Inflaming-retarding styrene-butadiene-rubber heat-insulation and waterproof paint and preparation method thereof

A styrene-butadiene rubber and waterproof coating technology, applied in the coating field, can solve the problems of low decorative wall bonding strength, limited coating application scope, unsuitable waterproof coating, etc., and achieves good application prospects, good flame retardant performance, and cost. low cost effect

Inactive Publication Date: 2016-10-12
ANHUI LENCAQI BUILDING MATERIAL
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Now this kind of coating is undergoing a transformation from industrial heat insulation to building heat insulation. Low and decorative properties need to be further improved, etc., which limit the scope of application of this type of coating
[0004] Patent No. 201510887384.8 discloses a waterproof rubber material, which is prepared from the following raw materials in parts by weight: polyethylene terephthalate 7-8, trioctyl citrate 3-4, rosin 1-2, polypropylene Nitrile 24-27, sodium diacetate 1-2, graphite 12-13, fly ash microbeads 3-4, sod

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0015] The flame-retardant styrene butadiene rubber heat insulation and waterproof coating of this embodiment is prepared from the following parts by weight of raw materials: 100 parts of styrene butadiene rubber emulsion, 10 parts of neoprene rubber emulsion, 15 parts of hydroxyethyl methacrylate, 8 parts of alkyl resorcinol formaldehyde resin, 2 parts of hexamethoxymethyl melamine, 5 parts of antimony trioxide, 4 parts of clay, 4 parts of aluminum hydroxide, 2 parts of sodium tripolyphosphate, 3 parts of tributyl phosphate , 2 parts of stearic acid, 1 part of 1,2-thiol imidazoline, 2 parts of dibutyl phthalate, 10 parts of hollow glass beads, appropriate amount of ethanol, and appropriate amount of deionized water.

[0016] The flame-retardant styrene-butadiene rubber heat insulation and waterproof coating of this embodiment is prepared by the following steps:

[0017] (1) Put antimony trioxide, aluminum hydroxide, and clay into a ball mill at a speed of 2800 rpm and a temperatur...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an inflaming-retarding styrene-butadiene-rubber heat-insulation and waterproof paint which is characterized by being prepared from the following raw materials in parts by weight: 100 parts of butadiene styrene rubber emulsion, 8-10 parts of chloroprene rubber emulsion, 15-20 parts of hydroxyethyl methylacrylate, 8-10 parts of alkylresorcinol formaldehyde resin, 1-2 parts of hexamethoxymethyl melamine, 3-5 parts of antimonous oxide, 3-5 parts of pottery clay, 3-4 parts of aluminum hydroxide, 1-2 parts of sodium tripolyphosphate, 2-3 parts of tributyl phosphate, 1-2 parts of stearic acid, 0.5-1 part of 1,2-mercaptoimidazoline, 1-2 parts of dibutyl phthalate, 8-10 parts of hollow glass micro-beads, a proper amount of ethanol and a proper amount of deionized water.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a heat-insulating and waterproof coating of flame-retardant styrene-butadiene rubber and a preparation method thereof. technical background [0002] Due to the sunlight, the temperature inside the building rises, which will increase the energy consumption of the air conditioner. In addition, industrial plants, prefabricated houses or temporary buildings mostly use metal steel plate roofs. In the sun, the indoor temperature will rise rapidly. In many cases, the effect of using air conditioning to cool down the indoor temperature is not good. Lowering indoor temperatures by lowering the roof surface temperature is usually the most practical way. The way to prevent the indoor temperature from rising is to make the outdoor heat (mainly the heat generated by sunlight) pass into the room as little as possible, and the indoor heat be dissipated as much as possible. [0003] The therm...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D109/08C09D115/02C09D161/12C09D5/18C09D7/12C08C19/28
CPCC08C19/28C08L2201/02C08L2205/03C09D5/18C09D7/62C09D7/63C09D7/70C09D109/08C08L15/02C08L61/12C08K13/06C08K9/04C08K7/28C08K3/2279C08K2003/2227C08K3/346
Inventor 乔启信金自海
Owner ANHUI LENCAQI BUILDING MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap