Primary glass fiber filter paper and preparation method thereof
A glass fiber and alkali-free glass fiber technology is applied in the field of primary glass fiber filter paper and its preparation, which can solve the problems that the filter paper cannot adapt to the high temperature working environment, the chemical fiber has poor flame retardant performance, and the product structure is loose, so as to achieve accelerated dehydration speed, The effect of reducing energy consumption and improving production efficiency
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0023] Example 1
[0024] Preparation of a primary glass fiber filter paper
[0025] (1) Raw material preparation: Weigh 5wt% of the non-alkali glass fiber with a diameter of 0.46 and 95wt% of the medium-alkali chopped glass fiber with a diameter of 12μm according to the component content of the primary glass fiber filter paper;
[0026] (2) Dispersion pulping: Add the raw materials prepared in step (1) to a disperser containing sulfuric acid aqueous solution for 5 minutes to be beaten and dispersed to obtain a slurry with a beating degree of 1.5. Adjust the pH of the slurry by adjusting the amount of sulfuric acid and water The value is 3.0, and the mass concentration is 2.0%;
[0027] (3) Wet molding: transfer the slurry obtained in step (2) to the storage tank to dilute to a mass concentration of 0.2%, and adjust the pH value to 3.0 by adjusting the amount of sulfuric acid and water, and then the slurry in the storage tank The material is conveyed to the inclined wire forming pape...
Example Embodiment
[0031] Example 2
[0032] Preparation of a primary glass fiber filter paper
[0033] (1) Preparation of raw materials: Weigh 10wt% of non-alkali glass fibers with a diameter of 0.55 and 90wt% of medium-alkali chopped glass fibers with a diameter of 8μm according to the component content in the primary glass fiber filter paper;
[0034] (2) Dispersion and pulping: Add the raw materials prepared in step (1) to a disperser containing sulfuric acid aqueous solution for 5 minutes to be beaten and dispersed to obtain a slurry with a beating degree of 3.4. Adjust the pH of the slurry by adjusting the amount of sulfuric acid and water The value is 3.5 and the mass concentration is 1.0%;
[0035] (3) Wet molding: transfer the slurry obtained in step (2) to the storage tank to be diluted to a mass concentration of 0.1%, and adjust the pH value to 3.5 by adjusting the amount of sulfuric acid and water, and then the slurry in the storage tank The material is conveyed to the inclined wire forming...
Example Embodiment
[0039] Example 3
[0040] Preparation of a primary glass fiber filter paper
[0041] (1) Preparation of raw materials: weigh 15wt% of non-alkali glass fibers with a diameter of 0.39 and 85wt% of medium-alkali chopped glass fibers with a diameter of 10μm according to the component content of the primary glass fiber filter paper;
[0042] (2) Dispersion and pulping: Add the raw materials prepared in step (1) to a disperser containing sulfuric acid aqueous solution for 6 minutes to be beaten and dispersed to obtain a slurry with a beating degree of 5.1. Adjust the pH of the slurry by adjusting the amount of sulfuric acid and water The value is 2.5, and the mass concentration is 3.0%;
[0043] (3) Wet molding: transfer the slurry obtained in step (2) to the storage tank to be diluted to a mass concentration of 0.3%, and adjust the pH value to 2.5 by adjusting the amount of sulfuric acid and water, and then the slurry in the storage tank The material is conveyed to the inclined wire formi...
PUM
Property | Measurement | Unit |
---|---|---|
Diameter | aaaaa | aaaaa |
Diameter | aaaaa | aaaaa |
Diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap