Waterborne expansion fire-proof coating with weather resistance and fire resistance and preparing method

A technology of fire-resistant performance and fire-resistant coatings, applied in fire-resistant coatings, coatings, etc., can solve problems such as fire-resistant performance, physical and chemical performance defects, unstable fire-resistant performance, and unsatisfactory outdoor weather resistance, so as to improve physical and chemical properties and fire-resistant performance The effect of stability, suitable expansion ratio and good construction performance

Inactive Publication Date: 2017-05-31
TIANJIN FIRE RES INST
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Water-based intumescent fireproof coatings generally use modified acrylic emulsion as the main adhesive. Due to the backwardness of my country's basic chemical industry technology, water-based intumescent fireproof coatings that use acrylic emulsion as the main adhesive have obvious differences in fire resistance, physical and chemical properties, etc. Defects
At present, the main acrylic emulsion manufacturers are still produced by the world's largest group companies, such as BASF, Rohm and Haas, Dow Chemical, Nippon Shokubai and Arkema. These international large companies have strong technical strength. A variety of acrylic emulsions used in water-based intumescent fire retardant coatings have been used. For example, the water-based steel structure fire retardant coatings of PPG and Jotun have good fire resistance (the coating thickness is 2.0mm, and the fire resistance limit is about 1.0 hours). Outdoor weather resistance and other indicators are not very ideal, and the fire resistance performance is unstable

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Example 1: Component A is composed of the following materials in parts by weight: modified inorganic bentonite: 0.3 parts; polyacrylic acid sodium salt water-based dispersant: 3 parts; defoamer containing metal soap and mineral oil mixture: 0.4 parts parts; fungicide: 0.3 parts; titanium dioxide: 5.0 parts; water: 10 parts.

[0022] Component B consists of the following materials in parts by weight: modified acrylic emulsion: 20 parts; pentaerythritol: 11 parts; melamine: 10 parts; ammonium polyphosphate: 24 parts; chlorinated paraffin: 3 parts; 3 parts; water: 10 parts.

[0023] (1) Preparation of component A

[0024] Add 10 parts of water into the stainless steel mixing tank, slowly add 0.3 parts of modified inorganic bentonite at a stirring speed of 200-300 rpm, stir for about 10 minutes, and then sequentially add 3 parts of polyacrylic acid sodium salt water-based dispersant, 0.4 parts of antifoaming agent containing a mixture of metal soap and mineral oil, 0.3 pa...

Embodiment 2

[0029] Example 2: Component A is composed of the following materials in parts by weight: modified inorganic bentonite: 0.3 parts; polyacrylic acid sodium salt water-based dispersant: 3 parts; defoamer containing metal soap and mineral oil mixture: 0.4 parts parts; fungicide: 0.3 parts; titanium dioxide: 5.0 parts; water: 10 parts.

[0030] Component B consists of the following materials in parts by weight: modified acrylic emulsion: 24 parts; pentaerythritol: 11 parts; melamine: 10 parts; ammonium polyphosphate: 24 parts; chlorinated paraffin: 3 parts; Coalescing agent: 3 parts; water: 8 parts.

[0031] (1) Preparation of component A

[0032] Add 10 parts of water into the stainless steel mixing tank, slowly add 0.3 parts of modified inorganic bentonite at a stirring speed of 200-300 rpm, stir for about 10 minutes, and then sequentially add 3 parts of polyacrylic acid sodium salt water-based dispersant, 0.4 parts of antifoaming agent containing a mixture of metal soap and mi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
minimum film forming temperatureaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a waterborne expansion fire-proof coating with the weather resistance and the fire resistance and a preparing method. The waterborne expansion fire-proof coating is mixed by A components and B components; the A components are prepared from a thickening agent, a dispersing agent, an antifoaming agent, a sterilizing agent, titanium dioxide and water; the B components are prepared from modified acrylic emulsion, pentaerythritol, tripolycyanamide, ammonium polyphosphate, chlorinated paraffin, a coalescing agent and water. The waterborne expansion fire-proof coating is an environment-friendly waterborne expansion fire-proof coating, and has the advantages of being good in ultraviolet light resistance, low in water absorption rate, high in fire resistance and the like, and the defects that the physical and chemical performance, the fire resistance and the like of domestic similar products are poor are overcome. Compared with foreign similar products, the physical and chemical performance and the stability of the fire resistance of a product are improved; meanwhile, the coating has the good construction performance, the decorative performance is high, the product storage stability is good, the raw materials are easy to obtain, and the cost is moderate; the weather resistance of the product meets the requirements of the standard technology.

Description

technical field [0001] The invention relates to the preparation technology of functional coatings, in particular to a water-based swelling fireproof coating with weather resistance and fire resistance and a preparation method. Background technique [0002] In the 1980s, my country's main fireproof material research department began to develop fireproof coatings. Up to now, domestic fireproof coating products and technical levels have been similar to foreign developed countries. There are many types of products: decorative fireproof coatings, cable fireproof coatings, and steel structures. Fireproof coatings, concrete structure fireproof coatings, etc. Intumescent fireproof coatings are favored by more application fields due to their thin coating, excellent fire resistance and strong decoration. [0003] With my country's continuous emphasis on environmental protection, fire-resistant coatings have also achieved certain results in environmentally friendly products and technolo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D131/04C09D5/18C09D7/12C09D7/00
CPCC09D131/04C08L2201/02C08L2201/08C08L2205/025C08L2205/035C09D5/185C09D7/40C09D7/43C09D7/61C09D7/65C08L91/06C08L33/02C08K13/06C08K3/346C08K5/34922C08K5/053C08K2003/323
Inventor 胡胜利马六甲赵璧谢浩
Owner TIANJIN FIRE RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap