A kind of cinnabar handicraft raw material powder and preparation method thereof

A handicraft and raw material powder technology, which is applied in the field of cinnabar handicraft raw material powder and its preparation, can solve the problems of unstable chemical properties, easy discoloration, loss of luster, etc., and achieve the effect of improving chemical stability, high grade, and bright color

Inactive Publication Date: 2020-03-20
贵州筑信达创科技有限公司
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the lack of sufficient scientific research basis for cinnabar powder, the color and luster and reproducibility of the ink pad made by it are not ideal, and the chemical properties are unstable, and it is easy to change color and lose luster after long-term storage; it directly affects the beauty and grade of cinnabar handicrafts.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The preparation of embodiment 1 cinnabar handicraft raw material powder

[0027] (1) Take 92g of cinnabar, wash it with water, crush it into granular cinnabar, soak it with 30% sodium sulfide solution for 1 hour, filter, dry the cinnabar particles, put it into a pulverizer, sieve it, and collect it through a 150 mesh sieve. Mesh sieve fine powder to get cinnabar powder, set aside.

[0028] (2) Get the cinnabar powder prepared in step (1) and mix evenly with 8 g of nano-copper powder to obtain the cinnabar handicraft raw material powder.

Embodiment 2

[0029] The preparation of embodiment 2 cinnabar handicraft raw material powder

[0030] (1) Take 94g of cinnabar, wash it with water, crush it into granular cinnabar, soak it with 35% sodium sulfide solution for 2 hours, filter, dry the cinnabar particles, put it into a pulverizer, sieve it, and collect it through a 180-mesh sieve. Mesh sieve fine powder to get cinnabar powder, set aside.

[0031] (2) Get the cinnabar powder prepared in step (1) and mix evenly with 6 g of nano-copper powder to obtain the cinnabar handicraft raw material powder.

Embodiment 3

[0032] The preparation of embodiment 3 cinnabar handicraft raw material powder

[0033] (1) Take 97g of cinnabar, wash it with water, crush it into granular cinnabar, soak it with 40% sodium sulfide solution for 2 hours, filter, dry the cinnabar particles, put it into a pulverizer, sieve it, and collect it through a 180-mesh sieve. Mesh sieve fine powder to get cinnabar powder, set aside.

[0034] (2) Get the cinnabar powder prepared in step (1) and mix evenly with 3 g of nano-copper powder to obtain the cinnabar handicraft raw material powder.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides cinnabar handicraft raw material powder and a preparation method thereof. The cinnabar handicraft raw material powder is prepared from 92-97% of cinnabar powder and 3-8% of nano copper powder, has stable in chemical property, rosiness and metal reflective gloss, bright color and fine texture, and is quite suitable for making cinnabar handicraft.

Description

technical field [0001] The invention belongs to the technical field of chemical industry, and in particular relates to raw material powder for cinnabar handicrafts and a preparation method thereof. Background technique [0002] Cinnabar is mercury sulfide, chemical name: HgS; cinnabar, also known as cinnabar, cinnabar, red dan, mercury sand, is a natural ore of mercury sulfide, bright red, diamond luster to metallic luster, and belongs to the trigonal crystal system. In the hearts of Chinese people, red represents solemnity, symbolizes power, and has the effect of calming the nerves and helping sleep. Therefore, cinnabar handicrafts are also deeply loved by consumers, such as cinnabar bracelets, cinnabar pendants, and cinnabar seals. However, due to the lack of sufficient scientific research basis for cinnabar powder, the color and luster and reproducibility of the ink pad made by it are not ideal, and the chemical properties are unstable, and it is easy to change color and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B22/14C04B103/54
CPCC04B40/0042C04B2103/54C04B22/14C04B22/04C04B20/008
Inventor 胡正勇黄璜
Owner 贵州筑信达创科技有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com