flexibility beauty and expressive vitality of the soil. In this way, a new form of ceramic art emerges, which is mastered, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C8/00C04B41/86
CPCC03C8/00C04B41/009C04B41/5022C04B41/86C04B35/14
Inventor 卢群山卢涛王峰
Owner JIESHOU LUSHI TEXTURING PAINTED POTTERY CO LTD