Nb(OH)5 nanowire/reduced graphene oxide composite photocatalyst, and preparation method and application thereof

A graphene composite and photocatalyst technology, applied in metal/metal oxide/metal hydroxide catalyst, catalyst activation/preparation, physical/chemical process catalyst, etc., can solve the human nervous system and ecological environment hazards, toxicity, Skin respiratory and digestive system hazards and other problems, to achieve the effect of simple and time-saving preparation process, promote separation, and improve photocatalytic activity

Active Publication Date: 2016-11-09
HENAN POLYTECHNIC UNIV
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Phenolic compounds in wastewater are a type of protoplasmic poisons, which can coagulate proteins and have great potential harm to the human nervous system and the ecological environment. At the same time, phenolic wastewater is often accompanied by the presence of heavy metal ions such as chromium, mercury, and lead. Among them, water-soluble Cr(VI) has strong toxicity and strong oxidizing property, which will cause serious harm to human skin, respiratory and digestive systems, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nb(OH)5 nanowire/reduced graphene oxide composite photocatalyst, and preparation method and application thereof
  • Nb(OH)5 nanowire/reduced graphene oxide composite photocatalyst, and preparation method and application thereof
  • Nb(OH)5 nanowire/reduced graphene oxide composite photocatalyst, and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A Nb(OH) 5 Preparation method of nanowire / reduced graphene oxide composite photocatalyst:

[0035] In terms of mass fraction, the mass content of reduced graphene oxide is 1.0%, Nb(OH) 5 It is an amorphous nanowire with a length of 3 μm and a diameter of 100 nm. The preparation method of this composite photocatalyst is as follows:

[0036] 1g Nb 2 o 5 The powder was placed in 70 mL of 10 mol / L KOH solution, stirred at room temperature for 1 h, and 10 mL of 1.0 mg / mL graphene oxide aqueous solution was added thereto, and the mixed suspension was obtained by ultrasonication at room temperature for 0.5 h; In a tetrafluoroethylene microwave reaction tank, after sealing, place it in a microwave reactor and react for 1.5h at a power of 300W; after cooling, vacuum filter the suspension in the reaction tank, and use 150mL of 0.02mol / L Washed with dilute hydrochloric acid for 3 times, and then washed with deionized water several times until the pH of the filtrate was about ...

Embodiment 2

[0043] A Nb(OH) 5 Preparation method of nanowire / reduced graphene oxide composite photocatalyst:

[0044] In terms of mass fraction, the mass content of reduced graphene oxide is 2.5%, Nb(OH) 5 It is an amorphous nanowire with a length of 3.5 μm and a diameter of 80 nm. The preparation method of this composite photocatalyst is as follows:

[0045] 2g Nb 2 o 5 The colloid was placed in 70mL of 16mol / L NaOH solution, stirred at room temperature for 0.5h, and then 10mL of 5.0mg / mL graphene oxide aqueous solution was added to it, and the mixed suspension was obtained by ultrasonication at room temperature for 2h; the resulting mixed suspension was transferred to polytetrafluoroethylene In an ethylene microwave reaction tank, seal it and place it in a microwave reactor for 1 hour at a power of 500W; after cooling, vacuum filter the suspension in the reaction tank, and wash the solids with 150mL of 1mol / L dilute hydrochloric acid respectively 3 times, and then washed with deion...

Embodiment 3

[0049] A Nb(OH) 5 Preparation method of nanowire / reduced graphene oxide composite photocatalyst:

[0050] In terms of mass fraction, the mass content of reduced graphene oxide is 5.0%, Nb(OH) 5 It is an amorphous nanowire with a length of 1.5 μm and a diameter of 120 nm. The preparation method of this composite photocatalyst is as follows:

[0051] 0.5g Nb 2 o 5The powder was placed in 70mL of 8mol / L KOH solution, stirred at room temperature for 1.5h, then 10mL of 2.5mg / mL GO aqueous solution was added to it, and the mixed suspension was obtained by ultrasonication at room temperature for 1.5h; the resulting mixed suspension was transferred to polytetrafluoroethylene In a microwave reaction tank, after sealing, place it in a microwave reactor and react for 2 hours at a power of 200W; after cooling, vacuum filter the suspension in the reaction tank, and wash the solids with 150mL of 0.1mol / L dilute hydrochloric acid respectively 3 times, and then washed with deionized wate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Lengthaaaaaaaaaa
Diameteraaaaaaaaaa
Lengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a Nb(OH)5 nanowire / reduced graphene oxide composite photocatalyst, and a preparation method and application thereof. The active compositions of the catalyst comprise Nb(OH)5 and reduced graphene oxide, and Nb(OH)5 nanowires are uniformly distributed on laminar reduced graphene oxide. According to the preparation method, Nb2O5 is taken as a niobium source, GO is taken as a carrier and a template agent, and a microwave synthesis process is employed for preparing an in-situ compound of the niobate nanowires and reduced graphene oxide, metal ions in the niobate layers are displaced by hydrogen ion through acid exchange, an obtained niobate nanowire and reduced graphene oxide compound is calcined, so that the Nb(OH)5 nanowire / reduced graphene oxide composite photocatalyst is obtained. The preparation method is simple and time-saving, the material morphology is uniform, the synthesis condition is easy to control, and the preparation method is suitable for industrialized batch production. When applied to remove phenol pollutants in waste water under irradiation of visible light at normal temperature, the Nb(OH)5 nanowire / reduced graphene oxide composite photocatalyst is capable of reducing high-toxicity hexavalent chromium into trivalent chromium and achieves the purpose of highly purifying composite polluted waste water.

Description

technical field [0001] The invention belongs to the technical field of photocatalysts, in particular to a Nb(OH) 5 Nanowire / reduced graphene oxide composite photocatalyst and its preparation method and application. Background technique [0002] Composite materials with controllable morphology and composition have great potential application value in the fields of heterogeneous catalysis, solar energy conversion and photoelectrochemistry (H.Liu, et al.3D Bi 2 MoO 6 Nanosheet / TiO 2 Nanobelt Heterostructure: Enhanced Photocatalytic Activities and Photoelectrochemical Performance, ACSCatal. 2015, 5, 4530-4536; X.S. Zhao, et al. Nitrogen-Doped Titanate-Anatase Core-Shell Nanobelts with Exposed{101}Anatase Facets and Enhanced Photo Visible, J .Am.Chem.Soc.2012, 134, 5754-5757; Han Cheng et al., Progress in the Preparation of Solar Fuels by Nano-heterojunction Photocatalytic Materials, Journal of Inorganic Chemistry. 2015, 30, 1121-1130; Li Shichao et al., Three-dimensional cl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B01J23/20C02F1/30C02F1/70C02F101/34C02F101/22
CPCC02F1/30C02F1/70B01J23/20B01J37/346C02F2101/345C02F2101/22B01J35/399B01J35/50B01J35/39Y02W10/37
Inventor 杨娟戴俊卞琳艳沈晓晓
Owner HENAN POLYTECHNIC UNIV
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com