ABS flame-retardant plastic

A technology of flame-retardant plastics and component content, applied in the field of ABS flame-retardant plastics, can solve problems such as health and environmental hazards, hydrogen halide toxic substances, etc., and achieve the effects of good cold resistance, good toughness and high strength

Inactive Publication Date: 2017-08-04
南通久聚高分子科技有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In recent years, many manufacturers at home and abroad have begun to research and develop flame-retardant plastics. However, most of the flame retardants added at present are halogen-based flame retardants, which will produce toxic hydrogen halides during long-term use, especially during combustion. Substances can cause great harm to people's health and the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A kind of ABS flame-retardant plastics, its component content mass fraction is:

[0036] ABS 60 parts

[0037] 15 parts of oxazine resin

[0038] Dimethyl trimethylsilyl phosphonate 5 parts

[0039] 3 parts antimony trioxide

[0040] 3 parts zinc borate

[0041] Antioxidant 2 parts

[0042] 2 parts magnesium hydroxide

[0043] 2 parts of cobalt silicate.

Embodiment 2

[0045] A kind of ABS flame-retardant plastics, its component content mass fraction is:

[0046] ABS 60-70 parts

[0047] 25 parts of oxazine resin

[0048] Dimethyl trimethylsilyl phosphonate 10 parts

[0049] 10 parts of antimony trioxide

[0050] 7 parts zinc borate

[0051] Antioxidant 6 parts

[0052] 8 parts magnesium hydroxide

[0053] 6 parts of cobalt silicate.

Embodiment 3

[0055] A kind of ABS flame-retardant plastics, its component content mass fraction is:

[0056] ABS 65 parts

[0057] 20 parts of oxazine resin

[0058] Dimethyl trimethylsilyl phosphonate 7 parts

[0059] 6 parts of antimony trioxide

[0060] Zinc borate 5 parts

[0061] Antioxidant 4 parts

[0062] Magnesium hydroxide 5 parts

[0063] 4 parts of cobalt silicate.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an ABS flame-retardant plastic, which is prepared from the following ingredients in parts by mass: 60 to 70 parts of ABS, 15 to 25 parts of oxazine resin, 5 to 10 parts of trimethylsilyl dimethyl methylphosphorate, 3 to 10 parts of antimonous oxide, 3 to 7 parts of zinc borate, 2 to 6 parts of antioxidants, 2 to 8 parts of magnesium hydrates and 2 to 6 parts of cobaltous silicate. The ABS flame-retardant plastic cannot easily combust under the condition of high temperature or other dangerous conditions; the use is safe; the elasticity is uniform and stable; deformation cannot be generated after the long time use; good performance of other polymer materials, such as the advantages of high intensity, high toughness and good cold-resistant performance can be realized.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to an ABS flame-retardant plastic. Background technique [0002] At present, plastic products are more and more widely used in many fields because of their unique good electrical resistance properties and high-frequency insulation properties that are not affected by humidity. However, since plastic itself is not flame retardant, it can cause fires due to its flammability when used in the electronics, construction, aviation and automotive industries. At present, with the advancement of technology, ubiquitous new products and new things have brought convenience and fast services to people's life and work, and people's lives have undergone earth-shaking changes. In order to protect national public property and citizens' personal safety, and to eliminate fire hazards, "high-quality and safe life" will gradually become an indispensable factor in life while enjoying a comfortab...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)