A kind of Longquan celadon She nationality doll and its manufacturing method

A manufacturing method and technology of Longquan celadon, applied in the field of Longquan celadon, can solve the problems of insufficient strength and color strength of celadon, high cost of raw materials, hindering the popularization and application of Longquan celadon, etc., to improve the stability of glaze color, strong three-dimensional effect, and improve resource utilization. rate effect

Active Publication Date: 2020-11-17
LISHUI UNIV
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, factors such as high cost of raw materials, insufficient celadon strength and color strength hinder the popularization and application of Longquan celadon

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] S1 In parts by weight, the oxide composition of Longquan celadon she doll blank is as follows: 20% of Longquan porcelain clay, 8% of quartz, 10% of calcined alumina powder, 30% of Longyan kaolin, 8% of potassium feldspar, 1% of limestone, Zijin soil 5%. Wherein the chemical composition of the Longquan green body contains the chemical composition of the Longquan green body containing SiO 2 65%, Al 2 o 3 22%, Fe 2 o 3 2.0%, K 2 O2.3%, Na 2 O 0.2%, CaO 0.1%, MgO 0.1%, TiO 2 0.6%.

[0035] S2 In terms of weight percentage, the weight percentage of raw materials, water and additives used for the Longquan celadon She nationality doll blank is 45:35:2. Wherein, based on the green body blank formula, the binder carboxymethyl cellulose is 2%, and the dispersant PMAA-NH 4 After mixing the blank raw materials, water and additives evenly, put them in a ball mill and grind them until D10>0.06μm, D90 is 0.35±0.05μm, and D100<3μm, then use a sieve with a pore size of 325 ...

Embodiment 2

[0040] S1 In parts by weight, the oxide composition of Longquan celadon She nationality doll blank is as follows: Longquan porcelain clay 25%, quartz 15%, calcined alumina 20%, Longyan kaolin 35%, potassium feldspar 15%, limestone 2%, Zijin Soil 6%. Wherein the chemical composition of the Longquan green body contains the chemical composition of the Longquan green body containing SiO 2 67%, Al 2 o 3 22%, Fe 2 o 3 2.0%, K 2 O2.5%, Na 2 O 0.3%, CaO 0.2%, MgO 0.1%, TiO 2 0.65%.

[0041] S2 In terms of weight percentage, the weight percentage of raw materials, water and additives used for the Longquan celadon She nationality doll blank is 48:36:3. Wherein, based on the green body blank formula, the binder is carboxymethyl cellulose at 2%; the dispersant is polyethylene glycol (average molecular weight is 10000) at 3%, and the raw materials for the green body, water and additives are mixed After uniformity, put it in a ball mill and ball mill until the fineness of D10>0...

Embodiment 3

[0046] S1 In terms of parts by weight, the oxide composition of Longquan celadon She nationality doll blank is as follows: Longquan porcelain clay 27%, quartz 16%, calcined alumina 15%, Longyan kaolin 33%, potassium feldspar 14%, limestone 2%, Zijin Soil 7%. Wherein the chemical composition of the Longquan green body contains the chemical composition of the Longquan green body containing SiO 2 66%, Al 2 o 3 23%, Fe 2 o 3 2.2%, K 2 O2.4%, Na 2 O 0.3%, CaO 0.2%, MgO 0.3%, TiO 2 0.8%.

[0047] S2 In terms of weight percentage, the weight percentage of raw materials, water and additives for Longquan celadon She nationality doll blank is 50:38:3. Wherein, based on the green body blank formula, the binder glycerin is 4%; the dispersant is polymethacrylamide (PMAA-NH 4 ) 3%, after mixing raw materials, water and additives for the billet evenly, put them in a ball mill and ball mill until the fineness of D10>0.06μm, D90 is 0.35±0.05μm, and D100<3μm. Sieve out impurities ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
impact strengthaaaaaaaaaa
flexural strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a Long quan celadon She nationality puppet and a production method of same. The puppet includes a green body raw material for the Long quan celadon She nationality puppet, water and additives according to the weight percentage ratio of 45-55:35-45:1-5. The Long quan celadon She nationality puppet green body oxide includes the raw materials including, by weight, 20-35% of Long quan porcelain clay, 5-20% of quartz, 10-30% of calcined aluminum oxide powder, 30-45% of Long yan kaolin, 5-18% of potassium feldspar, 1-3% of limestone and 5-10% of violet golden earth. On the basis of the Long quan celadon She nationality puppet green body material, the additive includes: 2-7% of a binder, and 1-5% of a dispersion agent. In the invention, traditional Long quan celadon art is combined with traditional She nationality costume, so that application and development of Long quan celadon production technology and traditional She nationality costume culture are effectively promoted. Production cost of the Long quan celadon in large scale is greatly reduced.

Description

technical field [0001] The invention relates to the technical field of Longquan celadon, in particular to a Longquan celadon She nationality doll and a manufacturing method thereof. Background technique [0002] The existing doll toys on the market are mass-produced low-end toys with similar shapes and structures, which cannot meet people’s strong spiritual and cultural needs for doll toys. The existing doll toys are manufactured according to comics or cartoon figures. Using materials such as wood or plastic, the shape is monotonous and dull and the aesthetic feeling is not strong. [0003] Such as the application publication number: CN102335509A application publication date: 2012.02.01 Chinese patent discloses a method for making a simulated doll. The information is stored in the computer; 2. Use the computer to control the three-dimensional engraving machine to carve the parts of the simulated doll; 3. Dismember the carved human body parts and inject them with fillers, an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/13C03C8/00C04B41/86C04B35/634
CPCC03C8/00C04B33/13C04B33/1305C04B35/63404C04B35/63488C04B41/009C04B41/5022C04B41/86C04B2235/3208C04B2235/3217C04B2235/3418C04B2235/3472C04B2235/96C04B2235/9607C04B2235/963C04B41/4535
Inventor 施群周灵
Owner LISHUI UNIV